Disclosed is a particle with a component (1) and a component (2), in which the component (2) covers at least a portion of the surface of the component (1), and the component (2) includes an organic silicon compound layer including a siloxane bond and an inorganic silicon compound layer including a siloxane bond.

In one aspect, composite nanoparticles are provided. In some embodiments, a composite nanoparticle comprises a host matrix comprising A.sub.4BX.sub.6-ZY.sub.Z and ABX.sub.3-PY.sub.P inclusions dispersed within the host matrix of the composite nanoparticle, wherein A is an alkali metal, B is an element selected from the group consisting of transition metals, Group IVA elements and rare earth elements and X and Y are independently selected from Group VIIA elements, 0≤z≤6, and 0≤p<3.

An infrared absorbing material fine particle dispersion liquid including infrared absorbing material fine particles and a solvent, the infrared absorbing material fine particles containing fine particles of composite tungsten oxide represented by a general formula MxWOy, the solvent containing water, wherein an absolute value of a zeta potential of the infrared absorbing material fine particle dispersion liquid is 5 mV or more and 100 mV or less.

The invention discloses a method of producing a filler composition to be used in paper or board production, said method comprising providing a suspension comprising calcium hydroxide and performing carbonation of the calcium hydroxide to form precipitated calcium carbonate (PCC). The invention is characterized in that starch and/or carboxy methyl cellulose (CMC) is added to the suspension during said carbonation of calcium hydroxide. The method of the invention enables an increased filler content in paper or paperboard without substantially increasing the dusting tendency or decreasing the strength of the paper or board.

A co-assembly method for synthesizing inverse photonic structures is described. The method includes combining an onium compound with a sol-gel precursor to form metal oxide (MO) nanocrystals, where each MO nanocrystal has crystalline and amorphous content. The MO nanocrystals are combined with templating particles to form a suspension. A solvent is evaporated from the suspension to form an intermediate or compound product, which then undergoes calcination to produce an inverse structure.

A method is provided for producing an article which is transparent to near-wave IR, mid-wave and Long-wave multi-spectral and IR wavelength in the region of 0.4 pm to 16 μm. The method includes the steps of (a) Producing ultra-fine powder of CaLa.sub.2S.sub.4 via SPLTS process, (b) followed by pretreatment of the ultra-fine powder under inert and reducing gas conditions including H.sub.2 or Argon or N.sub.2 or H.sub.2/H.sub.2S, H.sub.2S, and mixtures there of (c) followed by sieving the powder in 140 mesh screen and cold pressing the powder at 7000 psi for 7 min. into a disk shaped green body (d) then Cold-Isostatic Pressing (CIP) at 40,000 psi for 5 min in a rubber mold (e) finally sintered article of CaLa.sub.2S.sub.4 disk of 25.4 mm diameter with ultra-high density containing cubic phase of CaLa.sub.2S.sub.4 to yield IR transmission of a peak value of 57% within the IR wavelength range of 2 μm to 16 μm, either by using microwave sintering followed by hot isostatic press or spark plasma sintering followed by hot isostatic press or vacuum sintering at (3×10.sup.−6 torr) followed by hot isostatic press or hot press sintering followed by hot isostatic press and finally followed by mirror polished IR article, is obtained.

An object is to provide a quantum dot that has a narrow fluorescence half-width and a high fluorescence quantum yield, and emits blue fluorescence. A quantum dot (5) according to the present invention includes at least Zn and Se and does not include Cd, and has a particle diameter of 5 nm or more and 20 nm or less. In addition, the quantum dot (5) according to the present invention includes at least Zn and Se and does not include Cd, and has a fluorescence quantum yield of 5% or more and a fluorescence half-width of 25 nm or less. In the present invention, the fluorescence lifetime can be made 50 ns or less.

A method of producing a fluorescent nanodiamond exhibiting a zero phonon line (ZPL) for NV.sup.0 and/or NV.sup.− on its the fluorescence emission wavelength spectrum. The method includes a detonation step of exploding at least one type of explosive in an airtight container to obtain a nanodiamond raw material, a first annealing step of annealing, at a temperature from 1000° C. to 1600° C., the nanodiamond raw material or a nanodiamond which is obtained by removing sp2 carbon through strong acid treatment, ozone treatment, or gas-phase oxidation of the nanodiamond raw material, a vacancy forming step of creating vacancies on the nanodiamond by irradiating the nanodiamond with an ion beam or an electron beam after the first annealing step, and a second annealing step of annealing, at a temperature from 600° C. to 900° C., the nanodiamond containing vacancies to form Nitrogen-Vacancy (NV) centers.

An ink including at least one colloidal dispersion of particles and at least one metal halide binder, wherein the binder is a dissociated salt of metal and halogen. Also, a method for preparing a light-sensitive material, a light-sensitive material obtainable by the method, and a device including at least one light-sensitive material obtainable by the method.

A phosphor powder contains an EU-activated β-type sialon phosphor particles. When a median diameter in the phosphor powder having not been subjected to an ultrasonic homogenizer treatment is set as D1 and a median diameter in the phosphor powder having been subjected to an ultrasonic homogenizer treatment is set as D2, 1.05≤D1/D2≤1.70. A dispersion liquid in which 30 mg of the phosphor powder is uniformly dispersed in 100 ml of a 0.2% concentration of a sodium hexametaphosphate aqueous solution is added to a columnar container of which a bottom surface has an inner diameter of 5.5 cm. Then, the dispersion liquid is irradiated with ultrasonic waves for 3 minutes at a frequency of 19.5 kHz, and an output of 150 W, in a state where a cylindrical tip, which has an outer diameter of 20 mm, of an ultrasonic homogenizer is immersed in the dispersion liquid in ≥1.0 cm.