A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3), where said parts by weight are based upon 100 parts of the binder system.

A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3), where said parts by weight are based upon 100 parts of the binder system.

The subject matter of the invention is mold material mixtures for producing molds or cores for metal casting, consisting of at least one refractory base mold material, a binder and an additive based on factice. The invention also relates to a component system, a method for producing molds and cores using the mold material mixtures or the component system respectively, and to molds and cores produced by said method.

A release agent is disclosed for use with an organic binder system used in metal casting. The binder system has a Part I component including an epoxy resin and a free radical initiator and a Part II component having an epoxy resin and an acrylate, where the Part I and Part II components are kept separate until the time of use. The release agent will typically have a molecular weight in the range of 150 to 160, with eight to ten carbon atoms. Two examples of the epoxide are pinene oxide and decene-1 oxide, each of which is effective as an internal release agent when present in the binder for a cold box process in the range of about 0.15% to about 1% of the total weight of the Part I and Part II components.

The invention relates to a method of producing an article selected from the group consisting of casting mold, core, feeder and molding compound for production of part of a casting mold, core or feeder, comprising the following steps: (S1) producing or providing in the foundry: a first component (A), comprising a first binder component (b1) of a binder system and an amount of a first mold base material and, spatially separated therefrom, a second component (B), comprising a second binder component (b2) of the binder system and an amount of a second mold base material wherein the first binder component (b1) and the second binder component (b2) are suitable for chemical reaction with one another and for curing of a mixture of the first component (A) and the second component (B), (S2) mixing by contacting the first component (A) and the second component (B) in a particular mass ratio, so as to result in a self-curing molding compound.

The present disclosure relates slip techniques for lost casting cores. The teachings thereof may be embodied in methods for producing a slip for use in casting, e.g., for production of complex metal blades in gas turbines. Some embodiments may include methods for producing a slip comprising: mixing at least one inorganic constituent with at least one first binder; and forming a slip with the mixture. The first binder may include a mixture of at least one epoxy resin and at least one sterically hindered amine as hardener.

A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3), where said parts by weight are based upon 100 parts of the binder system.

A foundry mix includes a major amount of a foundry aggregate and an effective binding amount of a binder system. The foundry binder system cures in the presence of sulfur dioxide and a free radical initiator. The binder system may include (1) 10 to 70 parts by weight of an epoxy novolac resin; (2) 0.5 to 10 parts by weight of resorcinol; (3) 20 to 70 parts by weight of a monomeric or polymeric acrylate; and (4) an effective amount of a free radical initiator. Notably, (1), (2), (3) and (4) are separate components or mixed with another of said components, provided (4) is not mixed with (3) until a foundry mix is to be created, where said parts by weight are based upon 100 parts of the binder system.