Two workpieces 30, 40 are joined by means of ultrasound. First, a workpiece 30 with at least one energy direction sensor 31 and a second workpiece 40 are provided. The workpieces are brought into contact with each other in such a way that the energy direction sensor 31 comes into contact with a first surface 41 of the second workpiece 40. Ultrasonic vibrations are then introduced into one of the workpieces 40 via a working surface 11 of a sonotrode 10. A sonotrode 10 is used, which has a contour with contact lines 12 on the working surface 11. The sonotrode 10 is positioned with respect to the first workpiece 30 in such a way that the contact lines 12 run transversely to the energy direction generator 31.

A system for simultaneously forming and filling a polymeric container with a product. The system includes a mold defining a container profile and a mold vacuum vent extending from the container profile to an upper surface of the mold. A striker plate is secured to the upper surface of the mold. The striker plate defines a striker vacuum vent that aligns with the mold vacuum vent to allow some of the product to be pulled by vacuum out of the mold through the mold vacuum vent and the striker vacuum vent.

Provided is a polymer composition for manufacturing a large container that contains high-density polyethylene recycled from a secondary battery separator and has excellent mechanical properties. Specifically, a polymer composition having excellent processability may be prepared by recycling a secondary battery separator, and an eco-friendly large container having excellent mechanical properties such as a flexural modulus, an elongation, and an impact strength in a wide temperature range, and having an excellent environmental stress cracking resistance may be manufactured by molding the polymer composition.

There is provided a co-injection molded multilayer structure comprising a barrier layer and outer layers laminated to contact with the barrier layer on its both sides, wherein the barrier layer is made of a resin composition (X) comprising an ethylene-vinyl alcohol copolymer (A) and an alkali metal salt (B) of a higher fatty acid, having a melting point of 250° C. or lower; the ethylene-vinyl alcohol copolymer (A) has an ethylene unit content of 20 to 60 mol % and a saponification degree of 90% or more, and a content of the alkali metal salt (B) in the barrier layer is 50 to 1500 ppm in terms of metal atoms; and the outer layers are made of a resin composition (Y) comprising an unmodified high-density polyethylene (F) and a maleic anhydride-modified polyethylene (G), and a maleic anhydride modification rate relative to the whole resin composition (Y) is 0.005 to 0.1 wt %. This co-injection molded multilayer structure has excellent adhesiveness, so that its oxygen barrier performance can be maintained even after being subjected to an impact due to falling or the like.

Disclosed are compositions and methods for multilayer films, which, in one embodiment may comprise a core layer comprising at least 50 wt. % of high-density polyethylene. Further, the multilayer film may include a first skin layer comprising at least 80 wt. % of high-density polyethylene, and a second skin layer comprising either: (i) one or more low-density polyethylenes; or (ii) one or more polypropylene-based copolymers. The multilayer film may be oriented in at least one direction.

An injection stretch blow-molded (ISBM) container prepared by way of injection molding a tubular preform followed by reheating and concurrently stretching and blow-molding the heated preform into the container. The container and preform comprise from 70 wt. % to 97.5 wt. % of a semi-crystalline polyolefin composition comprising one or polymers selected from polyethylene polymers and polypropylene polymers and from 2.5 wt. % to 30 wt. % of an alicyclic polyolefin composition, wherein the alicyclic polyolefin composition has a glass transition temperature, Tg, of from 60° to 145° C.

The present disclosure provides a fitment. In an embodiment, a fitment is provided and includes a top portion, a base, and a channel extending through the top portion and the base for passage of a flowable material. The fitment is composed of a polymeric composition. The polymeric composition includes (i) from 70 to 90 weight percent of a high density polyethylene (HDPE) having a density from 0.940 g/cc to 0.970 g/cc, a melt temperature, Tm, greater than 125° C., and a melt index from 1 g/10 min to 50 g/10 min; and (ii) from 30 to 10 weight percent of an olefin-based elastomer having a density from 0.860 g/cc to 0.905 g/cc, a melt index from 0.2 g/10 min to 50 g/10 min, and a Tm less than 125° C.

The present disclosure provides a fitment. In an embodiment, a fitment is provided and includes a top portion, a base, and a channel extending through the top portion and the base for passage of a flowable material. The fitment is composed of a polymeric composition. The polymeric composition includes (i) from 70 to 90 weight percent of a high density polyethylene (HDPE) having a density from 0.940 g/cc to 0.970 g/cc, a melt temperature, Tm, greater than 125° C., and a melt index from 1 g/10 min to 50 g/10 min; and (ii) from 30 to 10 weight percent of an olefin-based elastomer having a density from 0.860 g/cc to 0.905 g/cc, a melt index from 0.2 g/10 min to 50 g/10 min, and a Tm less than 125° C.

The present invention relates to a recycling process for a laminate and a solution used in such a process. The present invention finds particular application in the removal of an adhered overlay from an underlying substrate material such as plastic. The process includes subjecting the laminate to an impact frictional striking force, thereby substantially separating the substrate layer from the one or more surface layers of the overlay and then washing the substrate layer with a washing solution to remove the remaining surface layers of the overlay and glue from the substrate layer. The washing solution may be an aqueous solution including a surfactant, a solvent and a base.

A method for fabrication of a 3D printed part with high through-plane thermal conductivity is provided, where pure polymer particles and a carbon-based filler for heat conduction are subjected to milling and mixing in the mechanochemical reactor disclosed in Chinese patent ZL 95111258.9 under the controlled milling conditions including milling pan surface temperature, milling pan pressure, and number of milling cycles; then a resulting mixture is extruded to obtain 3D printing filaments; and finally, the 3D printing filaments are used to fabricate the 3D printed part with high through-plane thermal conductivity through fused deposition modeling (FDM) 3D printing. The fabrication method can realize the fabrication of a 3D printed part with high through-plane thermal conductivity through the FDM 3D printing technology, features simple process, continuous production, etc., and is suitable for the industrial production of thermally-conductive parts with complex structures.