A material may include a pigment and one or more silicon oxycarbides (SiOC) disposed in the black ceramic pigment, wherein a surface of the pigment is free of one or more silanols (Si—OH) bonds.

Modified copper chromite spinel pigments exhibit lower coefficients of thermal expansion than unmodified structures. Three methods exist to modify the pigments: (1) the incorporation of secondary modifiers into the pigment core composition, (2) control of the pigment firing profile, including both the temperature and the soak time, and (3) control of the pigment core composition.

The present invention relates to semitransparent pearlescent pigments, to processes for producing them, and to the use of such pearlescent pigments, where the pearlescent pigments comprise monolithically constructed substrate platelets composed of a metal oxide having an average thickness of 1 to 40 nm and a form factor, expressed by the ratio of the mean size to the average thickness, of at least 80, which are enveloped by at least one substantially transparent coating A composed of at least one low-index metal oxide and/or metal oxide hydrate, having a refractive index of less than 1.8, and at least one interference layer in the form of a coating B composed of at least one high-index metal oxide, having a refractive index of at least 1.8.

A process for preparing whitened fly ash includes the steps of: (a) subjecting fly ash to a size classification step to obtain size classified fly ash having a particle size such that at least 90 wt % has a particle size of from 44 μm to 250 μm; (b) optionally, contacting the size classified fly ash from step (a) with water to form a slurry, wherein the slurry has a solid content of less than 40 wt %; (c) subjecting the slurry obtained in step (b) to an exhaustive magnetic separation step to form magnetically treated fly ash, wherein the exhaustive magnetic separation step includes a first magnetic extraction step and a second magnetic extraction step, wherein the second magnetic extraction step is carried out at a higher magnetic field strength than the first magnetic extraction step; and (d) subjecting the magnetically treated fly ash obtained in step (c) to milling to form whitened fly ash.

The present invention relates to metal effect pigments with a high covering power and a thin iron oxide coating, for creating a champagne tone.

Methods, processes, systems, devices and apparatus are provided for additive manufacture resulting in the 3D printing of ceramic materials and components with a thickness greater than three millimeters (3 mm). A sulfur-free 3D printable formulation comprises a liquid inorganic polymer resin using Stereolithograpy (SLA) printers and Digital Light Processing (DLP) curing of the polymer resin via the chemical bonding of the materials rather than sintering. Thus, the process has shorter manufacturing intervals, significantly lower energy use and produces larger scale ceramic components having less linear shrinkage, less mass loss and high ceramic yield with no corrosive sulfur compounds present in the ceramic component.

The present invention discloses magnesia and a method for manufacturing same, wherein the magnesia can be produced into granules of various shapes and sizes and can be improved in moisture resistance with the formation of a moisture resistant surface oxide layer by donor addition and then thermal treatment. The magnesia according to the present invention comprises a MgO granule; and a surface oxide layer formed on a surface of the MgO granule and a composition of the surface oxide layer is different from a composition of an inside of the MgO granule.

The invention provides dispersed inorganic mixed metal oxide pigment compositions in a hydrocarbon media utilizing a dispersant having polyisobutylene succinic anhydride structure reacted with a non-polymeric amino ether/alcohol to disperse a mixed metal oxide pigment in the media. The metal oxide pigment is of the type used to color ceramic or glass articles. A milling process using beads is also described to reduce the mixed metal oxide particle size to the desired range. A method of using the mixed metal oxide dispersion to digitally print an image on a ceramic or glass article using the dispersion jetted through a nozzle and subsequently firing the colored article is also described.

The invention provides dispersed inorganic mixed metal oxide pigment compositions in a hydrocarbon media utilizing a dispersant having polyisobutylene succinic anhydride structure reacted with a non-polymeric amino ether/alcohol to disperse a mixed metal oxide pigment in the media. The metal oxide pigment is of the type used to color ceramic or glass articles. A milling process using beads is also described to reduce the mixed metal oxide particle size to the desired range. A method of using the mixed metal oxide dispersion to digitally print an image on a ceramic or glass article using the dispersion jetted through a nozzle and subsequently firing the colored article is also described.

Modified copper chromite spinel pigments exhibit lower coefficients of thermal expansion than unmodified structures. Three methods exist to modify the pigments: (1) the incorporation of secondary modifiers into the pigment core composition, (2) control of the pigment firing profile, including both the temperature and the soak time, and (3) control of the pigment core composition.