Ethylene-based polymers are characterized by a melt index less than 1 g/10 min, a density from 0.94 to 0.965 g/cm.sup.3, a Mw from 100,000 to 250,000 g/mol, a relaxation time from 0.5 to 3 sec, and an average number of long chain branches (LCBs) per 1,000,000 total carbon atoms in a molecular weight range of 300,000 to 900,000 g/mol that is greater than that in a molecular weight range of 1,000,000 to 2,000,000 g/mol, or an average number of LCBs per 1,000,000 total carbon atoms in a molecular weight range of 1,000,000 to 2,000,000 g/mol of less than or equal to about 5 and a maximum ratio of η.sub.E/3η at an extensional rate of 0.1 sec.sup.−1 from 1.2 to 10. These polymers have substantially no long chain branching in the high molecular weight fraction of the polymer, but instead have significant long chain branching in a lower molecular weight fraction, such that polymer melt strength and parison stability are maintained for the fabrication of blow molded products and other articles of manufacture. These ethylene polymers can be produced using a dual catalyst system containing a single or two atom bridged metallocene compound with two indenyl groups, and a single atom bridged metallocene compound with a fluorenyl group and a cyclopentadienyl group.

Ethylene-based polymers are characterized by a melt index less than 1 g/10 min, a density from 0.94 to 0.965 g/cm.sup.3, a Mw from 100,000 to 250,000 g/mol, a relaxation time from 0.5 to 3 sec, and an average number of long chain branches (LCBs) per 1,000,000 total carbon atoms in a molecular weight range of 300,000 to 900,000 g/mol that is greater than that in a molecular weight range of 1,000,000 to 2,000,000 g/mol, or an average number of LCBs per 1,000,000 total carbon atoms in a molecular weight range of 1,000,000 to 2,000,000 g/mol of less than or equal to about 5 and a maximum ratio of η.sub.E/3η at an extensional rate of 0.1 sec.sup.−1 from 1.2 to 10. These polymers have substantially no long chain branching in the high molecular weight fraction of the polymer, but instead have significant long chain branching in a lower molecular weight fraction, such that polymer melt strength and parison stability are maintained for the fabrication of blow molded products and other articles of manufacture. These ethylene polymers can be produced using a dual catalyst system containing a single or two atom bridged metallocene compound with two indenyl groups, and a single atom bridged metallocene compound with a fluorenyl group and a cyclopentadienyl group.

Ethylene-based polymers having a density of 0.952 to 0.968 g/cm.sup.3, a ratio of HLMI/MI from 185 to 550, an IB parameter from 1.46 to 1.80, a tan δ at 0.1 sec.sup.−1 from 1.05 to 1.75 degrees, and a slope of a plot of viscosity versus shear rate at 100 sec.sup.−1 from 0.18 to 0.28 are described, with low melt flow versions having a HLMI from 10 to 30 g/10 min and a Mw from 250,000 to 450,000 g/mol, and high melt flow versions having a HLMI from 30 to 55 g/10 min and a Mw from 200,000 to 300,000 g/mol. These polymers have the processability of chromium-based resins, but with improved stress crack resistance and topload strength for bottles and other blow molded products.

Ethylene-based polymers having a density of 0.952 to 0.968 g/cm.sup.3, a ratio of HLMI/MI from 185 to 550, an IB parameter from 1.46 to 1.80, a tan δ at 0.1 sec.sup.−1 from 1.05 to 1.75 degrees, and a slope of a plot of viscosity versus shear rate at 100 sec.sup.−1 from 0.18 to 0.28 are described, with low melt flow versions having a HLMI from 10 to 30 g/10 min and a Mw from 250,000 to 450,000 g/mol, and high melt flow versions having a HLMI from 30 to 55 g/10 min and a Mw from 200,000 to 300,000 g/mol. These polymers have the processability of chromium-based resins, but with improved stress crack resistance and topload strength for bottles and other blow molded products.

A bimodal polymer composition comprising a lower molecular weight homopolymer and a higher molecular weight copolymer wherein the bimodal polymer composition has a density of from about 0.930 gram per cubic centimeter (g/cc) to about 0.970 g/cc, a ratio of high load melt index:melt index of from about 10 to about 150 and an Environmental Stress Crack Resistance (ESCR) of from about 25 hours to about 300 hours when measured in accordance with ASTM D1693 or ASTM D2561. A chromium-catalyzed polymer composition comprising (i) a lower molecular weight homopolymer and (ii) a higher molecular weight copolymer, wherein the bimodal polymer composition has an Environmental Stress Crack Resistance (ESCR) of from about 25 hours to about 300 hours when measured in accordance with ASTM D1693 or ASTM D2561.

A bimodal polymer composition comprising a lower molecular weight homopolymer and a higher molecular weight copolymer wherein the bimodal polymer composition has a density of from about 0.930 gram per cubic centimeter (g/cc) to about 0.970 g/cc, a ratio of high load melt index:melt index of from about 10 to about 150 and an Environmental Stress Crack Resistance (ESCR) of from about 25 hours to about 300 hours when measured in accordance with ASTM D1693 or ASTM D2561. A chromium-catalyzed polymer composition comprising (i) a lower molecular weight homopolymer and (ii) a higher molecular weight copolymer, wherein the bimodal polymer composition has an Environmental Stress Crack Resistance (ESCR) of from about 25 hours to about 300 hours when measured in accordance with ASTM D1693 or ASTM D2561.

The invention relates to a solid catalyst system comprising a chromium compound, a metal compound, an aluminium compound and a silicon oxide support, wherein the silicon oxide support has an average particle diameter in the range between ≥20 and ≤50 μm, a pore volume in the range between ≥1.7 ml/g and ≤3 ml/g, and a surface area in the range between ≥400 m.sup.2/g and ≤800 m.sup.2/g, and wherein the aluminium alkoxide compound has the formula
R.sub.1—Al—OR.sub.2
wherein R.sub.1 is selected from (C.sub.1-C.sub.8) alkyl groups and OR.sub.2 is selected from (C.sub.1-C.sub.8) alkoxyl groups.

The invention relates to a solid catalyst system comprising a chromium compound, a metal compound, an aluminium compound and a silicon oxide support, wherein the silicon oxide support has an average particle diameter in the range between ≥20 and ≤50 μm, a pore volume in the range between ≥1.7 ml/g and ≤3 ml/g, and a surface area in the range between ≥400 m.sup.2/g and ≤800 m.sup.2/g, and wherein the aluminium alkoxide compound has the formula
R.sub.1—Al—OR.sub.2
wherein R.sub.1 is selected from (C.sub.1-C.sub.8) alkyl groups and OR.sub.2 is selected from (C.sub.1-C.sub.8) alkoxyl groups.

Provided is an ethylene/1-hexene copolymer which has excellent long-term physical properties and processability, and thus may be usefully applied to manufacturing high-pressure resistant heating pipes, PE-RT pipes, large-diameter pipes, or the like.

Provided is an ethylene/1-hexene copolymer which has excellent long-term physical properties and processability, and thus may be usefully applied to manufacturing high-pressure resistant heating pipes, PE-RT pipes, large-diameter pipes, or the like.