Systems and methods for low-manganese welding alloys are disclosed. An example arc welding consumable that forms a weld deposit on a steel workpiece during an arc welding operation, wherein the welding consumable comprises: less than 0.4 wt % manganese; strengthening agents selected from the group consisting of nickel, cobalt, copper, carbon, molybdenum, chromium, vanadium, silicon, and boron; and grain control agents selected from the group consisting of niobium, tantalum, titanium, zirconium, and boron, wherein the grain control agents comprise greater than 0.06 wt % and less than 0.6 wt % of the welding consumable, wherein the weld deposit comprises a tensile strength greater than or equal to 70 ksi, a yield strength greater than or equal to 58 ksi, a ductility, as measured by percent elongation, that is at least 22%, and a Charpy V-notch toughness greater than or equal to 20 ft-lbs at 20 F., and wherein the welding consumable provides a manganese fume generation rate less than 0.01 grams per minute during the arc welding operation.

A flux-cored wire for gas-shielded arc welding has a steel outer sheath filled with a flux. The flux-cored wire includes specific amounts, relative to a total mass of the wire, of TiO.sub.2, at least one of Si, an Si oxide and an Si compound, C, Mn, Mo, Ni, at least one of metal Mg and an Mg alloy, an F compound, a K compound, an Na compound, B and a B compound, and Fe, respectively. A total content of each of Ti and a Ti alloy, metal Al and an Al alloy, and V is restricted to the specific range, respectively. A content of Ti is also restricted to the specific range relative to the total mass of the steel outer sheath.

The present invention relates to a method for arc-welding a steel plate having a C content of 0.08-0.30% by mass, wherein the arc welding method comprises welding under a condition whereby X represented by formula (1) is 200 or less using a welding wire in which the total content of Cr and Ni thereof is 1.00% by mass or greater. (1): X=0.8(300-279[C].sub.W-25[Si].sub.W-35[Mn].sub.W-49[Ni].sub.W-47[Cr].sub.W-61[Mo].sub.W) +0.2(300-279[C].sub.BM-25[Si].sub.BM-35[Mn].sub.BM-49[Ni].sub.BM-47[Cr].sub.BM-61[Mo].sub.BM) (where [C].sub.W, [Si].sub.W, [Mn].sub.W, [Ni].sub.W, [Cr].sub.W, [Mo].sub.W, [C].sub.BM, [Si].sub.BM, [Mn].sub.BM, [Ni].sub.BM, [Cr].sub.BM, and [Mo].sub.BM are defined in the specification).

A gas-shielded flux cored welding electrode comprises a ferrous metal sheath and a core within the sheath enclosing core ingredients. The core ingredients and sheath together comprise, in weight percentages based on the total weight of the core ingredients and the sheath: 0.25 to 1.50 manganese; 0.02 to 0.12 carbon; 0.003 to 0.02 boron; 0.2 to 1.5 silicon; 0 to 0.3 molybdenum; at least one of titanium, magnesium, and aluminum, wherein the total content of titanium, magnesium, and aluminum is 0.2 to 2.5; 3 to 12 titanium dioxide; at least one arc stabilizer, where the total content of arc stabilizers is 0.05 to 1.0; no greater than 10 of additional flux system components; remainder iron and incidental impurities.

A solder ball according to the present invention contains 0.2 to 2.2% by mass of Zn, and a balance of Sn, and has a spherical diameter of 0.1 to 120 m and a yellowness (b*) in an L*a*b* color system of 2.70 or more and 9.52 or less. An oxide film is formed by performing aging treatment. By producing a solder ball having a yellowness of 2.70 or more and 9.52 or less, it is possible to suppress the growth of a Cu.sub.3Sn layer and/or a CuZn(Sn) layer during joining.

Systems and methods for low-manganese welding alloys are disclosed. An example arc welding consumable may comprise: between 0.4 and 1.0 wt % manganese; strengthening agents selected from the group consisting of nickel, cobalt, copper, carbon, molybdenum, chromium, vanadium, silicon, and boron; and grain control agents selected from the group consisting of niobium, tantalum, titanium, zirconium, and boron. The grain control agents may comprise greater than 0.06 wt % and less than 0.6 wt % of the welding consumable. The resulting weld deposit may comprise a tensile strength greater than or equal to 70 ksi, a yield strength greater than or equal to 58 ksi, a ductility (as measured by percent elongation) of at least 22%, and a Charpy V-notch toughness greater than or equal to 20 ft-lbs at ?20? F. The welding consumable may provide a manganese fume generation rate less than 0.01 grams per minute during the arc welding operation.

Systems and methods for low-manganese welding alloys are disclosed. An example arc welding consumable may comprise: between 0.4 and 1.0 wt % manganese; strengthening agents selected from the group consisting of nickel, cobalt, copper, carbon, molybdenum, chromium, vanadium, silicon, and boron; and grain control agents selected from the group consisting of niobium, tantalum, titanium, zirconium, and boron. The grain control agents may comprise greater than 0.06 wt % and less than 0.6 wt % of the welding consumable. The resulting weld deposit may comprise a tensile strength greater than or equal to 70 ksi, a yield strength greater than or equal to 58 ksi, a ductility (as measured by percent elongation) of at least 22%, and a Charpy V-notch toughness greater than or equal to 20 ft-lbs at ?20? F. The welding consumable may provide a manganese fume generation rate less than 0.01 grams per minute during the arc welding operation.

A flux-cored wire for gas shielded arc welding may contain, based on total mass of the wire: Fe: 78 mass % or more; TiO.sub.2: 4 mass % to 13 mass %; Mn: 1.0 mass % to 2.4 mass %; Cr: 1.0 mass % to 3.0 mass %; Mo: 0.2 mass % to 1.2 mass %; Si: 0.1 mass % to 0.8 mass %; Mg: 0.1 mass % to 1.0 mass %; fluoride (F conversion value): 0.05 mass % to 0.25 mass %; C: 0.01 mass % to 0.10 mass %; V: 0.003 mass % to 0.020 mass %; Nb: 0.003 mass % to 0.020 mass %; and B: less than 100 ppm (including 0 ppm). The contents of Mn, C, and V based on total mass of the wire may satisfy a relationship of 28?Mn/(390?C+2370?V)?0.82.

This disclosure relates generally to welding and, more specifically, to electrodes for arc welding, such as Gas Metal Arc Welding (GMAW) or Flux Core Arc Welding (FCAW) of zinc-coated workpieces. In an embodiment, a welding consumable for welding a zinc-coated steel workpiece includes a zinc (Zn) content between approximately 0.01 wt % and approximately 4 wt %, based on the weight of the welding consumable. It is presently recognized that intentionally including Zn in welding wires for welding galvanized workpieces unexpectedly and counterintuitively alleviates spatter and porosity problems that are caused by the Zn coating of the galvanized workpieces.

Molybdenum is alloyed into stainless steel surface by electro-spark deposition technique. Shielding gas is used during electro-spark deposition process to minimize the oxidation of materials. Control of electro-spark voltage, frequency, capacitance, time can determine the alloying depth of Molybdenum. The alloyed surface thickness varies from 5 m to 80 m depending on the electro-spark deposition parameters. The alloyed surface comprises, by weight, 15 to 40% of Molybdenum, 8 to 22% of Cr, 0-15% of other alloy elements and impurities. The molybdenum alloyed stainless steel surface exhibits improvement in micro-hardness, wear resistance, and especially corrosion resistance in sodium chloride solutions. Thus, the present invention would be utilized in marine and handling of brines application, as well as in other applications which better corrosion resistance of stainless steel is desired.