The invention provides polypropylene compositions for producing soft nonwoven fabrics, consisting of at least three propylene-based copolymers differing in content of alpha-olefin comonomers. The provided fabrics are soft and pleasant to touch.

The invention is directed to a beta nucleated heterophasic propylene copolymer composition (HPPC).

The invention is directed to a beta nucleated heterophasic propylene copolymer composition (HPPC).

A polyethylene-based composition may include an ethylene-based copolymer produced from ethylene and one or more C3-C10 alpha olefin comonomers, wherein the ethylene-based copolymer has: a density ranging from 945 kg/m.sup.3 to 961 kg/m.sup.3 according to ASTM D792, a melt flow rate (MFR.sub.2) ranging from 0.5 g/10 min to 3.0 g/10 min according to ASTM D1238 at 190° C./2.16 kg, a molecular weight distribution (Mw/Mn) ranging from 3 to 25, and a stress exponent (SEx) ranging from 1.0 to 1.8.

A polyethylene-based composition may include an ethylene-based copolymer produced from ethylene and one or more C3-C10 alpha olefin comonomers, wherein the ethylene-based copolymer has: a density ranging from 945 kg/m.sup.3 to 961 kg/m.sup.3 according to ASTM D792, a melt flow rate (MFR.sub.2) ranging from 0.5 g/10 min to 3.0 g/10 min according to ASTM D1238 at 190° C./2.16 kg, a molecular weight distribution (Mw/Mn) ranging from 3 to 25, and a stress exponent (SEx) ranging from 1.0 to 1.8.

The invention relates to a pellet comprising a thermoplastic polymer sheath intimately surrounding glass filaments, which glass filaments are covered at least in part with an impregnating agent and extend in a longitudinal direction of said pellets, wherein the thermoplastic polymer sheath is prepared from a thermoplastic polymer composition comprising A) a heterophasic propylene copolymer consisting of a propylene-based matrix and a dispersed ethylene-α-olefin copolymer, wherein the heterophasic propylene copolymer has a melt flow rate of at least 40 g/10 min as determined in accordance with ISO 1133 (230° C., 2.16 kg) and a FOG value of at most 350 μg/g as determined by VDA 278, wherein the glass filaments are present in an amount of 10-70 wt % based on the pellet.

The invention relates to a pellet comprising a thermoplastic polymer sheath intimately surrounding glass filaments, which glass filaments are covered at least in part with an impregnating agent and extend in a longitudinal direction of said pellets, wherein the thermoplastic polymer sheath is prepared from a thermoplastic polymer composition comprising A) a heterophasic propylene copolymer consisting of a propylene-based matrix and a dispersed ethylene-α-olefin copolymer, wherein the heterophasic propylene copolymer has a melt flow rate of at least 40 g/10 min as determined in accordance with ISO 1133 (230° C., 2.16 kg) and a FOG value of at most 350 μg/g as determined by VDA 278, wherein the glass filaments are present in an amount of 10-70 wt % based on the pellet.

A biocide- and ammonia-free aqueous polymer dispersion is obtained by radically initiated multi-stage emulsion polymerization and comprising particles comprising at least a first polymer phase formed from a monomer composition I and a second polymer phase from a different monomer composition II. The first polymer phase has a glass transition temperature below 20° C., and the second polymer phase has a glass transition temperature above 20° C., both as determined by differential scanning calorimetry according to ISO 16805. The polymer dispersion further comprises at least one water-soluble alkali metal silicate, at least one water-soluble alkali metal or alkaline earth metal alkyl siliconate, or a mixture thereof and has a pH of 10.0 or higher.

A polyethylene composition for producing blow-molded hollow articles, having the following features: 1) density from 0.940 to 0.955 g/cm.sup.3 determined according to ISO 1183 at 23° C.; 2) ratio MIF/MIP from 12 to 30; 3) Mz from 2,000,000 to 4,500,000 g/mol; 4) η.sub.0.02 from 160,000 to 300,000 Pa.Math.s; and 5) long-chain branching index, LCBI, equal to or greater than 0.75.

Phosphorus-containing aqueous polymer dispersions and the use thereof as binders in coating formulations.