A polymer film and a laminated glass manufactured using the polymer film are provided. The polymer film has a first surface and a second surface, wherein the first surface has a standard deviation of a void volume (Vv) value at a material ratio of 10% ranging from 0.5 μm.sup.3/μm.sup.2 to 2.5 μm.sup.3/μm.sup.2, and wherein the material ratio and void volume are defined in accordance with ISO 25178-2:2012.

A film is described comprising a (meth)acrylic polymer and a polyvinyl acetal (e.g. butyral) resin. In some embodiments, the film has a glass transition temperature (i.e. Tg) ranging from 30° C. to 60° C. In some embodiments, the film has a gel content of at least 20% or greater. In some embodiments, the film has an elongation at break of at least 175%. The film typically comprises photoinitiator as a result of the method by which the film was made. The film may be a monolithic film or a layer of a multilayer film.

A gear is provided that has excellent continuous moldability for practical use, and both high slidability and high durability. The provided gear is a molded resin constructed of a resin composition comprising a thermoplastic resin (A) and cellulose nanofibers (B) with an average fiber diameter of 1000 nm or smaller, and having a number average molecular weight of the thermoplastic resin (A) in the range of 10,000 to 150,000, wherein a sliding surface of the gear with another gear teeth has an arithmetic mean surface roughness Sa of 3.0 .Math.m or lower.

The present invention discloses a fire extinguishing sheet which is used in places, facilities, devices, tools, structures and the like where a fire may break out, and which makes initial fire extinguishing possible. This fire extinguishing sheet contains at least a potassium compound as a fire extinguishing chemical that is thermally decomposed upon reaching a predetermined temperature and generates a fire extinguishing component; and this fire extinguishing sheet is arranged in places, facilities, devices, tools, structures and the like where a fire may break out. If a fire breaks out, aerosols containing potassium radicals (a potassium compound) are generated from the fire extinguishing sheet, and the chain of combustion is interrupted by a negative catalytic effect, thereby quickly extinguishing or suppressing the fire.

The present invention relates to a polyvinyl acetal resin film, comprising a polyvinyl acetal resin material, wherein the polyvinyl acetal resin film has a thickness of 5 to 350 μm, and satisfies the following Formulae (1) and (2) where, comparing one surface and the other surface, a mean value of the 10-point average roughness of a rougher surface A and a mean value of the 10-point average roughness of a smoother surface B are defined as Rz1(a) μm and Rz2(a) μm, respectively:
Rz1(a)>1.1×Rz2(a)  (1)
3>Rz2(a)  (2), a value obtained by dividing the standard deviation of the 10-point average roughness of the surface A by Rz1(a) and a value obtained by dividing the standard deviation of the 10-point average roughness of the surface B by Rz2(a) are each 0 to 0.30, a viscosity of a toluene/ethanol (1:1, mass ratio) solution containing 10%-by-mass of a polyvinyl acetal resin contained in the polyvinyl acetal resin material, which is measured at 20° C. and 30 rpm using a Brookfield-type (B-type) viscometer, is 100 to 1,000 mPa.Math.s, and the amount of a plasticizer in the polyvinyl acetal resin film is 0 to 20% by mass based on a total mass of the polyvinyl acetal resin film.

Embodiment relates to film for bonding, and a light-transmitting laminate including the same and the like, a film for bonding comprising an embossed surface, wherein the embossed surface has an A2/A1 value of 1 or less are disclosed. A film for bonding have improved in deairing stability during formation of a light transmitting laminate, an edge sealing characteristic, and the like by controlling characteristics of a embossed surface.

Provided is an interlayer film for laminated glass capable of enhancing the sound insulating properties of laminated glass, and making foaming less likely to occur in an end part. The interlayer film for laminated glass according to the present invention includes a first layer, and a lateral covering part that covers at least part of a lateral part of the first layer, and the first layer has a shear elastic modulus at 25° C. of 0.17 MPa or less, and the lateral covering part has a shear elastic modulus at 25° C. of more than 1 MPa.

An interlayer film for laminated glass, comprising a first layer containing a polyvinyl acetal-based resin, wherein the first layer contains no plasticizer or contains a plasticizer in an amount of 15 parts by mass or less based on 100 parts by mass of the resin contained in the first layer, and the first layer has a glass transition temperature (Tg) of 50° C. or lower.

The present invention relates to a modified polyvinyl butyral material, comprising a polyvinyl butyral composite material, a filler, an anti-hydrolysis agent, a first plasticizer, zinc stearate, calcium stearate, and a polymeric dispersant; wherein the polyvinyl butyral composite material is obtained by plasticizing a composition comprising polyvinyl butyral and a second plasticizer. The present invention also relates to a preparation method of the modified polyvinyl butyral material, a modified polyvinyl butyral product comprising at least one modified polyvinyl butyral layer prepared from a material comprising the modified polyvinyl butyral material, and the preparation method of the modified polyvinyl butyral product.

Provided is an interlayer film for laminated glass capable of reducing the variation in double images in laminated glass in the direction perpendicular to the direction connecting one end and the other end of the interlayer film, and effectively suppressing double images. An interlayer film for laminated glass according to the present invention has one end and the other end being at the opposite side of the the one end, the other end has a thickness of larger than a thickness of the one end, the interlayer film for laminated glass as a whole has a wedge angle of 0.1 mrad or more, and the interlayer film for laminated glass has a thickness varying region in a region extending in the direction perpendicular to the direction connecting the one end and the other end of the interlayer film, having a standard deviation of 11 partial wedge angles measured by the following measuring method of 0.040 mrad or less.