Anti-Collapse Oil Casing with High Strength and Manufacturing Method Therefor
An anti-collapse oil casing with high strength and a manufacturing method therefor, comprising the following chemical elements in percentage by mass: C:0.08%-0.18%; Si:0.1%-0.4%; Mn:0.1%-0.28%; Cr:0.2%-0.8%; Mo:0.2%-0.6%; Nb:0.02%-0.08% b; V:0.01%-0.15%; Ti:0.02%-0.05%; B:0.0015%-0.005%; and Al:0.01%-0.05%. The manufacturing method for the anti-collapse oil casing with high strength comprises the steps of: (1) smelting and continuous casting; (2) perforating, rolling, and sizing; (3) controlled cooling: the initial cooling temperature being Ar3+50° C. and the final cooling temperature being ≤80° C.; the cooling step being performed only to the outer surface of the casing without performing to the inner wall of the casing; and the rate of the controlled cooling being 30-70° C./s; (4) tempering; and (5) thermal straightening. The anti-collapse oil casing with high strength according to the present invention has reasonable chemical composition and process design, which not only has excellent economic efficiency, but also has high strength, high toughness and high anti-collapse performance.
DUPLEX STAINLESS STEEL SEAMLESS PIPE
The duplex stainless steel seamless pipe according to the present disclosure has the chemical composition described in the description and a microstructure consisting of 30 to 55% of ferrite, and austenite. In a square observation field of view region with sides of 250 μm including a center portion of the wall thickness and including a T direction and a C direction, a number of intersections NT which is a number of intersections between the line segment T1 to T4 described in the description and ferrite interfaces is 65 or more. A number of intersections NC which is a number of intersections between the line segments C1 to C4 described in the description and ferrite interfaces is 50 or more.
Method for modifying surface grain structure of the material and apparatus thereof
The present invention provides a simple, cost effective and hassle-free method and apparatus for modifying the surface grain structure of the material, thereby providing a material with multi-modal grain structure having high strength and good formability. The present invention uses a single step processing technique known as submerged static friction stir processing for modifying the surface grain structure of the material, thereby generating a multi-modal grain structure. In the present invention since the working material is completely immersed in the coolant, this maintains the working temperature of the system. Further the present invention does not involve long processing steps and do not need any specialized equipments.
Method for modifying surface grain structure of the material and apparatus thereof
The present invention provides a simple, cost effective and hassle-free method and apparatus for modifying the surface grain structure of the material, thereby providing a material with multi-modal grain structure having high strength and good formability. The present invention uses a single step processing technique known as submerged static friction stir processing for modifying the surface grain structure of the material, thereby generating a multi-modal grain structure. In the present invention since the working material is completely immersed in the coolant, this maintains the working temperature of the system. Further the present invention does not involve long processing steps and do not need any specialized equipments.
Hot stamped body
A hot stamped body comprising a steel base material and an Al—Zn—Mg-based plating layer formed on a surface of the steel base material, wherein the plating layer has a predetermined chemical composition, the plating layer comprises an interfacial layer positioned at an interface with the steel base material and containing Fe and Al and a main layer positioned on the interfacial layer, the main layer comprises, by area ratio, 10.0 to 85.0% of an Mg—Zn containing phase and 15.0 to 90.0% of an Fe—Al containing phase, the Mg—Zn containing phase comprises at least one selected from the group consisting of an MgZn phase, Mg.sub.2 Zn.sub.3 phase, and MgZn.sub.2 phase, and the Fe—Al containing phase comprises at least one of an FeAl phase and Fe—Al—Zn phase and an area ratio of the Fe—Al—Zn phase in the main layer is 10.0% or less.
SEAMLESS STEEL PIPE HAVING DESIRABLE SULFURIC ACID DEW-POINT CORROSION RESISTANCE, AND METHOD FOR MANUFACTURING SAME
A seamless steel pipe of the present invention is a seamless steel pipe having a composition that includes, in mass %, C: 0.02 to 0.12%, Si: 0.010 to 1.00%, Mn: 0.10 to 2.00%, P: 0.050% or less, S: 0.004% or less, Al: 0.010 to 0.100%, Cu: 0.03 to 0.80%, Ni: 0.02 to 0.50%, Cr: 0.55 to 1.00%, Sb: 0.005 to 0.20%, and the balance Fe and incidental impurities, and satisfying the following formula (1),
1.7×Cu*+11×Cr*+3.8×Sb*≥13.5 (1), where Cu*, Cr*, and Sb* represent average concentrations of Cu, Cr, and Sb, respectively, in mass %, as measured in a region 0.5 to 2.0 mm away from an outer surface of the steel pipe, the seamless steel pipe having a yield strength of 230 MPa or more, and a tensile strength of 380 MPa or more.
