A zirconia-based porous body including an oxide of a rare earth element, in which when a pore volume in a pore distribution range of 30 nm or more and 200 nm or less after heating at 1150° C. for 12 hours under atmospheric pressure is defined as pore volume A and a pore volume in a pore distribution range of 30 nm or more and 200 nm or less before heating is defined as pore volume B, the pore volume A is 0.10 ml/g or more and 0.40 ml/g or less, and a pore volume retention ratio X in a pore distribution range of 30 nm or more and 200 nm or less represented by a formula [[(pore volume A)/(pore volume B)]×100] is 25% or more and 95% or less.

A method for producing mesoporous magnesium hydroxide nanoplates involving solvothermal treatment of a solution of a magnesium salt, a base, a glycol, and water is disclosed. The method does not use a surfactant or template in the solvothermal treatment. The method yields mesoporous nanoparticles of magnesium hydroxide having a plate-like morphology with a diameter of 20 nm to 100 nm, a mean pore diameter of 2 to 10 nm, a surface area of 50 to 70 m.sup.2/g, and a type-III nitrogen adsorption-desorption BET isotherm with a H3 hysteresis loop. An antibacterial composition containing the mesoporous magnesium hydroxide nanoplates is also disclosed. A method for reducing nitroaromatic compounds with a reducing agent and the mesoporous magnesium hydroxide nanoplates as a catalyst is also disclosed.

Provided are a nickel-manganese composite hydroxide capable of producing a secondary battery having a high particle fillability and excellent battery characteristics when used as a precursor of a positive electrode active material and a method for producing the same. A nickel-manganese composite hydroxide is represented by General Formula: Ni.sub.xMn.sub.yM.sub.z(OH).sub.2+α and contains a secondary particle formed of a plurality of flocculated primary particles. The primary particles have an aspect ratio of at least 3, and at least some of the primary particles are disposed radially from a central part of the secondary particle toward an outer circumference thereof. The secondary particle has a ratio I(101)/I(001) of a diffraction peak intensity I(101) of a 101 plane to a peak intensity I(001) of a 001 plane, measured by an X-ray diffraction measurement, of up to 0.15.

Porous metal oxide microspheres are prepared via a process comprising forming a liquid solution or dispersion of polydisperse polymer nanoparticles and a metal oxide; forming liquid droplets from the solution or dispersion; drying the liquid droplets to provide polymer template microspheres comprising polymer nanospheres and metal oxide; and removing the polymer nanospheres from the template microspheres to provide the porous metal oxide microspheres. The porous microspheres exhibit saturated colors and are suitable as colorants for a variety of end-uses.

The hydrogen storage product comprises one or more reduced-graphene oxide layers functionalized with a boron species and decorated with an alkali or alkaline earth metal. Each layer of the structure further comprises boron-oxygen functional groups comprising oxygen atoms bonded to boron atoms. The hydrogen storage product has a composition suitable for physisorption of hydrogen molecule, and operates to reversibly store hydrogen under operating conditions of low pressure and ambient temperature.

The present invention provides an iron-loaded aluminosilicate zeolite having a maximum pore opening defined by eight tetrahedral atoms and having the framework type CHA, AEI, AFX, ERI or LTA, wherein the iron (Fe) is present in a range of from about 0.5 to about 5.0 wt. % based on the total weight of the iron-loaded aluminosilicate zeolite, wherein an ultraviolet-visible absorbance spectrum of the iron-loaded synthetic aluminosilicate zeolite comprises a band at approximately 280 nm, wherein a ratio of an integral, peak-fitted ultraviolet-visible absorbance signal measured in arbitrary units (a.u.) for the band at approximately 280 nm to an integral peak-fitted ultraviolet-visible absorbance signal measured in arbitrary units (a.u.) for a band at approximately 340 nm is >about 2. The present invention further provides a method of making an metal-loaded aluminosilicate zeolite having a maximum pore opening defined by eight tetrahedral atoms from pre-existing aluminosilicate zeolite crystallites, wherein the metal is present in a range of from 0.5 to 5.0 wt. % based on the total weight of the metal-loaded aluminosilicate zeolite.

