A high-strength plated steel sheet sequentially includes an internal oxidized layer, a soft layer containing the internal oxidized layer, and a hard layer including a structure having metallic structure which contains a low-temperature-transformation produced phase in a proportion of 20 to 85% by area of the whole of the metallic structure, polygonal ferrite in a proportion more than 10% by area, and 70% or less by area of the whole of the metallic structure, and-retained austenite in a proportion of 5% or more by volume of the whole of the metallic structure. The high-strength plated steel sheet satisfies the average depth D of the soft layer being 20 μm or more, the average depth d of the internal oxidized layer being 4 μm or more and less than D, and a tensile strength being 980 MPa or more.

When a non-oriented electrical steel sheet is produced by hot rolling a slab containing, by mass %, C: not more than 0.0050%, Si: 1.5-5.0%, Mn: 0.20-3.0%, sol. Al: not more than 0.0050%, P: not more than 0.2%, S: not more than 0.0050% and N: not more than 0.0040% to form a hot rolled sheet, cold rolling the hot rolled sheet without conducting a hot band annealing and then subjecting to a finish annealing, a compositional ratio of CaO in oxide-based inclusions existing in the slab defined by CaO/(SiO.sub.2+Al.sub.2O.sub.3+CaO) is set to not less than 0.4 and/or a compositional ratio of Al.sub.2O.sub.3 defined by Al.sub.2O.sub.3/(SiO.sub.2+Al.sub.2O.sub.3+CaO) is set to not less than 0.3, and a coiling temperature in the hot rolling is set to not lower than 650° C.

A series of solid solutions AlFe.sub.2.sub._.sub.xMnxB.sub.2 have been synthesized by arc-melting and characterized by powder X-ray diffraction, and magnetic measurements. All the compounds adopt the parent AlFe.sub.2B.sub.2-type structure, in which infinite zigzag chains of B atoms are connected by Fe atoms into [Fe.sub.2B.sub.2] slabs that alternate with layers of Al atoms along the b axis. The parent AlFe.sub.2B.sub.2 is a ferromagnet with T.sub.c=282 K. A systematic investigation of solid solutions AlFe.sub.2.sub._.sub.xMn.sub.x.B.sub.2 showed a non-linear change in the structural and magnetic behavior. The ferromagnetic ordering temperature is gradually decreased as the Mn content (x) increases. The substitution of Mn for Fe offers a convenient method for the adjustment of the ferromagnetic ordering temperature of AlFe.sub.2B.sub.2.

A non-oriented electrical steel sheet includes C: 0 to 0.0050 mass %, Si: 0.50 to 2.70 mass %, Mn: 0.10 to 3.00 mass %, Al: 1.00 to 2.70 mass %, and P: 0.050 to 0.100 mass %. In the non-oriented electrical steel sheet, Al/(Si+Al+0.5×Mn) is 0.50 to 0.83, Si+Al/2+Mn/4+5×P is 1.28 to 3.90, Si+Al+0.5×Mn is 4.0 to 7.0, the ratio of the intensity of {100} plane I{100} to the intensity of {111} plane I{111} is 0.50 to 1.40, the specific resistance is 60.0×10.sup.−8 Ω.Math.m or higher at room temperature, and the thickness is 0.05 mm to 0.40 mm.

A method of manufacturing a part including selective laser melting of a powder including a steel alloy containing, by weight, 16% to 19% chromium and 12.2% to 13.5% nickel, wherein the powder is substantially non-magnetic.

Disclosed herein is a high-strength plated steel sheet having a plated layer on the surface of a base steel sheet and containing predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet; and a hard layer consisting of a structure which is mainly composed of martensite and bainite and in which the average grain size of prior austenite is 20 μm or less. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.

The high-strength plated steel sheet of the present invention has a plated layer on the surface of a base steel sheet and contains predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet: and a hard layer containing martensite, bainite, and ferrite in predetermined ranges. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.

Disclosed herein is a high-strength plated steel sheet containing an internal oxidized layer, a soft layer including the internal oxidized layer, and a hard layer including a structure having metallic structure containing a low-temperature-transformation produced phase in a proportion of 70% or more by area of the whole of the metallic structure, in which polygonal ferrite is in a proportion of 0% or more by area, and 10% or less by area of the same, and retained austenite is in a proportion of 5% or more by volume of the same. The high-strength plated steel sheet satisfies the average depth D of the soft layer is 20 μm or more, the average depth d of the internal oxidized layer is 4 μm or more and less than D, and a tensile strength of 980 MPa or more.

Provided is an oriented electrical steel sheet including a groove existing on the surface of the electrical steel sheet and a forsterite layer formed on a part or all of the surface of the electrical steel sheet, in which forsterite which is extended from the forsterite layer and penetrates to a base steel sheet in an anchor form is present on the surface of the side of the groove.

A bolt of the present invention has a composition comprising: 0.50 mass % or greater and 0.65 mass % or less of carbon (C), 1.5 mass % or greater and 2.5 mass % or less of silicon (Si), 1.0 mass % or greater and 2.0 mass % or less of chromium (Cr), 0.2 mass % or greater and 1.0 mass % or less of manganese (Mn), 1.5 mass % or greater and 5.0 mass % or less of molybdenum (Mo), wherein a total amount of phosphorous (P) and sulfur (S) as impurities is 0.03 mass % or less, the remaining is iron (Fe), and the bolt comprises an iron based oxide film with a film thickness of 3 μm or greater and 20 μm or less on the surface thereof. The bolt has excellent delayed fracture resistance and reliably provides a fastening axial force.