A steel sheet with a tensile strength (TS) of 780 MPa or more and less than 1180 MPa, a member, and a method for producing them. In a region of the steel sheet within 4.9 μm in the thickness direction, a region with a Si concentration not more than one-third of the Si concentration in the chemical composition of the steel sheet and with a Mn concentration not more than one-third of the Mn concentration in the chemical composition of the steel sheet has a thickness of 1.0 μm or more. The lowest Si concentration L.sub.Si and the lowest Mn concentration L.sub.Mn in the region within 4.9 μm from the surface of the steel sheet and a Si concentration T.sub.Si and a Mn concentration T.sub.Mn at a quarter thickness position of the steel sheet satisfy the following formula (1):

L.sub.Si+L.sub.Mn≤(T.sub.Si+T.sub.Mn)/4  (1).

Provided are a high-yield-ratio high-strength galvanized steel sheet and a method for manufacturing thereof. The high-yield-ratio high-strength galvanized steel sheet has a steel sheet having a specified chemical composition and a metallographic structure including, in terms of area ratio, in terms of area ratio, 15% or less of ferrite, 20% or more and 50% or less of martensite, and bainite and tempered martensite in a total amount of 30% or more, and a galvanized layer formed on the steel sheet having a coating weight of 20 g/m.sup.2 to 120 g/m.sup.2 per side, in which a yield strength ratio is 65% or more, a tensile strength is 950 MPa or more, and Mn oxides are contained in the galvanized layer in an amount of 0.015 g/m.sup.2 to 0.050 g/m.sup.2.

A rolled steel sheet, for press hardening is provided, having a chemical composition where Ti/N>3.42, and the carbon, manganese, chromium and silicon contents satisfy: $2.6C+\frac{\mathrm{Mn}}{5.3}+\frac{\mathrm{Cr}}{13}+\frac{\mathrm{Si}}{15}\ge 1.1\%.$
The sheet has a nickel content Ni.sub.surf at any point of the steel in the vicinity of the surface over a depth Δ, such that: Ni.sub.surf >Ni.sub.nom, Ni.sub.nom denoting the nominal nickel content of the steel, and such that, Ni.sub.max denoting the maximum nickel content within Δ: $\frac{\left({\mathrm{Ni}}_{\max }+{\mathrm{Ni}}_{\mathrm{nom}}\right)}{2}\times \left(\Delta \right)\ge 0.6,$
and such that: $\frac{\left({\mathrm{Ni}}_{\max }-{\mathrm{Ni}}_{\mathrm{nom}}\right)}{\Delta }\ge 0.01$
and the surface density of all of the particles D.sub.i and the surface density of the particles D.sub.(>2 μm) larger than 2 micrometers satisfy, at least to a depth of 100 micrometers in the vicinity of the surface of said sheet:
D.sub.i+6.75 D.sub.(>2 μm) <270
D.sub.i and D.sub.(>2 μm) being expressed as number of particles per square millimeter, and said particles denoting all the oxides, sulfides, and nitrides, either pure or combined such as oxysulfides and carbonitrides, present in the steel matrix.

Provided is a hot rolled steel sheet comprising a predetermined composition wherein the hot rolled steel sheet comprises first ferrite with an average orientation difference in the same grain of 0.5 to 5.0° in 30 to 70 vol %, at least one type of structures among bainite and second ferrite with an average orientation difference of 0 to less than 0.5° and the first ferrite in a total of 95 vol % or more, a balance microstructure of 5 vol % or less, has an average grain size of the first ferrite of 0.5 to 5.0 μm, and has an average grain size of the other structures of 1.0 to 10 μm. Provided is a method for producing a hot rolled steel sheet comprising rolling where two or more consecutive passes of rolling including a final pass are performed under conditions of a rolling temperature: A point or more and less than Ae.sub.3 point etc., and where a total strain amount of all passes satisfying the conditions is 1.4 to 4.0, cooling by a 20 to 50° C./sec average cooling rate, and coiling the steel sheet at 300° C. to 600° C.

The present disclosure relates to wear-resistant steel comprising, by weight, carbon (C): 0.19 to 0.28%, silicon (Si): 0.1 to 0.7%, manganese (Mn): 0.6 to 1.6%, phosphorus (P): 0.05% or less, sulfur (S): 0.02% or less, aluminum (Al): 0.07% or less, chromium (Cr): 0.01 to 0.5%, nickel (Ni): 0.01 to 3.0%, copper (Cu): 0.01 to 1.5%, molybdenum (Mo): 0.01 to 0.5%, boron (B): 50 ppm or less, and cobalt (Co): 0.02% or less, further comprising one or more selected from the group consisting of titanium (Ti): 0.02% or less, niobium (Nb): 0.05% or less, vanadium (V): 0.05% or less, and calcium (Ca): 2 to 100 ppm, and comprising a remainder of iron (Fe) and other unavoidable impurities, wherein C, Ni, and Cu satisfy the following relationship 1, wherein a microstructure includes 97 area % or more of martensite:
C×Ni×Cu≥0.05.  [Relationship 1]
.

