A powdered catalyst material on a titanium oxide basis. The powdered catalyst material includes a combined content of at least 90 wt.-% of a hydrated titanium oxide having the general formula TiO.sub.(2-x)(OH).sub.2x, with 0<x≤1, (calculated as TiO.sub.2), and a silicon dioxide and hydrated precursors of the silicon dioxide (calculated as SiO.sub.2). A weight ratio of TiO.sub.2/SiO.sub.2, determined for TiO.sub.2 and SiO.sub.2 respectively, is at least 3 and less than 30. The wt.-% is based on a total weight of the catalyst material after the catalyst material has been dried at 105° C. for at least 2 hours. The powdered catalyst material has a specific surface area of >300 m.sup.2/g and an isoelectric point of from 4.0 to 7.0.

A catalyst for use in chemical looping combustion is provided. The catalyst includes a mixture of metal oxides dispersed on a ceramic support. The mixture of metal oxides forms a nickel tungsten oxide (NiWO.sub.4) interaction complex which functions as an oxygen carrier in the chemical looping combustion reaction.

The present invention addresses to a catalyst, and the method for obtaining the same, for generating hydrogen and/or syngas. More specifically, the present invention describes a catalyst based on nickel, molybdenum and tungsten, for steam reforming processes of natural gas or other hydrocarbon streams (refinery gas, propane, butane, naphtha or any mixture thereof) that presents high resistance to deactivation by coke deposition. According to the present invention, the catalyst has NiMoW as its active phase, in bulk form and/or supported on an alumina oxide and other high surface area oxide supports, and may also contain other promoters. Furthermore, the present invention teaches the production of a catalyst whose active phase of NiMoW has high activity for hydrocarbon steam reforming reaction.

The present disclosure provides for methods for designing and constructing metal/semiconductor heterostructures as catalysts for a wide range of applications such as oxygen activation. In a particular aspect, the present disclosure provides for the manipulation of atomic structures at MJ/TiO.sub.2 interface (e.g., Au/TiO.sub.2 interface) that significantly alters the interfacial electron distribution and prompts O.sub.2 activation. In an aspect, the present disclosure provides for a M/TiO.sub.2 composites (e.g., heterostructures) having a N defect-free M/TiO.sub.2 interface and method of making the M/TiO.sub.2 composites having a defect-free M/TiO.sub.2 interface. The M can be Au, Ag, Cu, Al, Pt, Ni, or Pd, for example.

The present invention relates to a novel heterogeneous catalyst for selective carbon dioxide methanation reaction having high activity and long-term stability, wherein the catalyst comprising of at least one alkali promoter metal, active metals selected from Nickel and Iron and a stable support for active metals having combination of CeO.sub.2 \-γAl.sub.2O.sub.3.Further, the present invention provides a process for synthesis of said catalyst. Secondly, the present invention also provides a sustainable process for synthesis of methane using said novel heterogenous catalyst. The benefits of present invention are that it provides a sustainable CO.sub.2 methanation process as the novel outstanding catalyst having high performance and long-term stability and totally eliminates catalyst regeneration or reloading step due to its very long-term stability for > 1000 h.

The present disclosure provides an exhaust gas purification material and an exhaust gas purification device that can efficiently remove harmful components even after being exposed to high temperature. Such exhaust gas purification material comprises metal oxide particles and noble metal particles supported on the metal oxide particles. The noble metal particles have a particle size distribution with a mean of 1.5 nm and 18 nm and a standard deviation of less than 1.6 nm.

A process for the production of an ester product from a mixture of at least two different ester compounds includes the steps of mixing together at least two different starting ester compounds to form a first ester mixture; and contacting the first ester mixture with a catalyst including from 30-60% of calcium oxide and at least one second metal oxide at a temperature of at least 180° C., for a duration of at least one hour, with mixing, to form a second ester mixture having a melting point which is lower than the melting point of the first ester mixture.

The present invention is directed to multifunctional nanomaterials for photothermal heating and catalytic applications. The present invention discloses a method of photothermally heating a solution. The present method also discloses a method of catalyzing a reaction. Both methods require a step of exposing a solution to at least one wavelength of the electromagnetic spectrum. A gold-iron oxide nanomaterial comprising an iron oxide substrate and discrete gold particles deposited on the substrate is also disclosed.

The present invention relates to a metal oxide coated composite comprising a core consisting of a mixture of a La stabilised AI.sub.2O.sub.3 phase and an Ce/Zr/RE.sub.2O.sub.3 mixed oxide phase, the core having a specific crystallinity, specific pore volume and a specific pore size distribution, and a method for the production of the metal oxide coated composite.

The invention relates to a method for preparing a catalyst or catalyst precursor comprising a catalytically active material and a carrier material. The invention relates to a catalyst particle and catalyst precursor thereof obtainable by said method. The catalyst may be used in a process for synthesising hydrocarbons.