Processing aid for aiding in orienting an extruded film layer including a preponderance, by weight, of a high crystal-line polypropylene is a crystalline polypropylene wax. An oriented film layer including a blend of crystalline polypropylene wax and high crystallinity polypropylene homopolymer is part of the invention. The invention includes a method of forming an oriented film layer including a preponderance by weight of a high crystallinity polypropylene and includes the steps of blending a high crystallinity polypropylene with a crystalline polypropylene wax, directing the blend through an extruder to form a film layer and then orienting the film layer. The invention includes a biaxially oriented, multi-layer film including a base layer and at least one skin layer. The base layer includes a blend of crystalline metallocene catalyzed polypropylene wax and a high crystallinity polypropylene.

A stable aqueous film forming dispersion comprising:

a polymer selected from the group consisting of: polyvinyl butyral, polyvinyl acetyl, ethylene vinyl acetate, vinyl acetate and mixtures thereof:

a plasticiser;

an emulsifier; and

a water soluble organometallic crosslinking agent.

Provided herein are seam tapes and related methods. The seam tapes can be compatible with polyolefin-based waterproof/breathable (w/b) membranes, including polypropylene (PP) w/b membranes and/or polyethylene (PE) w/b membranes. Also provided are seams sealed by means of these seam tapes, as well as materials, fabrics, and garments including one or more of these sealed seams.

Provided herein are seam tapes and related methods. The seam tapes can be compatible with polyolefin-based waterproof/breathable (w/b) membranes, including polypropylene (PP) w/b membranes and/or polyethylene (PE) w/b membranes. Also provided are seams sealed by means of these seam tapes, as well as materials, fabrics, and garments including one or more of these sealed seams.

A phase difference film and a circularly polarizing film each achieve suppressed coloration when viewed from the front direction, a smaller difference in tint between views from the front direction and the oblique direction, and suppressed image unevenness, where the film is applied to an image display panel, in particular, an organic EL panel; as well as an image display device including the circularly polarizing film. The phase difference film includes optically anisotropic layers A and B, in which a retardation RthA of layer A in the thickness direction at a wavelength of 550 nm is larger than 0, layer A exhibits predetermined optical properties, a retardation RthB of layer B in the thickness direction at a wavelength of 550 nm is smaller than 0, layer B satisfies predetermined optical properties, and the angle formed between a slow axis of the optically anisotropic layers A and B is 90°±10°.

A phase difference film and a circularly polarizing film each achieve suppressed coloration when viewed from the front direction, a smaller difference in tint between views from the front direction and the oblique direction, and suppressed image unevenness, where the film is applied to an image display panel, in particular, an organic EL panel; as well as an image display device including the circularly polarizing film. The phase difference film includes optically anisotropic layers A and B, in which a retardation RthA of layer A in the thickness direction at a wavelength of 550 nm is larger than 0, layer A exhibits predetermined optical properties, a retardation RthB of layer B in the thickness direction at a wavelength of 550 nm is smaller than 0, layer B satisfies predetermined optical properties, and the angle formed between a slow axis of the optically anisotropic layers A and B is 90°±10°.

This disclosure relates to ethylene interpolymer compositions and films prepared therefrom. Specifically: ethylene interpolymer products having: a dimensionless Long Chain Branching Factor, LCBF, greater than or equal to 0.001; a residual catalytic metal of from ≥0.03 to ≤5 ppm of hafnium, and; a dimensionless unsaturation ratio, UR, of from ≥−0.40 to ≤0.06, wherein UR is defined by the following relationship; UR=(SC.sup.U−T.sup.U)/T.sup.U, where SC.sup.U is the amount of a side chain unsaturation per 100 carbons and T.sup.U is amount of a terminal unsaturation per 100 carbons, in said ethylene interpolymer product. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.855 to about 0.975 g/cc, a polydispersity (M.sub.w/M.sub.n) from about 1.7 to about 25 and a Composition Distribution Breadth Index (CDBI.sub.50) from about 1% to about 98%.

This disclosure relates to ethylene interpolymer compositions and films prepared therefrom. Specifically: ethylene interpolymer products having: a dimensionless Long Chain Branching Factor, LCBF, greater than or equal to 0.001; a residual catalytic metal of from ≥0.03 to ≤5 ppm of hafnium, and; a dimensionless unsaturation ratio, UR, of from ≥−0.40 to ≤0.06, wherein UR is defined by the following relationship; UR=(SC.sup.U−T.sup.U)/T.sup.U, where SC.sup.U is the amount of a side chain unsaturation per 100 carbons and T.sup.U is amount of a terminal unsaturation per 100 carbons, in said ethylene interpolymer product. The disclosed ethylene interpolymer products have a melt index from about 0.3 to about 500 dg/minute, a density from about 0.855 to about 0.975 g/cc, a polydispersity (M.sub.w/M.sub.n) from about 1.7 to about 25 and a Composition Distribution Breadth Index (CDBI.sub.50) from about 1% to about 98%.

There is provided a polarizer excellent in durability. A polarizer according to one embodiment of the present invention includes a resin film containing boric acid, wherein the resin film has a low-concentration portion, which contains a lower concentration of the boric acid than that in any other site, formed in an end portion thereof.

There is provided a polarizer excellent in durability. A polarizer according to one embodiment of the present invention includes a resin film containing boric acid, wherein the resin film has a low-concentration portion, which contains a lower concentration of the boric acid than that in any other site, formed in an end portion thereof.