A method for preparing a nanoporous silica sol-gel matrix containing at least one amine reactant selected from hydroxylamine, methylhydroxylamine, tertbutylhydroxylamine, methoxyamine, tetraethylenepentamine, dicarboxylic acid dihydrazides, particularly adipic acid dihydrazide, and the salts thereof, said method including the following steps: a) synthesising a gel from tetramethoxysilane or from a mixture of tetramethoxysilane and another organosilicon precursor selected from among phenyltrimethoxysilane, phenyltriethoxysilane, a fluoroalkyltrimethoxysilane, a fluoroalkyltriethoxysilane, a chloroalkylmethoxysilane, a chloroalkylethoxysilane, an alkyltrimethoxysilane, an alkyltriethoxysilane, an aminopropyltriethoxysilane and the mixtures thereof, the synthesis being performed in an aqueous medium at a temperature ranging from 10 to 70° C. in the presence of at least one amine reactant selected from among hydroxylamine, methylhydroxylamine, tertbutylhydroxylamine, methoxyamine, dicarboxylic acid dihydrazides, particularly adipic acid dihydrazide, and the salts thereof; b) drying the gel obtained during step a) so as to obtain a sol-gel matrix containing at least one amine reactant.

A method for producing a hierarchical mesoporous beta includes mixing a beta zeolite with an aqueous metal hydroxide solution and heating the beta zeolite and the aqueous metal hydroxide mixture to produce a desilicated beta zeolite, contacting the desilicated beta zeolite with an ammonium salt solution to produce an intermediate hierarchical mesoporous beta zeolite, and treating the intermediate hierarchical mesoporous beta zeolite with an acidic solution to produce the hierarchical mesoporous beta zeolite. The hierarchical mesoporous beta zeolite includes a molar ratio of silicon to aluminum of greater than 12.5, a total pore volume of greater than or equal to the total pore volume of the intermediate hierarchical mesoporous beta zeolite, and an average mesopore size of greater than or equal to the average mesopore size of the hierarchical mesoporous beta zeolite. The method may also include calcining the intermediate hierarchical mesoporous beta zeolite.

One aspect of the present invention relates to a carbonaceous material having a BET specific surface area calculated from a nitrogen adsorption isotherm by a BET method, of 750 m.sup.2/g or more and 1000 m.sup.2/g or less, a ratio of a pore volume of pores of 0.3875 to 0.9125 nm calculated from the nitrogen adsorption isotherm by a HK method to a total pore volume calculated from the nitrogen adsorption isotherm by the HK method, of 80% or more, and an average pore diameter obtained by the following formula using the BET specific surface area and the total pore volume calculated from the nitrogen adsorption isotherm by the HK method, of 1.614 nm or less: D=4000×V/S (wherein D represents the average pore diameter (nm), V represents the total pore volume (mL/g), and S represents the specific surface area (m.sup.2/g)).

A powdered catalyst material on a titanium oxide basis. The powdered catalyst material includes a combined content of at least 90 wt.-% of a hydrated titanium oxide having the general formula TiO.sub.(2-x)(OH).sub.2x, with 0<x≤1, (calculated as TiO.sub.2), and a silicon dioxide and hydrated precursors of the silicon dioxide (calculated as SiO.sub.2). A weight ratio of TiO.sub.2/SiO.sub.2, determined for TiO.sub.2 and SiO.sub.2 respectively, is at least 3 and less than 30. The wt.-% is based on a total weight of the catalyst material after the catalyst material has been dried at 105° C. for at least 2 hours. The powdered catalyst material has a specific surface area of >300 m.sup.2/g and an isoelectric point of from 4.0 to 7.0.