This high-strength cold-rolled steel sheet has a predetermined chemical composition, wherein a microstructure at a ¼ position of a sheet thickness from a surface includes predetermined ranges of volume percentages of tempered martensite, residual austenite, ferrite and bainite, and martensite, wherein a microstructure at a position 25 μm from the surface includes, predetermined ranges of volume percentage of ferrite and bainite, and martensite and tempered martensite, wherein in the position 25 μm from the surface, an average grain size of the martensite and the tempered martensite is 5.0 μm or less, a tensile strength is 1,310 MPa or more, and a uniform elongation is 5.0% or more, and R/t is 5.0 or less, the R/t being a ratio of a limit bend radius R in 90° V-bending to a sheet thickness t.

A high-strength galvanized steel sheet of the present invention includes a steel sheet having a chemical composition containing a predetermined component element, and a steel structure in which an average grain size of inclusions containing at least one of Al, Si, Mg, and Ca and existing in an area extending from a surface to a position of ⅓ of a sheet thickness is 50 μm or less, and an average nearest distance between ones of the inclusions is 20 μm or more; and a galvanized layer provided on a surface of the steel sheet and having a coating weight per one surface of 20 g/m.sup.2 or more and 120 g/m.sup.2 or less, in which an amount of diffusible hydrogen contained in the steel is less than 0.25 mass ppm, and a tensile strength is 1100 MPa or more.

The present invention relates to a flat steel product which has good deep-drawing ability, low edge-crack sensitivity and good bending behaviour. To this end, the flat steel product contains a steel which consists of (in wt %) 0.1-0.5% C, 1.0-3.0% Mn, 0.9-1.5% Si, up to 1.5% Al, up to 0.008% N, up to 0.020% P, up to 0.005% S, 0.01-1% Cr and optionally one or more of the following elements: up to 0.2% Mo, up to 0.01% B, up to 0.5% Cu, up to 0.5% Ni and optionally a total of 0.005-0.2% microalloying elements, the remainder being iron and unavoidable impurities, wherein 75<(Mn2+55*Cr)/Cr<3000 where Mn is the Mn content of the steel in wt % and Cr is the Cr content of the steel in wt %. The steel has a structure which consists of at least 80 area % martensite, of which at least 75 area % is tempered martensite and at most 25 area % is non-tempered martensite, at least 5 volume % residual austenite, 0.5 to 10 area % ferrite and at most 5 area % bainite, wherein in the region of the phase boundary between tempered martensite and residual austenite there is a low-Mn ferrite seam which has a width of at least 4 nm and at most 12 nm and the Mn content of which is at most 50% of the average Mn content of the flat steel product. The flat steel product contains carbides with a length of less than or equal to 250 nm. The invention also relates to a method for producing a flat steel product according to the invention, in which method the structural characteristics of the flat steel product according to the invention are set by suitable heat treatment.

Disclosed are a high-strength ultra-thick steel material and a method for manufacturing same. The high-strength ultra-thick steel material comprises in weight % 0.04-0.1% of C, 1.2-2.0% of Mn, 0.2-0.9% of Ni, 0.005-0.04% of Nb, 0.005-0.03% of Ti and 0.1-0.4% of Cu, 100 ppm or less of P and 40 ppm or less of S with a balance of Fe, and inevitable impurities, and comprises, in a subsurface area up to t/10 (t hereafter being referred to as the thickness of the steel material), polygonal ferrite of 50 area % or greater (including 100 area %) and bainite of 50 area % or less (including 0 area %) as microstructures.

Provided is a high strength steel sheet that has a tensile strength of 1180 MPa or more and a uniform elongation of 6 % or more. The high strength steel sheet has a chemical composition that contains predetermined components with a MSC of 3.0 mass% to 4.2 mass%. The high strength steel sheet has a microstructure including upper bainite in an area fraction of 70 % or more as a main phase, fresh martensite and retained austenite in a total area fraction of 7 % to 30 %, with the retained austenite having an area fraction of 2 % or more. The high strength steel sheet has a mechanical property with a uniform elongation of 6 % or more and a tensile strength of 1180 MPa or more.