A method for producing a supplementary cementitious material (SCM) that includes providing a starting material containing dolomite and aluminium silicate, converting the starting material to the supplementary cementitious material by burning in the temperature range of >800 to 1100° C. or by burning in the temperature range of 725 to 950° C. in the presence of a mineralizer and cooling the supplementary cementitious material.

A method for producing aggregates from non-hardened cement compositions, in particular from concrete or residual concrete, which method includes adding a) a water-absorbing agent and b) a crystallization deactivator to a non-hardened cement composition and mixing until a granular material has formed. The method allows unneeded residues of still liquid concrete to be converted into a practical product, which can then be reused to produce new concrete compositions. The invention further relates to a granulated cement material that can be obtained according to a corresponding method, to the use of the granulated cement material as an additive for cement compositions, and to additive combinations for cement compositions, which additive combinations include a water-absorbing agent and a crystallization activator.

A method for producing aggregates from non-hardened cement compositions, in particular from concrete or residual concrete, which method includes adding a) a water-absorbing agent and b) a crystallization deactivator to a non-hardened cement composition and mixing until a granular material has formed. The method allows unneeded residues of still liquid concrete to be converted into a practical product, which can then be reused to produce new concrete compositions. The invention further relates to a granulated cement material that can be obtained according to a corresponding method, to the use of the granulated cement material as an additive for cement compositions, and to additive combinations for cement compositions, which additive combinations include a water-absorbing agent and a crystallization activator.

The present invention relates to an inorganic binder system comprising blast furnace slag, and at least one solid alkali metal silicate, wherein the inorganic binder system is obtainable by co-grinding a mixture comprising the blast furnace slag and the at least one solid alkali metal silicate.

The present invention relates to an inorganic binder system comprising blast furnace slag, and at least one solid alkali metal silicate, wherein the inorganic binder system is obtainable by co-grinding a mixture comprising the blast furnace slag and the at least one solid alkali metal silicate.

A concrete durability protection method is provided, including following steps: Step one: rinsing the concrete surface; Step two: spraying agent A material or alternately spraying agent B material and agent A material at the wet surface of the concrete; Step three: repeating step two. The beneficial effects of the present invention include: nanoscale active silicate penetrates into the concrete surface layer within a certain depth and reacts with free calcium ions within the concrete to form C—S—H crystalline, thereby improving the compactness of the concrete surface layer within a certain depth, repairing defects in the concrete surface layer within a certain depth, such as the capillary interstices, pores, microcracks, etc., so as to effectively improve the durability of concrete. The unreacted nanoscale active silicate material has permanent activity. It could recover its activity when the concrete absorbs moisture, and continue to react with free calcium ions in the concrete to quickly form C—S—H crystals, realizing the permanent concrete durability protection.

A concrete durability protection method is provided, including following steps: Step one: rinsing the concrete surface; Step two: spraying agent A material or alternately spraying agent B material and agent A material at the wet surface of the concrete; Step three: repeating step two. The beneficial effects of the present invention include: nanoscale active silicate penetrates into the concrete surface layer within a certain depth and reacts with free calcium ions within the concrete to form C—S—H crystalline, thereby improving the compactness of the concrete surface layer within a certain depth, repairing defects in the concrete surface layer within a certain depth, such as the capillary interstices, pores, microcracks, etc., so as to effectively improve the durability of concrete. The unreacted nanoscale active silicate material has permanent activity. It could recover its activity when the concrete absorbs moisture, and continue to react with free calcium ions in the concrete to quickly form C—S—H crystals, realizing the permanent concrete durability protection.

Water-based paint is used as a sacrificial agent to reduce the detrimental effect of carbon-containing fly ash on the entrainment of air in concrete. The invention provides a composition for reducing the effect of carbon contained in fly ash on air entrainment in cementitious mixtures comprising water, cement, fly ash and entrained air. The composition comprises water-based paint and one or more of pulverized or un-pulverized pozzolan, pulverized or un-pulverized cementitious solids, a superplasticizer, a defoamer, an air-entraining admixture, a water-reducing admixture, a retarding admixture, an accelerating admixture, a hydration control admixture and a rheology modifying admixture. The invention also provides a method of reducing the effect of carbon on air entrainment in carbon-containing fly ash, comprising mixing the fly ash with water-based paint.

Water-based paint is used as a sacrificial agent to reduce the detrimental effect of carbon-containing fly ash on the entrainment of air in concrete. The invention provides a composition for reducing the effect of carbon contained in fly ash on air entrainment in cementitious mixtures comprising water, cement, fly ash and entrained air. The composition comprises water-based paint and one or more of pulverized or un-pulverized pozzolan, pulverized or un-pulverized cementitious solids, a superplasticizer, a defoamer, an air-entraining admixture, a water-reducing admixture, a retarding admixture, an accelerating admixture, a hydration control admixture and a rheology modifying admixture. The invention also provides a method of reducing the effect of carbon on air entrainment in carbon-containing fly ash, comprising mixing the fly ash with water-based paint.

A method for manufacturing a binder of a hydratable material includes providing a starting material from one or more raw materials convertible by tempering at 600 to 1200° C. into the hydratable material and tempering the starting material to provide the hydratable material containing not more than 10% by weight monocalcium silicate and at least 15% by weight hydratable phases in the form of lime and dicalcium silicate. The residence time and the tempering temperature are adapted to obtain the hydratable material by converting not more than 80% by weight of the starting material, and the hydratable material is then cooled to provide the binder comprising the hydratable material. The binder can be mixed with water and optionally one or more of aggregate, additives, admixtures to obtain a binder paste that is placed, hydrated and carbonated to produce a building product.