Aluminum-based plated steel sheet, method of manufacturing aluminum-based plated steel sheet, and method of manufacturing component for vehicle
An aluminum-based plated steel sheet according to an aspect of the present invention includes: a base material; an aluminum-based plating layer located above the base material; and an intermetallic compound layer that is located between the base material and the aluminum-based plating layer and contains an intermetallic compound of Al and Fe, in which the base material has a chemical component within a predetermined range, the aluminum-based plating layer contains, on average, 80 mass % or more and 97 mass % or less of Al, 3 mass % or more and 15 mass % or less of Si, 0 mass % or more and 5 mass % or less of Zn, 0 mass % or more and 5 mass % or less of Fe, 0 mass % or more and 3 mass % or less in total of one or more selected from the group consisting of Mg and Ca, and impurities so that a total amount thereof is 100 mass %, an average value of a thickness of the intermetallic compound layer is 2 μm or more and 10 μm or less, a maximum value of the thickness of the intermetallic compound layer is 10 μm or more and 25 μm or less, and a standard deviation of the thickness of the intermetallic compound layer is 2 μm or more and 10 μm or less.
FORGED PART OF STEEL AND A METHOD OF MANUFACTURING THEREOF
A steel for forging mechanical parts including the following elements, expressed in percentage by weight 0.2%≤C≤0.5%; 0.8%≤Mn≤1.5% ; 0.4%≤Si≤1%; 0.15%≤V≤0.6%; 0.01%≤Nb≤0.15%; 0.01%≤Cr≤0.5%; 0.01%≤P≤0.05%; 0.04%≤S≤0.09%; 0.01%≤N≤0.025%; and can contain one or more of the following optional elements 0%≤Al≤0.05%; 0%≤Mo≤0.5%; 0.01%≤Ni≤0.5%; 0%≤Ti≤0.2%; 0%≤B≤0.008%; 0%≤Cu≤0.5%; the remainder composition being composed of iron and unavoidable impurities caused by processing, the microstructure of said steel comprising 50% to 90% of Pearlite, 10% to 40% of Ferrite, with an optional presence of acicular ferrite between 0% and 2%, a niobium equivalent of 80% or more.
FORGED PART OF STEEL AND A METHOD OF MANUFACTURING THEREOF
A steel for forging mechanical parts including the following elements, expressed in percentage by weight 0.2%≤C≤0.5%; 0.8%≤Mn≤1.5% ; 0.4%≤Si≤1%; 0.15%≤V≤0.6%; 0.01%≤Nb≤0.15%; 0.01%≤Cr≤0.5%; 0.01%≤P≤0.05%; 0.04%≤S≤0.09%; 0.01%≤N≤0.025%; and can contain one or more of the following optional elements 0%≤Al≤0.05%; 0%≤Mo≤0.5%; 0.01%≤Ni≤0.5%; 0%≤Ti≤0.2%; 0%≤B≤0.008%; 0%≤Cu≤0.5%; the remainder composition being composed of iron and unavoidable impurities caused by processing, the microstructure of said steel comprising 50% to 90% of Pearlite, 10% to 40% of Ferrite, with an optional presence of acicular ferrite between 0% and 2%, a niobium equivalent of 80% or more.
HOT STAMPED BODY
A hot stamped body with high strength, good bendability and crack propagation resistance, consisting of: in mass %, C: 0.06% or more to less than 0.20%, Si: 0.010-1.00%, Mn: 0.80-2.00%, P: 0.100% or less, S: 0.010% or less, Al: 0.010-0.500%, N: 0.010% or less, Nb: more than 0.020% to 0.10% or less, Ti: 0-0.10%, V: 0-0.10%, Cr: 0-0.50%, Mo: 0-1.00%, B: 0-0.0100%, Ni: 0-0.50%, REM: 0-0.0100%, Mg: 0-0.010%, Ca: 0-0.0100%, and Co: 0-2.0%, with the balance: Fe and impurities, wherein a microstructure includes, in area fraction, ferrite: 5-50%, and martensite: 50-95%, a proportion of regions in the martensite where GAIQ values are 35000 or more to less than 45000 is 30 area % or more, and a maximum bending angle α (deg) is 90 or more.