An exemplary embodiment of the present invention relates to a magnesium alloy sheet and a manufacturing method thereof. According to an exemplary embodiment of the present invention, a magnesium alloy sheet including 1.0 to 10.5 wt % of Al, 0.1 to 2.0 wt % of Zn, 0.1 to 2.0 wt % of Ca, 0.03 to 1.0 wt % of Y, 0.002 to 0.02 wt % of Be, and a balance of Mg and inevitable impurities, with respect to a total of 100 wt % of the magnesium alloy sheet, may be provided.

An exemplary embodiment of the present invention relates to a magnesium alloy sheet and a manufacturing method thereof. According to an exemplary embodiment of the present invention, a magnesium alloy sheet including 1.0 to 10.5 wt % of Al, 0.1 to 2.0 wt % of Zn, 0.1 to 2.0 wt % of Ca, 0.03 to 1.0 wt % of Y, 0.002 to 0.02 wt % of Be, and a balance of Mg and inevitable impurities, with respect to a total of 100 wt % of the magnesium alloy sheet, may be provided.

The invention is directed to the interventionless activation of wellbore devices using dissolving and/or degrading and/or expanding structural materials. Engineered response materials, such as those that dissolve and/or degrade or expand upon exposure to specific environment, can be used to centralize a device in a wellbore.

The invention is directed to the interventionless activation of wellbore devices using dissolving and/or degrading and/or expanding structural materials. Engineered response materials, such as those that dissolve and/or degrade or expand upon exposure to specific environment, can be used to centralize a device in a wellbore.

The invention relates to a preparation method for a magnesium matrix composite. The preparation method comprises the following steps: (1) preparing magnesium ingots as raw materials and salt flux and reinforcements; (2) placing the salt flux in a crucible, performing heating to prepare salt flux melts, adding the reinforcements; (3) performing pouring into a normal-temperature crucible, and performing cooling to obtain precursors; (4) adding the raw materials in an iron crucible, and performing melting at 953K-1043K; (5) placing the precursors in raw material melt, after stirring, under a condition of 953K-993K, performing standing so that scum and melt are obtained; and (6) removing the scum, lowering temperature to 973K-982K, and performing casting. The method provided by the present invention is simple in process and low in cost. The method can be used for preparing bulk structural members of the magnesium matrix composite, and can be used for automatic production.

The invention relates to a preparation method for a magnesium matrix composite. The preparation method comprises the following steps: (1) preparing magnesium ingots as raw materials and salt flux and reinforcements; (2) placing the salt flux in a crucible, performing heating to prepare salt flux melts, adding the reinforcements; (3) performing pouring into a normal-temperature crucible, and performing cooling to obtain precursors; (4) adding the raw materials in an iron crucible, and performing melting at 953K-1043K; (5) placing the precursors in raw material melt, after stirring, under a condition of 953K-993K, performing standing so that scum and melt are obtained; and (6) removing the scum, lowering temperature to 973K-982K, and performing casting. The method provided by the present invention is simple in process and low in cost. The method can be used for preparing bulk structural members of the magnesium matrix composite, and can be used for automatic production.

This application relates to a wrought magnesium alloy and a method of manufacturing the same, and a high-speed extrusion method for manufacturing an extrudate using the same. In one aspect, the magnesium alloy includes 2.0 wt % to 8.0 wt % of bismuth (Bi), 0.5 wt % to 6.5 wt % aluminum (Al), the balance of magnesium (Mg), and inevitable impurities. Using a magnesium alloy for high-speed extrusion according to the present disclosure, it is possible to manufacture a magnesium alloy extrudate having a good surface quality without hot cracking even under high-temperature (extrusion temperature: 300° C. to 450° C.) and high-speed (die-exit speed: 40 m/min to 80 m/min) extrusion conditions. Furthermore, the extrudate manufactured from the magnesium alloy exhibits greatly improved strength and elongation compared to existing magnesium extrudates even when the alloy does not contain a rare-earth metal.

This application relates to a wrought magnesium alloy and a method of manufacturing the same, and a high-speed extrusion method for manufacturing an extrudate using the same. In one aspect, the magnesium alloy includes 2.0 wt % to 8.0 wt % of bismuth (Bi), 0.5 wt % to 6.5 wt % aluminum (Al), the balance of magnesium (Mg), and inevitable impurities. Using a magnesium alloy for high-speed extrusion according to the present disclosure, it is possible to manufacture a magnesium alloy extrudate having a good surface quality without hot cracking even under high-temperature (extrusion temperature: 300° C. to 450° C.) and high-speed (die-exit speed: 40 m/min to 80 m/min) extrusion conditions. Furthermore, the extrudate manufactured from the magnesium alloy exhibits greatly improved strength and elongation compared to existing magnesium extrudates even when the alloy does not contain a rare-earth metal.

An injection molding material for magnesium thixomolding includes: a powder containing Mg as a main component; and a chip containing Mg as a main component, in which a proportion of the powder in the injection molding material for magnesium thixomolding is 5 mass % or more and 45 mass % or less, and a tap density of the powder is 0.15 g/cm.sup.3 or more.

A method for manufacturing a thixomolding material for thixomolding includes a drying step of heating a mixture containing a first powder that contains Mg as a main component, a second powder, a binder, and an organic solvent to dry the organic solvent contained in the mixture, and a stirring step of stirring the mixture heated in the drying step.