The present disclosure provides processes for producing polyethylene resins. In at least one embodiment, a polyethylene has: a density of from about 0.91 g/cm.sup.3 to about 0.94 g/cm.sup.3; a value of Mz of about 1,500,000 g/mol or greater; and a ratio of Mz to Mw of about 7 or greater. A process includes introducing a first feed stream having ethylene monomer and a first free radical initiator to a first inlet of a first reaction zone, where the first reaction zone has a first inlet temperature. The process further includes introducing a second feed stream having ethylene monomer and a second free radical initiator to a second inlet of a second reaction zone, where the second reaction zone has a second inlet temperature that is the same or different than the first inlet temperature.

Provided is a fluorine-based resin multilayer film for vacuum forming which does not cause wrinkles and the like when a three-dimensional surface decoration method is applied. The fluorine-based resin multilayer film for vacuum forming includes a front surface layer containing 60% by mass to 85% by mass of a vinylidene fluoride-based resin and 40% by mass to 15% by mass of a methacrylate ester-based resin; and a back surface layer containing 0% by mass to 50% by mass of a vinylidene fluoride-based resin and 100% by mass to 50% by mass of a methacrylate ester-based resin, wherein the thermal dimensional change in a film flow direction when heated at 120° C. for 30 minutes, which is measured based on JIS K7133, is −15% to −2%.

Nanofiber spinning apparatuses and methods for making core-sheath materials using touch spinning are provided. The apparatus includes at least one rotating plate with an aperture through which a core yarn passes and at least one post contacting the rotating plate. A speed control device can be configured to control rotation of the rotating plate, and a dispensing device can be configured to dispense a nanofiber-forming material onto the post. To make a core-sheath yarn a core yarn is passed through an aperture in a rotating plate having at least one post. The post is contacted with a nanofiber-forming material the rotating plate is rotated to draw a fiber of nanofiber-forming material from the post to wrap the fiber around the core yarn.

A color 3D printer and its method of use are disclosed. The color 3D printer uses a number of chambers to dye a filament to a given color. This colored filament is then extruded, pursuant to an associated 3D model of an object, to produce varying colored physical objects, on demand, with the use of a single filament and a single print head. Further, the color 3D printer features a waste management apparatus which provides a number of ways to dispose of waste fluid.

An additive manufacturing system configured to a 3D print using a metal wire material includes a drive mechanism configured to feed the metal feedstock into an inlet tube and a liquefier. The liquefier has a chamber configured to accept the metal feedstock from the inlet tube. The metal feed stock is heated in the chamber such that a melt pool is formed in the chamber. The liquefier has an extrusion tube in fluid communication with the chamber, the extrusion tube having a length (L) and a diameter (D) wherein the ratio of length to diameter (L/D) ranges from about 4:1 to about 20:1. The system has a platen with a surface configured to accept melted material from the liquefier, wherein the platen and the liquefier move in at least three dimensions relative to each other. The system includes a regulated source of pressurized inert gas flowably coupled to the liquefier and configured to place a controlled positive pressure onto the melt pool sufficient to overcome the resistance of the extrusion tube such that a part may be formed by the extrusion of the liquidus metal along toolpaths defined by the relative motion of the liquefier and the platen.

Methods of making polytetrafluoroethylene (PTFE)/polymer composites are disclosed herein. The products can be used in the field of bio- and medical applications, such as for use in artificial blood vessels, vascular grafts, cardiovascular and soft tissue patches, facial implants, surgical sutures, and endovascular prosthesis, and for any products known in the aerospace, electronics, fabrics, filtration, industrial and sealant arts.

A manufacturing system is disclosed herein. The manufacturing system includes one or more stations, a monitoring platform, and a control module. Each station of the one or more stations is configured to perform at least one step in a multi-step manufacturing process for a product. The monitoring platform is configured to monitor progression of the product throughout the multi-step manufacturing process. The control module is configured to dynamically adjust processing parameters of each step of the multi-step manufacturing process to achieve a desired final quality metric for the product.

A technique for planarizing build surfaces in three-dimensional printing includes the use of a three-dimensional printer having an extruder with a sensor mechanically coupled thereto, where the sensor is operable to sense a contact force between the extruder and a separate structure. In particular, the sensor may be used to measure the contact force at a plurality of locations across a build surface of the separate structure, so that a difference between the measured contact force at two or more locations can be identified. In response to the difference between the measured contact force at these locations, a control signal may be created to reduce the difference for planarizing the build surface, e.g., by fabricating a layer on the build surface that mitigates irregularities therein, by gap filling on the build surface, or by adjusting a parameter of the three-dimensional printer.

A method of manufacturing a polymer film includes melting a resin, extruding the melted resin through a die to produce a polymer film, shaping the polymer film, cooling the polymer film, capturing an image of a test pattern through the polymer film, calculating a modulation transfer function value from the image, and adjusting a process parameter of the melting, the extruding, the shaping, or the cooling based on the calculated modulation transfer function value.

A method for forming a multilayer plastic sheet material (1) for floor and/or wall panels, wherein a first polymer mass comprising a rigid PVC is melted under pressure and is passed through an extruder head at a specified discharge rate in the form of a plastic strand in sheet form that is provided with one or more layers so that a multilayer plastic strand is formed, which is passed to two or more rolls of a finishing stand, which processes the multilayer plastic strand into a sheet of defined thickness, which is then led away via a transport device to a sawing device to be cut to the desired length, wherein, after the plastic strand in sheet form leaves the extruder head, it is first passed between a top roll and a bottom roll of a roughing stand, wherein the speed of the rolls of the finishing stand and the rolls of the roughing stand is synchronized with the discharge rate of the plastic strand in sheet form from the extruder head, so that said plastic strand is processed without stress.