A cerium-zirconium based mixed oxide composition have: (a) a Ce:Zr molar ratio of 1 or less, and (b) a cerium oxide content of 10-50% by weight. The composition has (i) a surface area of at least 18 m.sup.2/g, and a total pore volume as measured by N.sub.2 physisorption of at least 0.11 cm.sup.3/g, after ageing at 1100° C. in an air atmosphere for 6 hours, (ii) a surface area of at least 42 m.sup.2/g, and a total pore volume as measured by N.sub.2 physisorption of at least 0.31 cm.sup.3/g, after ageing at 1000° C. in an air atmosphere for 4 hours, and (iii) Dynamic Oxygen Storage Capacity (D-OSC) value as measured by H.sub.2-TIR of greater than 500 μmol/g at 600° C. after aging at 800° C. in an air atmosphere for 2 hours. A process contacts the exhaust gas with the composition Another process is for preparing the composition.

A cerium-zirconium based mixed oxide composition have: (a) a Ce:Zr molar ratio of 1 or less, and (b) a cerium oxide content of 10-50% by weight. The composition has (i) a surface area of at least 18 m.sup.2/g, and a total pore volume as measured by N.sub.2 physisorption of at least 0.11 cm.sup.3/g, after ageing at 1100° C. in an air atmosphere for 6 hours, (ii) a surface area of at least 42 m.sup.2/g, and a total pore volume as measured by N.sub.2 physisorption of at least 0.31 cm.sup.3/g, after ageing at 1000° C. in an air atmosphere for 4 hours, and (iii) Dynamic Oxygen Storage Capacity (D-OSC) value as measured by H.sub.2-TIR of greater than 500 μmol/g at 600° C. after aging at 800° C. in an air atmosphere for 2 hours. A process contacts the exhaust gas with the composition Another process is for preparing the composition.

A ceramic powder for a ceramic component, in particular based on zirconia and/or alumina, in particular for a timepiece or jewelry piece. The powder includes at least one noble metal among platinum, rhodium, osmium, palladium, ruthenium and iridium, at a quantity of less than or equal to 5% by weight.

A ceramic powder for a ceramic component, in particular based on zirconia and/or alumina, in particular for a timepiece or jewelry piece. The powder includes at least one noble metal among platinum, rhodium, osmium, palladium, ruthenium and iridium, at a quantity of less than or equal to 5% by weight.

Disclosed herein are materials and processes for production of lithium oxide materials, such as lithium lanthanum zirconium oxide (LLZO), having a small particle size and high density for use in lithium-ion batteries. Some embodiments are directed to forming and then heating a multiphase material comprising lithium carbonate and La.sub.2Zr.sub.2O.sub.7 in the presence of hydrogen gas at a temperature below the melting point of the lithium carbonate, such that at least a portion of the lithium carbonate decomposes to form lithium oxide. In some embodiments, the lithium oxide is heated to a temperature sufficient to crystallize the lithium oxide to form the solid electrolyte material comprising lithium lanthanum zirconium oxide (LLZO) particles.

Disclosed herein are materials and processes for production of lithium oxide materials, such as lithium lanthanum zirconium oxide (LLZO), having a small particle size and high density for use in lithium-ion batteries. Some embodiments are directed to forming and then heating a multiphase material comprising lithium carbonate and La.sub.2Zr.sub.2O.sub.7 in the presence of hydrogen gas at a temperature below the melting point of the lithium carbonate, such that at least a portion of the lithium carbonate decomposes to form lithium oxide. In some embodiments, the lithium oxide is heated to a temperature sufficient to crystallize the lithium oxide to form the solid electrolyte material comprising lithium lanthanum zirconium oxide (LLZO) particles.

An acidified metal oxide (“AMO”) material, preferably in monodisperse nanoparticulate form 20 nm or less in size, having a pH<7 when suspended in a 5 wt % aqueous solution and a Hammett function H.sub.0>−12, at least on its surface. The AMO material is useful in applications such as a battery electrode, catalyst, or photovoltaic component.

An acidified metal oxide (“AMO”) material, preferably in monodisperse nanoparticulate form 20 nm or less in size, having a pH<7 when suspended in a 5 wt % aqueous solution and a Hammett function H.sub.0>−12, at least on its surface. The AMO material is useful in applications such as a battery electrode, catalyst, or photovoltaic component.

A cerium-zirconium oxide-based ionic conductor (CZOIC) material including zirconium oxide in an amount ranging from 5 wt. % up to 95 wt. %, cerium oxide in an amount ranging from 95 wt. % to 5 wt. %, and at least one oxide or a rare earth metal in an amount ranging from 30 wt. % or less, based on the overall mass of the CZOIC material. The CZOIC material exhibits a structure comprising one or more expanded unit cells and a plurality of crystallites having ordered nano-domains. The structure of the CZOIC material exhibits a crystal lattice defined by a d-value measured at multiple (hkl) locations using a SAED technique that exhibit distortions, such that the d-values for the same (hkl) location varies from about 2% to about 5% from the d-value measured for a reference cerium-zirconium material at the same (hkl) location.

Disclosed are methods of dehydrogenating a light alkane gas (and/or light alkene gas), which include adding hydrogen (H.sub.2) to the light alkane gas (and/or light alkene gas) in the presence of a catalyst composition containing zirconium oxide. Also disclosed are catalyst compositions containing zirconium oxide and methods of preparation thereof, where the catalyst compositions are useful in methods of dehydrogenating light alkane gas.