A piercing machine includes a plurality of skewed rolls, a plug, a mandrel bar and an outer surface cooling mechanism. The outer surface cooling mechanism is disposed around the mandrel bar at a position that is rearward of the plug, and with respect to an outer surface of a hollow shell advancing through a cooling zone which has a specific length in an axial direction of the mandrel bar and which is located rearward of the plug, as seen from an advancing direction of the hollow shell, the outer surface cooling mechanism ejects a cooling fluid toward an upper part of the outer surface, a lower part of the outer surface, a left part of the outer surface and a right part of the outer surface of the hollow shell to cool the hollow shell inside the cooling zone.

Provided is an electric resistance welded steel pipe or tube having excellent fatigue durability after rapid and short-time heating quenching treatment. An electric resistance welded steel pipe or tube comprises: a base metal being a steel sheet having a specific chemical composition and an electric resistance weld portion having a bond width of 40×10.sup.−6 m or more and 120×10.sup.−6 m or less, wherein C.sub.0-C.sub.1 is 0.05 mass % or less, where C.sub.0-C.sub.1 is a difference between C.sub.1 in mass % which is a minimum C content of the electric resistance weld portion and C.sub.0 in mass % which is a C content of the steel sheet, and a depth of a total decarburized layer in each of an inner surface layer and an outer surface layer of the electric resistance welded steel pipe or tube is 50×10.sup.−6 m or less.

Provided is an electric resistance welded steel pipe or tube having excellent fatigue durability after rapid and short-time heating quenching treatment. An electric resistance welded steel pipe or tube comprises: a base metal being a steel sheet having a specific chemical composition and an electric resistance weld portion having a bond width of 40×10.sup.−6 m or more and 120×10.sup.−6 m or less, wherein C.sub.0-C.sub.1 is 0.05 mass % or less, where C.sub.0-C.sub.1 is a difference between C.sub.1 in mass % which is a minimum C content of the electric resistance weld portion and C.sub.0 in mass % which is a C content of the steel sheet, and a depth of a total decarburized layer in each of an inner surface layer and an outer surface layer of the electric resistance welded steel pipe or tube is 50×10.sup.−6 m or less.

An electric resistance welded steel pipe includes a base metal zone and an electric resistance welded zone. The base metal zone has a predetermined chemical composition and a microstructure including, by volume, ferrite: more than 30%, and bainite: 10% or more. The total volume fraction of the ferrite and the bainite is 70% or more and 95% or less. The balance being one or two or more phases selected from pearlite, martensite, and austenite. Further, when regions surrounded by boundaries between adjacent crystals having a misorientation of 15° or more are defined as crystal grains, the average size of the crystal grains is less than 7.0 μm, and the volume fraction of crystal grains having a size of 40.0 μm or more is 30% or less. A compressive residual stress generated in the inner and outer surfaces of the steel pipe in the axial direction is 250 MPa or less.

An electric resistance welded steel pipe includes a base metal zone and an electric resistance welded zone. The base metal zone has a predetermined chemical composition and a microstructure including, by volume, ferrite: more than 30%, and bainite: 10% or more. The total volume fraction of the ferrite and the bainite is 70% or more and 95% or less. The balance being one or two or more phases selected from pearlite, martensite, and austenite. Further, when regions surrounded by boundaries between adjacent crystals having a misorientation of 15° or more are defined as crystal grains, the average size of the crystal grains is less than 7.0 μm, and the volume fraction of crystal grains having a size of 40.0 μm or more is 30% or less. A compressive residual stress generated in the inner and outer surfaces of the steel pipe in the axial direction is 250 MPa or less.

Provided herein is a high-strength seamless steel pipe, and a method for manufacturing same. A high-strength seamless steel pipe of the present invention has a yield strength of 758 MPa or more, and a K.sub.ILIMIT value of 23.0 MPa√m or more as an evaluation index of sulfide stress corrosion cracking resistance.

A seamless steel pipe of the present invention is a seamless steel pipe having a composition including, in mass %, C: 0.01 to 0.12%, Si: 0.01 to 0.8%, Mn: 0.10 to 2.00%, P: 0.050% or less, S: 0.040% or less, Al: 0.010 to 0.100%, Cu: 0.03 to 0.80%, Ni: 0.01 to 0.50%, Mo: 0.01 to 0.20%, Sb: 0.002 to 0.50%, Cr: 0.004% or less, W: 0.002% or less, and the balance Fe and incidental impurities, and a structure including a ferrite phase having an area percentage of 50 to 65%, a pearlite phase having an area percentage of 2% or less, and one or both of a bainite phase and a martensitic phase representing the remainder, the seamless steel pipe having a yield strength of 230 MPa or more, and a tensile strength of 380 MPa or more.

A seamless steel pipe of the present invention is a seamless steel pipe having a composition including, in mass %, C: 0.01 to 0.12%, Si: 0.01 to 0.8%, Mn: 0.10 to 2.00%, P: 0.050% or less, S: 0.040% or less, Al: 0.010 to 0.100%, Cu: 0.03 to 0.80%, Ni: 0.01 to 0.50%, Mo: 0.01 to 0.20%, Sb: 0.002 to 0.50%, Cr: 0.004% or less, W: 0.002% or less, and the balance Fe and incidental impurities, and a structure including a ferrite phase having an area percentage of 50 to 65%, a pearlite phase having an area percentage of 2% or less, and one or both of a bainite phase and a martensitic phase representing the remainder, the seamless steel pipe having a yield strength of 230 MPa or more, and a tensile strength of 380 MPa or more.

A stainless steel seamless pipe having high strength and excellent corrosion resistance. The stainless steel seamless pipe has a specified composition in which C, Si, Mn, Cr, Ni, Mo, Cu, and N satisfy a predetermined formula, a microstructure containing at least 25% martensitic phase, at most 65% ferrite phase, and at most 40% retained austenite phase by volume, and a yield strength of 758 MPa or more.

A stainless steel seamless pipe having high strength and excellent corrosion resistance. The stainless steel seamless pipe has a specified composition in which C, Si, Mn, Cr, Ni, Mo, Cu, and N satisfy a predetermined formula, a microstructure containing at least 25% martensitic phase, at most 65% ferrite phase, and at most 40% retained austenite phase by volume, and a yield strength of 758 MPa or more.