A method for forming cement-based cementitious material includes: pouring a cement paste into a mold; applying an electrical current to the cement paste to perform an electro-osmotic reaction; and transferring the reacted cement paste into a water tank for curing, thereby obtaining a functionally graded cement-based cementitious material. A pair of electrodes is placed in the mold and connected to an external power source. The compressive strength of the functionally graded cement-based cementitious material in the middle is lower than that at either of both ends.

A method for forming cement-based cementitious material includes: pouring a cement paste into a mold; applying an electrical current to the cement paste to perform an electro-osmotic reaction; and transferring the reacted cement paste into a water tank for curing, thereby obtaining a functionally graded cement-based cementitious material. A pair of electrodes is placed in the mold and connected to an external power source. The compressive strength of the functionally graded cement-based cementitious material in the middle is lower than that at either of both ends.

Foundry casting elements and methods of forming the same, the methods including: forming an aqueous slurry including an inorganic binder precursor, shaping the slurry using a pattern, curing the shaped slurry using a low temperature solidification process to form a casting element, and removing the pattern from the casting element.

Foundry casting elements and methods of forming the same, the methods including: forming an aqueous slurry including an inorganic binder precursor, shaping the slurry using a pattern, curing the shaped slurry using a low temperature solidification process to form a casting element, and removing the pattern from the casting element.

Disclosed herein are methods and compositions for cementing. An example method may comprise providing a cement composition. The cement composition may comprise a composite cementitious material comprising a micronized particulate solid and a monophase amorphous hydraulic binder. The micronized particulate solid may have a mean particle size of about 500 microns or less. The cement composition may further comprise water. The method may further comprise introducing the cement composition into a subterranean formation; and allowing the cement composition to set.

Disclosed herein are methods and compositions for cementing. An example method may comprise providing a cement composition. The cement composition may comprise a composite cementitious material comprising a micronized particulate solid and a monophase amorphous hydraulic binder. The micronized particulate solid may have a mean particle size of about 500 microns or less. The cement composition may further comprise water. The method may further comprise introducing the cement composition into a subterranean formation; and allowing the cement composition to set.

Provided is a method for producing a silica aerogel blanket having high thermal insulation and high strength, wherein an acicular metal-silica composite is added to a step of preparing a silica precursor solution during the production of the silica aerogel blanket to produce a silica aerogel blanket having characteristics of high thermal insulation, high strength, high thermal resistance and low dust.

Provided is a method for producing a silica aerogel blanket having high thermal insulation and high strength, wherein an acicular metal-silica composite is added to a step of preparing a silica precursor solution during the production of the silica aerogel blanket to produce a silica aerogel blanket having characteristics of high thermal insulation, high strength, high thermal resistance and low dust.

A sound insulating material, a sound insulating plate, and a partition structure of a train carriage are provided. The sound insulating material comprises the following components in weight ratio: 2-8 parts of tricalcium silicate; 4-10 parts of calcium hydroxide; 10-30 parts of aluminosilicate; 4-10 parts of alumina; 5-15 parts of iron oxide; 10-30 parts of a binder; and 5-10 parts of a curing agent, wherein the binder is at least two of lithium silicate, sodium silicate and calcium silicate; the curing agent is at least one of lithium oxide, magnesium oxide and silica; and the mixture of the aluminosilicate, alumina and iron oxide expands at 1000° C.-1350 ° C. to form particles. The sound insulating plate made of this material is lightweight and has a sound insulation capacity of 35-42 dB.

A sound insulating material, a sound insulating plate, and a partition structure of a train carriage are provided. The sound insulating material comprises the following components in weight ratio: 2-8 parts of tricalcium silicate; 4-10 parts of calcium hydroxide; 10-30 parts of aluminosilicate; 4-10 parts of alumina; 5-15 parts of iron oxide; 10-30 parts of a binder; and 5-10 parts of a curing agent, wherein the binder is at least two of lithium silicate, sodium silicate and calcium silicate; the curing agent is at least one of lithium oxide, magnesium oxide and silica; and the mixture of the aluminosilicate, alumina and iron oxide expands at 1000° C.-1350 ° C. to form particles. The sound insulating plate made of this material is lightweight and has a sound insulation capacity of 35-42 dB.