A production method for a high-strength steel sheet having a tensile strength TS of 780 MPa or more is provided. The production method comprises: heating a steel slab having a predetermined chemical composition; hotrolling the steel slab; coiling the hot-rolled sheet; subjecting the hot-rolled sheet to pickling treatment; holding the hot-rolled sheet in a pre-determined temperature range for predetermined time; cold rolling the hot-rolled sheet to obtain a cold-rolled sheet; subjecting the cold-rolled sheet to first annealing treatment; cooling the cold-rolled sheet at a pre-determined average cooling rate; cooling the cold-rolled sheet to room temperature; reheating the clod-rolled sheet to perform second annealing treatment; cooling the cold-rolled sheet at a first average cooling rate; cooling the cold-rolled sheet at a second average cooling rate; reheating the cold-rolled sheet to a predetermined reheating temperature range; and holding the cold-rolled sheet in the reheating temperature range.

An embodiment of the present invention provides a steel wire rod and a method for producing same, the steel wire rod comprising 0.3-0.5 wt % of C, 0.02-0.4 wt % of Si, 1.0-1.5 wt % of Mn, 0.3-0.7 wt % of Cr, 0.003 wt % or less of B, 0.03 wt % or less of Ti, 0.03 wt % or less of P, 0.01 wt % or less of S, 0.02-0.05 wt % of Al, and 0.001-0.01 wt % of N, with the balance being Fe and inevitable impurities, and having a microstructure in which the main phase thereof is a complex structure of ferrite+pearlite, and contains at most 5 area % (including 0 area %) of at least one of bainite or martensite, wherein the average pearlite colony size in a region extending from the ⅖ point to the ⅗ point of the diameter is at most 7 μm.

In some embodiments, a coating applied to steel reinforcement bar (e.g., steel rebar) that could considerably extend the lifetime of concrete structures by reducing steel rebar corrosion is disclosed. The coating includes a thin, passivating steel (e.g., stainless steel) layer that is applied to the outside of conventional steel rebar. The coating can be applied in-line through metal cold spray manufacturing, which is a high throughput coating technique that can be integrated into existing steel manufacturing plants. Furthermore, a novel, high performance ferritic steel with tailored resistance to corrosion from chlorides is described. The new ferritic steel is distinct from other commercial and experimental steels, and is better suited for coating low-cost steel structures like rebar. Multiple alloying elements including Cr, Al, and Si will each form protective oxides independently, increasing the total amount of protection and extending it over much wider ranges of pH and electrical potential.

Provided is a high-strength steel sheet having high impact resistance. The steel sheet includes: by weight %, carbon (C): 0.05% to 0.14%, silicon (Si): 0.01% to 1.0%, manganese (Mn): 1.5% to 2.5%, aluminum (Al): 0.01% to 0.1%, chromium (Cr): 0.005% to 1.0%, phosphorus (P): 0.001% to 0.05%, sulfur (S): 0.001% to 0.01%, nitrogen (N): 0.001% to 0.01%, niobium (Nb): 0.005% to 0.06%, titanium (Ti): 0.005% to 0.11%, and the balance of iron (Fe) and inevitable impurities. The steel sheet has a microstructure comprising ferrite and bainite in a total area fraction of 90% or more. The steel sheet has a value of 0.05 to 1.0 as a shear texture ({110}<112>, {112}<111>) area ratio of a center region (ranging deeper than 1/10t to ½t in a thickness direction, t refers to thickness (mm)) and a surface region (ranging from a surface to 1/10t in the thickness direction).

An method of manufacturing a hot press-formed member comprises heating a blank of an aluminum-based plated steel sheet in a heating furnace, removing the heated blank from the heating furnace and conveying the removed blank between an upper mold portion and a lower mold portion of a mold, mounted on a press, to be seated; and performing a forming process after the upper mold portion of the mold is in contact with the seated blank.

A powder metal composition for high wear and temperature applications is made by atomizing a melted iron based alloy including 3.0 to 7.0 wt. % carbon; 10.0 to 25.0 wt. % chromium; 1.0 to 5.0 wt. % tungsten; 3.5 to 7.0 wt. % vanadium; 1.0 to 5.0 wt. % molybdenum; not greater than 0.5 wt. % oxygen; and at least 40.0 wt. % iron. The high carbon content reduces the solubility of oxygen in the melt and thus lowers the oxygen content to a level below which would cause the carbide-forming elements to oxidize during atomization. The powder metal composition includes metal carbides in an amount of at least 15 vol. %. The microhardness of the powder metal composition increases with increasing amounts of carbon and is typically about 800 to 1,500 Hv50.

The present invention relates to a formed product used in vehicle components and the like, and to a method for manufacturing the same. The present invention provides heat treatable steel, a formed product using the same having ultra-high strength and excellent durability, and a method for manufacturing the same, wherein the heat treatable steel contains, in wt %, C (0.22-0.42%), Si (0.05-0.3%), Mn (1.0-1.5%), Al (0.01-0.1%), P (0.01% or less (including 0), S (0.005% or less), Mo (0.05-0.3%), Ti (0.01-0.1%), Cr (0.05-0.5%), B (0.0005-0.005%), N (0.01% or less), the balance Fe, and other inevitable impurities, Mn and Si satisfying Relationship formula (1), below, Mo/p satisfying Relationship formula (2), below: [Relationship formula 1] Mn/Si≧5 [Relationship formula 2] Mo/P≧15.

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 30% or more of a ferrite phase, 40% to 65% of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 40% to 55% and the total area ratio of a bainite phase having a grain diameter of more than 5 μm and/or a martensite phase having a grain diameter of more than 5 μm is 20% or less, and a tensile strength is 980 MPa or more.

A high-strength galvanized steel sheet that includes a chemical composition containing, by mass %, C: 0.15% or more and 0.25% or less, Si: 0.50% or more and 2.5% or less, Mn: 2.3% or more and 4.0% or less, P: 0.100% or less, S: 0.02% or less, Al: 0.01% or more and 2.5% or less, and Fe and inevitable impurities. The steel sheet having a microstructure containing, by an area percentage basis, a tempered martensite phase: 30% or more and 73% or less, a ferrite phase: 25% or more and 68% or less, a retained austenite phase: 2% or more and 20% or less, and other phases: 10% or less (including 0%), the other phases containing a martensite phase: 3% or less (including 0%) and a bainitic ferrite phase: less than 5% (including 0%).

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 25% or less of a ferrite phase, 75% or more of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 5% to 20%, and a tensile strength is 1180 MPa or more.