A ductile iron composition including, by weight: about 3.4% to about 4.0% Si; about 3.0% to about 3.5% C; about 0.5% to about 1.0% Cr; about 0.02% to about 0.05% Mo; up to about 0.01% S; up to about 0.5% Mn; and balance iron and incidental impurities.

The composition has a a ferritic body center cubic microstructure and has a graphite nodule density of greater than 100 per mm.sup.2. A method for forming a ductile iron composition is also disclosed.

One embodiment of the present invention provides an ultra-thick structural steel having excellent brittle crack initiation resistance, and a manufacturing method therefor, the ultra-thick structural steel comprising, by wt %, 0.03-0.08% of C, 1.6-2.2% of Mn, 0.6-1.3% of Ni, 0.005-0.03% of Nb, 0.005-0.02% of Ti, 0.1-0.4% of Cu, 100 ppm or less of P, 40 ppm or less of S, 1.5 ppm or less of H, and the balance of Fe and other inevitable impurities, wherein the sum of acicular ferrite and granular bainite in the microstructure is 80% or more by area fraction, the sum of the total length of cracks having a size of 30 μm or more per unit area of 1 mm2 in a ±1 mm region on the basis of the thickness center of the steel is 130 μm or less, and the yield strength is 500 MPa or more.

In a hot-rolled steel sheet, an average pole density of an orientation group of {100}<011> to {223}<110>, which is represented by an arithmetic average of pole density of each orientation of {100}<011>, {116}<110>, {114}<110>, {112}<110>, and {223}<110> in a center portion of a sheet thickness which is a range of the sheet thickness of ⅝ to ⅜ from a surface of the steel sheet, is 1.0 or more and 4.0 or less, the pole density of a crystal orientation of {332}<113> is 1.0 or more and 4.8 or less, an average grain size in a center in the sheet thickness is 10 μm or less, and a microstructure includes, by a structural fraction, pearlite more than 6% and ferrite in the balance.

A hot-rolled steel sheet includes, by mass %, C: 0.030% or more and less than 0.075%, Si+Al: 0.08% to 0.40%, Mn: 0.5% to 2.0%, and Ti: 0.020% to 0.150%, and includes a microstructure having a ferrite and a martensite. The hot-rolled steel sheet includes a microstructure having, by area %, 90% to 98% of the ferrite, 2% to 10% of the martensite, 0% to 3% of a bainite, and 0% to 3% of a pearlite. In the martensite, the number proportion of martensite grains having a hardness of 10.0 GPa or more is 10% or less, and a ratio N1/N2 of the number N1 of martensite grains having a hardness of 8.0 GPa or more and less than 10.0 GPa to the number N2 of martensite grains having a hardness of less than 8.0 GPa is 0.8 to 1.2.

The present invention relates to a hot stamped component, a precoated steel sheet used for hot stamping, and a hot stamping process. The hot stamped component of the present invention is provided with a coating of aluminium or an aluminium alloy on at least one surface of the base steel, the coating is produced by interdiffusion between the base steel and a precoating of aluminium or aluminium alloy, and the coating has a thickness of 6 to 26 μm.

Provided is a high-strength hot-dip galvanized steel sheet having excellent plating adhesion, formability, and hole expandability with an ultimate tensile strength of 980 MPa or more, the hot-dip galvanized steel sheet comprising a hot-dip galvanized layer formed on a surface of a base steel sheet. The base steel sheet contains, by mass %, C: 0.05% to 0.4 %; Si: 0.01% to 3.0%; Mn: 0.1% to 3.0%; Al: 0.01 to 2.0%; in which Si+Al >0.5%, P: limited to 0.04% or less; S: limited to 0.05% or less; N: limited to 0.01% or less; and a balance including Fe and inevitable impurities, a microstructure of the base steel sheet contains 40% or more by total volume fraction of martensite and bainite, 8% or more by volume fraction of residual austenite, and a balance of the microstructure being ferrite or ferrite and 10% or less by volume fraction of pearlite. The martensite contains 10% or more by total volume fraction of two or more kinds of three kinds of martensites (1), (2), and (3), and the hot-dip galvanized layer contains less than 7 mass % of Fe.

A steel for a carburizing and a carburized steel component having a steel portion and a carburized layer with a thickness of more than 0.4 mm to less than 2 mm which is formed on an outside of the steel portion. A chemical composition of the steel for the carburizing and the steel portion of the carburized steel component satisfies simultaneously equations of a hardness parameter, a hardenability parameter, and a TiC precipitation parameter.

A steel for a carburizing and a carburized steel component having a steel portion and a carburized layer with a thickness of more than 0.4 mm to less than 2 mm which is formed on an outside of the steel portion. A chemical composition of the steel for the carburizing and the steel portion of the carburized steel component satisfies simultaneously equations of a hardness parameter, a hardenability parameter, and an AlN precipitation parameter.

The present invention is steel for surface hardening for machine structural use which contains, by mass %, C: 0.3 to 0.6%, Si: 0.02 to 2.0%, Mn: 0.35 to less than 1.5%, and Al: 0.01 to 0.5%, is restricted to B: less than 0.0003%, S: 0.0001 to 0.021%, N: 0.003 to 0.0055%, P: 0.0001 to 0.03%, and O: 0.0001 to 0.0050%, has a ratio Mn/S of Mn and S satisfying 70 to 30,000, has a balance of Fe and unavoidable impurities, and, when nitrided, then induction hardened, has a surface hardenability of a Vicker's hardness when tempered at 300° C. of 650 or more.

A method that improves stretch flange formability of a steel sheet by individual treatment matching a material of the steel sheet without performing heat treatment in a die. This method is a method for manufacturing a steel sheet for cold press, and the steel sheet is manufactured by heating an edge of the steel sheet to a temperature within a heating temperature range preset according to a microstructure of the steel sheet and cooling the steel sheet. A region, within an edge of the steel sheet subjected to shearing in a shearing step, where it is estimated that a stretch flange crack is likely to occur when a press component is formed by cold pressing is determined, and a site to be heated and cooled is set within the region. By press-forming the manufactured steel sheet, a target press component is manufactured.