An expanded beads molded article containing a block copolymer of a polyethylene block and an ethylene-α-olefin copolymer block and having a density of 150 kg/m.sup.3 or more and 500 kg/m.sup.3 or less and a tensile strength of 0.5 MPa or more.

Methods of forming a lightweight reinforced thermoplastic core layer and articles including the core layer are described. In some examples, the methods use a combination of thermoplastic material, reinforcing fibers and bicomponent fibers to enhance retention of lofting agents in the core layer. The processes permit the use of less material while still providing sufficient lofting capacity in the final formed core layer.

A method for preparing an aerogel comprising nano attapulgite and phenolic aldehyde and a method for preparing abrasion-resistant vehicle tire. 80-100 weight distributions of rubber, 3-8 weight distributions of SiO.sub.2.nH.sub.2O, 3-6 weight distributions of an anti-aging agent, 3-4 weight distributions of a heat stabilizer, 3-5 weight distributions of a compatibilizing agent, and 3-12 weight distributions of the aerogel comprising the nano attapulgite and the phenolic aldehyde is selected as a raw material of the abrasion-resistant rubber material to prepare rubber composite material for the abrasion-resistant vehicle tire.

A method of removing metal ions is provided, which includes contacting a metal removal composition with a solution containing metal ions for removing the metal ions from the solution, wherein the metal removal composition includes a polymer with a chemical structure of: ##STR00001##
wherein Q is a quinoline-based group, n=90˜450, o=10˜50, and p=0˜20. The metal removal composition has a type of fiber or film. In addition, the metal removal composition has a porosity of 60% to 90%.

A foam flooring includes a stone-plastic base material structure, which sequentially comprises, from top to bottom, a first stable layer, a foaming layer and a second stable layer. The first stable layer and the second stable layer are both sheets with a PVC resin and filler powder as main components, with 25-40 parts by mass of the PVC resin and 55-75 parts by mass of the filler powder; and the density of the SPC foam flooring is 1.4-1.6 g/cm3. The foaming layer is arranged between the two stable layers, such that the overall density of the flooring is significantly reduced and reaches 1.4-1.6 g/m3; since the foaming layer is arranged inside, the surface strength of the overall flooring is not influenced.

A composition includes a 4-methyl-1-pentene-based polymer in which at least one or more temperatures showing a local maximum value of a loss tangent (tan δ) are present in a range of 10° C. or higher and 100° C. or lower, and the local maximum value of the loss tangent is 0.5 or more and 3.5 or less, and an organic compound, in which a content of the organic compound is 5 to 250 parts by mass with respect to 100 parts by mass of the 4-methyl-1-pentene-based polymer, and the organic compound has a viscosity (mPa.Math.s) in a range of 65 to 120, or a ratio between a melt flow rate (g/10 min.) of the 4-methyl-1-pentene-based copolymer and a melt flow rate (g/10 min.) of the organic compound is 1:1.0 to 0.1.

A hybrid expandable composition that provides improved expansion and loft properties is disclosed. The hybrid expandable composition is particularly useful in providing insulation and/or cushion to substrates.

The disclosure is directed to methods of manufacturing protective packaging materials, as well as the protective packaging materials produced using the disclosed methods. These packaging materials can be biodegradable, compostable, and/or recyclable.

A foamable composition comprising at least one cellulose acetate, a plasticizer, a nucleating agent, and either a chemical blowing agent or a physical blowing agent is disclosed. The composition is formed into foamed articles that are biodegradable.

Provided are rapidly cross-linkable silicone foam compositions, kits, and methods for filling implanted medical devices in situ or in vivo, the implanted medical devices, including for example, body implants and tissue expanders, the compositions including a platinum divinyl disiloxane complex; a low viscosity vinyl terminated polydimethylsiloxane; a low viscosity hydride terminated polydimethylsiloxane; a silicone cross-linker; and a gas and/or gas-filled microcapsules, where the rapidly cross-linkable silicone foam composition has a viscosity of ≤150 cPs for ≥1 min. post-preparation and ≤300 cPs≤5 min. post-preparation, at ambient temperature.