A grain-oriented electrical steel sheet having excellent iron loss property is produced from a steel slab containing, by mass %, C: 0.002-0.15%, Si: 2.5-6.0%, Mn: 0.01-0.80%, Al: 0.010-0.050% and N: 0.003-0.020%, when: a heating rate between 500-700° C. in decarburization annealing is not less than 80° C./s, a surface roughness Ra of a work roll in final cold rolling is 0.01-3.0 μm, a total content of alkaline earth metals to MgO in annealing separator is 0-5 mass %, an average length L in rolling direction of passed crystal grains is not more than 25 mm, a ratio of crystal grains having a length in rolling direction of not more than 5 mm is 40-90%, and an existence ratio of alkaline earth metal sulfides having a size corresponding to circle of not less than 0.5 μm in a cross section of forsterite film is not more than 0.2/μm per unit length in sheet width direction.

A grain-oriented electrical steel sheet having excellent iron loss property is produced from a steel slab containing, by mass %, C: 0.002-0.15%, Si: 2.5-6.0%, Mn: 0.01-0.80%, Al: 0.010-0.050% and N: 0.003-0.020%, when: a heating rate between 500-700° C. in decarburization annealing is not less than 80° C./s, a surface roughness Ra of a work roll in final cold rolling is 0.01-3.0 μm, a total content of alkaline earth metals to MgO in annealing separator is 0-5 mass %, an average length L in rolling direction of passed crystal grains is not more than 25 mm, a ratio of crystal grains having a length in rolling direction of not more than 5 mm is 40-90%, and an existence ratio of alkaline earth metal sulfides having a size corresponding to circle of not less than 0.5 μm in a cross section of forsterite film is not more than 0.2/μm per unit length in sheet width direction.

With a hot-rolled steel sheet for electrical steel sheet production having a scale layer on the surface, where the surface of the steel sheet has a lightness L* as defined in JIS Z 8781-4: 2013 satisfying 30≤L*≤50, and chromaticities a* and b* as defined in JIS Z 8781-4: 2013 satisfying −1≤a*≤2 and −5≤b*≤3 respectively, and with one end portion in the longitudinal direction of a coil as a reference, a color difference ΔE.sub.ab* as defined in JIS Z 8781-4: 2013 at the central portion and at the opposite end portion satisfies ΔE.sub.ab*≤8, it is possible to obtain a grain-oriented electrical steel sheet where the variation of properties in a product coil is small.

With a hot-rolled steel sheet for electrical steel sheet production having a scale layer on the surface, where the surface of the steel sheet has a lightness L* as defined in JIS Z 8781-4: 2013 satisfying 30≤L*≤50, and chromaticities a* and b* as defined in JIS Z 8781-4: 2013 satisfying −1≤a*≤2 and −5≤b*≤3 respectively, and with one end portion in the longitudinal direction of a coil as a reference, a color difference ΔE.sub.ab* as defined in JIS Z 8781-4: 2013 at the central portion and at the opposite end portion satisfies ΔE.sub.ab*≤8, it is possible to obtain a grain-oriented electrical steel sheet where the variation of properties in a product coil is small.

An ultra-high-strength hot-rolled steel plate and steel strip having good fatigue and reaming properties and a manufacturing method therefor. The weight percentages of the components of the steel plate and the steel strip are: C: 0.07-0.14%, Si: 0.1-0.4%, Mn: 1.55-2.00%, P≤0.015%, S≤0.004%, Al: 0.01-0.05%, N≤0.005%, Cr: 0.15-0.50%, V: 0.1-0.35%, Nb: 0.01%-0.06%, Mo: 0.15-0.50%, Ti≤0.02%, and the balance of Fe and unavoidable impurities. Such components need to meet: 1.0≤[(Cr/52)/(C/4)+(Nb/93+Ti/48+V/51+Mo/96)/(C/12)]≤1.6. The tensile strength of the ultrahigh-strength hot-rolled steel plate and steel strip is ≥780 MPa, the yield strength thereof is ≥660 MPa, the tensile fatigue limit (10 million cycles) FL thereof is ≥570 MPa, or the fatigue limit to tensile strength FL/Rm thereof is ≥0.72. The reaming rate meets: if an original hole is a punched hole, the reaming rate thereof is >85%; and if the original hole is a reamed hole, the reaming rate thereof is >120%.

