The iron alloy particle is a particle including an iron alloy. The particle includes multiple mixed-phase particles, each including nanocrystals of 10 nm or more and 100 nm or less (i.e., from 10 nm to 100 nm) in crystallite size and an amorphous phase; and a grain boundary layer between the mixed-phase particles. Also, the iron alloy has a composition containing Fe, Si, P, B, C, and Cu.

A thermoelectric conversion material having a high dimensionless figure of merit ZT includes: a large number of polycrystalline grains which include a skutterudite-type crystal structure containing Yb, Co, and Sb; and an intergranular layer which is between the neighboring polycrystalline grains and includes crystals in which an atomic ratio of O to Yb is more than 0.4 and less than 1.5. A method for manufacturing a thermoelectric conversion material includes: a weighing step; a mixing step; a ribbon preparation step by rapidly cooling and solidifying a melt of the raw materials by using a rapid liquid cooling solidifying method; a first heat treatment step including heat treating in an inert atmosphere with an adjusted oxygen concentration; a second heat treatment step including heat treating in a reducing atmosphere; and manufacturing the thermoelectric conversion material by a pressure sintering step in an inert atmosphere.

A thermoelectric conversion material having a high dimensionless figure of merit ZT includes: a large number of polycrystalline grains which include a skutterudite-type crystal structure containing Yb, Co, and Sb; and an intergranular layer which is between the neighboring polycrystalline grains and includes crystals in which an atomic ratio of O to Yb is more than 0.4 and less than 1.5. A method for manufacturing a thermoelectric conversion material includes: a weighing step; a mixing step; a ribbon preparation step by rapidly cooling and solidifying a melt of the raw materials by using a rapid liquid cooling solidifying method; a first heat treatment step including heat treating in an inert atmosphere with an adjusted oxygen concentration; a second heat treatment step including heat treating in a reducing atmosphere; and manufacturing the thermoelectric conversion material by a pressure sintering step in an inert atmosphere.

The present disclosure provides a method for manufacturing a multi-main-phase structure magnet having excellent coercive force and a multi-main-phase structure magnet manufactured therefrom.

The present disclosure is directed at methods of preparing rare earth-based permanent magnets having improved coercivity and remanence, the method comprising one or more steps comprising: (a) homogenizing a first population of particles of a first GBM alloy with a second population of particles of a second core alloy to form a composite alloy preform, the first GBM alloy being substantially represented by the formula: AC.sub.bR.sub.xCo.sub.yCu.sub.dM.sub.z, the second core alloy being substantially represented by the formula G.sub.2Fe.sub.14B, where AC, R, M, G, b, x, y, and z are defined; (b) heating the composite alloy preform particles to form a population of mixed alloy particles; (c) compressing the mixed alloy particles, under a magnetic field of a suitable strength to align the magnetic particles with a common direction of magnetization and inert atmosphere, to form a green body; (d) sintering the green body; and (e) annealing the sintered body. Particular embodiments include magnets comprising neodymium-iron-boron core alloys, including Nd.sub.2Fe.sub.14B.

The present disclosure is directed at methods of preparing rare earth-based permanent magnets having improved coercivity and remanence, the method comprising one or more steps comprising: (a) homogenizing a first population of particles of a first GBM alloy with a second population of particles of a second core alloy to form a composite alloy preform, the first GBM alloy being substantially represented by the formula: AC.sub.bR.sub.xCo.sub.yCu.sub.dM.sub.z, the second core alloy being substantially represented by the formula G.sub.2Fe.sub.14B, where AC, R, M, G, b, x, y, and z are defined; (b) heating the composite alloy preform particles to form a population of mixed alloy particles; (c) compressing the mixed alloy particles, under a magnetic field of a suitable strength to align the magnetic particles with a common direction of magnetization and inert atmosphere, to form a green body; (d) sintering the green body; and (e) annealing the sintered body. Particular embodiments include magnets comprising neodymium-iron-boron core alloys, including Nd.sub.2Fe.sub.14B.

The present disclosure provides a preparation method of a metal powder material. An alloy sheet composed of a matrix phase and a dispersive phase with different chemical reactivities is prepared by the rapid solidification technique of alloy melt. Metal powder is prepared by the reaction of the alloy sheet and an acid solution. Please refer to the description for the detailed preparation method. This method is simple in operation, can be used to prepare many kinds of metal powder materials of different shapes and at the nanometer scale, the submicron scale and the micron scale, and has a good application prospect in the fields of catalysis, powder metallurgy and 3D printing.

The present disclosure provides a preparation method of a metal powder material. An alloy sheet composed of a matrix phase and a dispersive phase with different chemical reactivities is prepared by the rapid solidification technique of alloy melt. Metal powder is prepared by the reaction of the alloy sheet and an acid solution. Please refer to the description for the detailed preparation method. This method is simple in operation, can be used to prepare many kinds of metal powder materials of different shapes and at the nanometer scale, the submicron scale and the micron scale, and has a good application prospect in the fields of catalysis, powder metallurgy and 3D printing.

The present disclosure provides a preparation method of a metal powder material. An alloy sheet composed of a matrix phase and a dispersive phase with different chemical reactivities is prepared by the rapid solidification technique of alloy melt. Metal powder is prepared by the reaction of the alloy sheet and an acid solution. Please refer to the description for the detailed preparation method. This method is simple in operation, can be used to prepare many kinds of metal powder materials of different shapes and at the nanometer scale, the submicron scale and the micron scale, and has a good application prospect in the fields of catalysis, powder metallurgy and 3D printing.

The present disclosure provides a preparation method of a metal powder material. An alloy sheet composed of a matrix phase and a dispersive phase with different chemical reactivities is prepared by the rapid solidification technique of alloy melt. Metal powder is prepared by the reaction of the alloy sheet and an acid solution. Please refer to the description for the detailed preparation method. This method is simple in operation, can be used to prepare many kinds of metal powder materials of different shapes and at the nanometer scale, the submicron scale and the micron scale, and has a good application prospect in the fields of catalysis, powder metallurgy and 3D printing.