To provide a resin composition having large light transmittance and capable of providing a molded article which is highly laser-weldable to an absorbing resin member, as well as a kit, a method for manufacturing the resin composition, a method for manufacturing a formed article, and a formed article. The resin composition contains a polyamide resin, a maleic anhydride-modified polyphenylene ether-based resin, a phosphazene-based flame retardant, a zinc metal oxide, and a light transmitting dye.

Provided is a polyamide resin composition that has a large light transmittance with respect to 940 nm laser beam, and is capable of yielding a molded article that is highly laser weldable; and a kit, a method for manufacturing a molded article, and a molded article, using such polyamide resin composition.

A glued arrangement, preferably for a motor vehicle, is disclosed. The glued arrangement includes a first component, a second component, and at least one adhesive layer for connecting the two components. The adhesive layer includes a central zone and an edge zone that surrounds the central zone where, in the hardened state, the adhesive in the edge zone has a higher elasticity than the adhesive in the central zone.

A method of producing flexible polypropylene fabric bags with heat fused seams comprising providing fabric pieces, wherein each fabric piece has a coated side and an uncoated side; positioning fabric pieces so that a coated side of one fabric piece faces a coated side of another fabric piece; selecting an area of fabric to be joined for forming a seam or joint; applying heat to the area to be joined that is less than the melting point of the fabrics, for forming one or more seams or joints and wherein the heat fused seams or joints of a resulting polypropylene bag retains at least 85% of the fabric strength without using sewing machines.

A friction stir welding method using a resin composition including: a monomer (A) having an ethylenically unsaturated bond; a thermosetting resin (B); a radical polymerization initiator (C); and a fiber reinforcing material (D), wherein the thermosetting resin (B) is an unsaturated polyester resin or a vinyl ester resin.

A compound heat seal structure that, when heat-sealing a bag with a stacked area level difference, reliably seals even a section having different level and that can be easily opened. A compound heat seal structure is provided as a peelable seal in a band shape on a bag and a linear heat seal is added as a peelable seal in that band-shaped peelable heat seal in the longitudinal direction thereof.

A connection including a first profile having a first end and a first lumen, the first profile including a first polymeric material and a second profile having a second end and a second lumen, the second profile including a second polymeric material, a metal, or combination thereof, wherein the first end and the second end are coincidently welded via an ionized gas treatment.

A connection includes: a first profile having a first end, the first profile including a first polymeric material comprising a thermoset material; and a second profile having a second end, the second profile including a second polymeric material, a metal, or combination thereof, wherein the first end and the second end are coincidently bonded without a bonding material at an interface of the first end and the second end.

Methods for applying high shrink wrap labels to a shaped article are disclosed. The leading edge of the label is bonded to the article. A seaming agent is applied, and the label is wrapped around the article. The seaming agent is then exposed to radiation to cure the seaming agent, and the label is then exposed to heat to cause heat-shrinking. The label is made of a film with at least one external layer that has a Hildebrand solubility parameter. The seaming agent includes a component having a Hildebrand solubility parameter that is within 2.2 MPa.sup.1/2 or within 4.4 calories.sup.1/2.Math.cm.sup.3/2 of the Hildebrand solubility parameter of the external layer of the film. The seaming agent also has a viscosity of at least 1 centipoise and less than 1000 centipoise when measured at any temperature between ambient temperature and 60 C. Articles including such affixed high shrink wrap labels are also disclosed.

Disclosed is a resin composition for an exterior material of a vehicle. The resin composition may include an amount of about 40 to 90 parts by weight of polypropylene resin having a melt index of about 70 to 110 g/10 min; an amount of about 10 to 40 parts by weight of an olefin block copolymer including an ethylene-based repeating unit and a -olefin-based repeating unit having 4 to 30 carbon atoms; an amount of about 10 to 20 parts by weight of needle-shaped inorganic filler having an aspect ratio of about 5 to 10; and an 0.01 to 5 parts by weight of laser-transmitting black colorant, wherein all the parts by weights based on 100 parts by weight of the resin composition. In particular, an average transmittance may range from about 0.01 to about 1% or less in a wavelength of about 380 to 700 nm, and an average transmittance may range from about 15% or greater and less than about 100% in a wavelength of about 800 to 1200 nm.