A dephosphorization method using a top and bottom blown converter. This method uses a converter charged with molten iron and slag, to blow an oxygen-containing gas from a top-blowing lance, supply the gas from an inlet of a blowing hole, and supply a control gas from an opening toward an axial center. This method has: a slag top-surface position measurement step, with the top surface of the molten iron measured in advance, measuring an arbitrary position in a top surface of the slag; a slag top-surface difference calculation of slag thickness difference between the measured top-surface positions of the molten iron and the slag; and a jetting condition adjustment step of, using the obtained slag thickness, adjusting a jetting condition of the gas jetted from the top-blowing lance into an appropriate range. The top-blown jetting condition is adjusted by comparing the slag thickness and the depth of a surface depression.

A non-oriented silicon steel and a production method are provided. The non-oriented silicon steel is prepared by using the processes of molten iron desulfurization, converter smelting, RH refining, continuous casting, hot rolling, acid tandem rolling, annealing, coating and finishing, and a chemical composition is as follows in mass percent: C0.003%, S0.008%, Si: 0.35%+1, Mn: 0.15-0.25%, P: 0.04-0.06%, Sn: 0.015%+2, Nb0.004%, V0.004%, Ti0.005%, Mo0.004%, Cr0.03%, Ni0.03%, Cu0.03%, N0.003% and the balance of Fe and inevitable inclusions. The non-oriented silicon steel has the iron loss P.sub.1.5/505.5 W/kg and the magnetic induction intensity B.sub.50001.75 when having the thickness of 0.5 mm, and desulfurization is not needed in the RH refining process.

A non-oriented silicon steel and a production method are provided. The non-oriented silicon steel is prepared by using the processes of molten iron desulfurization, converter smelting, RH refining, continuous casting, hot rolling, acid tandem rolling, annealing, coating and finishing, and a chemical composition is as follows in mass percent: C0.003%, S0.008%, Si: 0.35%+1, Mn: 0.15-0.25%, P: 0.04-0.06%, Sn: 0.015%+2, Nb0.004%, V0.004%, Ti0.005%, Mo0.004%, Cr0.03%, Ni0.03%, Cu0.03%, N0.003% and the balance of Fe and inevitable inclusions. The non-oriented silicon steel has the iron loss P.sub.1.5/505.5 W/kg and the magnetic induction intensity B.sub.50001.75 when having the thickness of 0.5 mm, and desulfurization is not needed in the RH refining process.