An ultra-high-strength hot-rolled steel plate and steel strip having good fatigue and reaming properties and a manufacturing method therefor. The weight percentages of the components of the steel plate and the steel strip are: C: 0.07-0.14%, Si: 0.1-0.4%, Mn: 1.55-2.00%, P≤0.015%, S≤0.004%, Al: 0.01-0.05%, N≤0.005%, Cr: 0.15-0.50%, V: 0.1-0.35%, Nb: 0.01%-0.06%, Mo: 0.15-0.50%, Ti≤0.02%, and the balance of Fe and unavoidable impurities. Such components need to meet: 1.0≤[(Cr/52)/(C/4)+(Nb/93+Ti/48+V/51+Mo/96)/(C/12)]≤1.6. The tensile strength of the ultrahigh-strength hot-rolled steel plate and steel strip is ≥780 MPa, the yield strength thereof is ≥660 MPa, the tensile fatigue limit (10 million cycles) FL thereof is ≥570 MPa, or the fatigue limit to tensile strength FL/Rm thereof is ≥0.72. The reaming rate meets: if an original hole is a punched hole, the reaming rate thereof is >85%; and if the original hole is a reamed hole, the reaming rate thereof is >120%.

Method for the manufacture of a galvannealed steel sheet includes the following steps: A) the provision of a pre-coated steel sheet coated with a first coating comprising iron and nickel, such steel sheet having the following chemical composition in weight percent 0.10<C<0.40%, 1.5<Mn<3.0%, 0.7<Si<2.0%, 0.05<Al<1.0%, 0.75<(Si+Al)<3.0% and on a purely optional basis, one or more elements such as Nb≤0.5%, B≤0.005%, Cr≤1.0%, Mo≤0.50%, Ni≤1.0%, Ti≤0.5%, the remainder of the composition making up of iron and inevitable impurities resulting from the elaboration, B) the thermal treatment of such pre-coated steel sheet at a temperature between 600 to 1000° C., C) the hot-dip coating of the steel sheet obtained in step B) with a second coating based on zinc and D) an alloying treatment to form a galvannealed steel sheet.

Method for the manufacture of a galvannealed steel sheet includes the following steps: A) the provision of a pre-coated steel sheet coated with a first coating comprising iron and nickel, such steel sheet having the following chemical composition in weight percent 0.10<C<0.40%, 1.5<Mn<3.0%, 0.7<Si<2.0%, 0.05<Al<1.0%, 0.75<(Si+Al)<3.0% and on a purely optional basis, one or more elements such as Nb≤0.5%, B≤0.005%, Cr≤1.0%, Mo≤0.50%, Ni≤1.0%, Ti≤0.5%, the remainder of the composition making up of iron and inevitable impurities resulting from the elaboration, B) the thermal treatment of such pre-coated steel sheet at a temperature between 600 to 1000° C., C) the hot-dip coating of the steel sheet obtained in step B) with a second coating based on zinc and D) an alloying treatment to form a galvannealed steel sheet.

A production method for a high-strength steel sheet having a tensile strength TS of 780 MPa or more is provided. The production method comprises: heating a steel slab having a predetermined chemical composition; hotrolling the steel slab; coiling the hot-rolled sheet; subjecting the hot-rolled sheet to pickling treatment; holding the hot-rolled sheet in a pre-determined temperature range for predetermined time; cold rolling the hot-rolled sheet to obtain a cold-rolled sheet; subjecting the cold-rolled sheet to first annealing treatment; cooling the cold-rolled sheet at a pre-determined average cooling rate; cooling the cold-rolled sheet to room temperature; reheating the clod-rolled sheet to perform second annealing treatment; cooling the cold-rolled sheet at a first average cooling rate; cooling the cold-rolled sheet at a second average cooling rate; reheating the cold-rolled sheet to a predetermined reheating temperature range; and holding the cold-rolled sheet in the reheating temperature range.

A production method for a high-strength steel sheet having a tensile strength TS of 780 MPa or more is provided. The production method comprises: heating a steel slab having a predetermined chemical composition; hotrolling the steel slab; coiling the hot-rolled sheet; subjecting the hot-rolled sheet to pickling treatment; holding the hot-rolled sheet in a pre-determined temperature range for predetermined time; cold rolling the hot-rolled sheet to obtain a cold-rolled sheet; subjecting the cold-rolled sheet to first annealing treatment; cooling the cold-rolled sheet at a pre-determined average cooling rate; cooling the cold-rolled sheet to room temperature; reheating the clod-rolled sheet to perform second annealing treatment; cooling the cold-rolled sheet at a first average cooling rate; cooling the cold-rolled sheet at a second average cooling rate; reheating the cold-rolled sheet to a predetermined reheating temperature range; and holding the cold-rolled sheet in the reheating temperature range.