To provide a biaxially oriented polyamide-based resin film being excellent in laminate strength, pin-hole resistance under a low-temperature environment, impact resistance, and transparency, and which retains satisfactory a good external appearance even after being sterilized in hot water. A biaxially oriented polyamide-based resin film comprising a polyamide resin and 1 to 5% by mass of a polyamide-based block copolymer, wherein the polyamide-based block copolymer comprises a hard part including a residue of cyclic lactam having 4 to 10 carbon atoms, and a soft part including a residue of polyoxypropylene glycol or polyoxytetramethylene glycol having a weight average molecular weight of 500 to 3000, and the content X of the hard part and the content Y and the weight average molecular weight Mw of the soft part satisfy the following formulae (1) and (2):
X+Y=100(parts by mass)(1)
478.74Mw.sup.0.2989Y93(parts by mass)(2).

A method of forming a film of photonic crystal material. A first process is performed upon a material capable of having a photonic crystal structure, this process causing deformation of the material so as to form a film in which incident light received by the material is selectively reflected or transmitted to generate a first optical effect in the film. A second process is performed upon substantially all of the film which applies a shear stress to the film. This causes a change in the material structure so as to generate a second optical effect in the film, different from the first optical effect, in response to incident light. Security films, devices, articles and documents formed using the method are also discussed.

[Problem] To provide polypropylene for a microporous film having excellent heat resistance and strength. [Solution] Polypropylene for a microporous film satisfying the following requirements (1) and (2): (1) the weight-average molecular weight (Mw) value, as determined by gel permeation chromatography (GPC), is not less than 100,000 but less than 800,000, the value (Mw/Mn) obtained by dividing the weight-average molecular weight by the number-average molecular weight is more than 7.0 but not more than 12.0, and the value (Mz/Mw) obtained by dividing the Z-average molecular weight by the weight-average molecular weight is not less than 3.8 but not more than 9.0, and (2) the mesopentad fraction, as measured by .sup.13C-NMR (nuclear magnetic resonance method), is not less than 95.5%.

Apertured elastic films include a polyolefin, a styrene block copolymer, a non-styrene block copolymer, or a combination thereof. Methods for forming polymeric films and articles of manufacture prepared therefrom are described.

Stretched elastic films include a polyolefin, a styrene block copolymer, a non-styrene block copolymer, or a combination thereof. Methods for forming polymeric films and articles of manufacture prepared therefrom are described

Provided is a film for packaging chemicals which does not change in appearance (e.g. yellowing), or does not generate odor, even after long-term storage; which is prevented from being scratched or contaminating rolls when the film is drawn from a roll thereof; and which expresses excellent chemical resistance. Also provided is a film for packaging chemicals which is easily detachable from a heat seal plate when contents are packed and sealed therein. The film for packaging chemicals includes polyvinyl alcohol; and a surfactant, the amount of the surfactant being 0.9% to 5% by mass based on 100% by mass of the polyvinyl alcohol, the surfactant having a polyoxyethylene structure, the number of moles of oxyethylene groups in the surfactant being 5 to 13 mol, the surfactant having a HLB of 9 to 14.5.

A producing method of a power storage device includes roll pressing a mixture laminated portion of a wide strip-shaped electrode plate, non-laminated-portion stretching of stretching a pair of mixture non-laminated portions of the wide strip-shaped electrode plate in a longitudinal direction, laminated-portion stretching of stretching a pair of mixture non-laminated-portion-side sections of the mixture laminated portion located on the mixture non-laminated portion side, cutting the wide strip-shaped electrode plate at a center of a width direction in the longitudinal direction to divide into two strip-shaped electrode plates, winding up the two strip-shaped electrode plates around winding cores with applying tensile force in the longitudinal direction in a roll-like shape to form electrode rolls, and storing each of the electrode rolls.