A sliding member includes a back metal layer and a sliding layer on the back metal layer. The sliding layer includes a synthetic resin matrix and graphite particles dispersed in the matrix in a volume ratio of 5-50% of that of the sliding layer. The graphite particles are composed of spheroidal and flake-like particles. The flake-like particles have a volume ratio of 10-40% of total graphite particles. The spheroidal particles have a cross-sectional structure with a plurality of AB planes of a graphite crystal laminated along a curved particle surface, from the surface toward a center direction. The flake-like graphite particles have a cross-sectional structure with the plurality of AB planes laminated in a thickness direction of the thin plate shape. The spheroidal particles have an average particle size of 3-50 μm, and the flake-like graphite particles have an average particle size of 1-25 μm.

Disclosed herein are embodiments of a method of making a lubricant composition for lapping a ceramic material. The method includes mixing a base lubricant component and a powdered wax composition component to form the lubricant composition. The powdered wax composition component includes a powdered wax dispersion or a powdered wax emulsion. The amount of powdered wax composition component mixed with the base lubricant component is from 0.01 to 10 percent by weight of the lubricant composition. Also disclosed herein are embodiments of related lubricant compositions and/or methods of using the lubricant to lap a ceramic substrate (e.g., one or more bars of sliders).

Disclosed herein are embodiments of a method of making a lubricant composition for lapping a ceramic material. The method includes mixing a base lubricant component and a powdered wax composition component to form the lubricant composition. The powdered wax composition component includes a powdered wax dispersion or a powdered wax emulsion. The amount of powdered wax composition component mixed with the base lubricant component is from 0.01 to 10 percent by weight of the lubricant composition. Also disclosed herein are embodiments of related lubricant compositions and/or methods of using the lubricant to lap a ceramic substrate (e.g., one or more bars of sliders).

A polymeric material mixture comprising a fluorine-containing polymer, a siloxane polymer, and at least two polymer processing additives (PPA), wherein the at least two polymer processing additives have different chemistries. For example, there can be a flexible coextruded pipe for providing a protective housing for cables, fluids, sludge or solids, the pipe comprising a pair of telescopically related inner and outer layers, where said inner layer is lubricated with the polymeric material mixture.

This invention provides a threaded connection for pipes or tubes having excellent misalignment resistance and high torque on shoulder resistance, and also having excellent corrosion resistance properties, as well as a method for producing the threaded connection for pipes or tubes. The threaded connection for pipes or tubes includes a pin and a box. The pin and the box include contact surfaces having threaded portions and unthreaded metal contact portions. The threaded connection for pipes or tubes includes, on at least one of the contact surfaces of the pin and the box, surface roughness, a Zn—Ni alloy plating layer, a Cu—Sn—Zn alloy plating layer and a solid lubricant coating layer. These are deposited from the contact surface side in the order of: surface roughness, the Zn—Ni alloy plating layer, the Cu—Sn—Zn alloy plating layer and the solid lubricant coating layer.

This invention provides a threaded connection for pipes or tubes having excellent misalignment resistance and high torque on shoulder resistance, and also having excellent corrosion resistance properties, as well as a method for producing the threaded connection for pipes or tubes. The threaded connection for pipes or tubes includes a pin and a box. The pin and the box include contact surfaces having threaded portions and unthreaded metal contact portions. The threaded connection for pipes or tubes includes, on at least one of the contact surfaces of the pin and the box, surface roughness, a Zn—Ni alloy plating layer, a Cu—Sn—Zn alloy plating layer and a solid lubricant coating layer. These are deposited from the contact surface side in the order of: surface roughness, the Zn—Ni alloy plating layer, the Cu—Sn—Zn alloy plating layer and the solid lubricant coating layer.

A polymeric material mixture comprising a fluorine-containing polymer, a siloxane polymer, and at least two polymer processing additives (PPA), wherein the at least two polymer processing additives have different chemistries. For example, there can be a flexible coextruded pipe for providing a protective housing for cables, fluids, sludge or solids, the pipe comprising a pair of telescopically related inner and outer layers, where said inner layer is lubricated with the polymeric material mixture.

A polymeric material mixture comprising a fluorine-containing polymer, a siloxane polymer, and at least two polymer processing additives (PPA), wherein the at least two polymer processing additives have different chemistries. For example, there can be a flexible coextruded pipe for providing a protective housing for cables, fluids, sludge or solids, the pipe comprising a pair of telescopically related inner and outer layers, where said inner layer is lubricated with the polymeric material mixture.

A sliding member includes: a base material; a coating layer formed on the base material and made of a resin composition including: a binder resin including polyamideimide; PTFE dispersed in the binder resin; and at least one of graphite and MoS.sub.2 dispersed in the binder resin; wherein a surface roughness of the coating layer after a sliding test is equal to or less than the surface roughness of the coating layer before the sliding test.

A sliding member includes: a base material; a coating layer formed on the base material and made of a resin composition including: a binder resin including polyamideimide; PTFE dispersed in the binder resin; and at least one of graphite and MoS.sub.2 dispersed in the binder resin; wherein a surface roughness of the coating layer after a sliding test is equal to or less than the surface roughness of the coating layer before the sliding test.