Disclosed is a high-permeability ferrite-based stainless steel. According to an embodiment, the disclosed high-permeability ferrite-based stainless steel includes, in percent by weight (wt %), 0.0005 to 0.02% of C, 0.005 to 0.02% of N, 0.2 to 2.0% of Si, 10.0 to 25.0% of Cr, 0.05 to 0.5% of Nb, and the remainder of Fe and other inevitable impurities, wherein a Nb/(C+N) value satisfies a range of 5 to 20 and a <001>//RD texture fraction is 5% or more.

The present invention relates to a grain-oriented electrical steel sheet including 2.0 to 6.0 wt % of Si, 0.01 wt % or less (excluding 0 wt %) of C, 0.01 wt % or less (excluding 0 wt %) of N, and 0.005 to 0.1 wt % of Co, and including a balance of Fe and other inevitable impurities.

A method for manufacturing a non-oriented electrical steel sheet includes a step of performing hot rolling on a steel material having a predetermined chemical composition, a step of performing first cold rolling, a step of performing process annealing, a step of performing second cold rolling, and a step of performing any one or both of final annealing and stress relief annealing. A final pass of finish rolling is performed in a temperature range equal to or higher than an Ar1 temperature, the steel sheet is held for 2 hours or less in a temperature range lower than an Ac1 temperature in the final annealing, and the steel sheet is held for 1200 sec or more in a temperature range equal to or higher than 600° C. and lower than the Ac1 temperature in the stress relief annealing.

Disclosed is a ferritic stainless steel having improved magnetization including, in percent by weight (wt %), 0.01% or less (excluding 0) of C) 0.003% or less (excluding 0) of N, 15 to 18% of Cr, 0.3 to 1.0% of Mn, 0.2 to 0.3% of Si, 0.005% or less (excluding 0) of Al, 0.005% or less (excluding 0) of Ti, and the balance of Fe and inevitable impurities, and satisfying the following equation,

(Ti+Al+8*(C+N)/Mn)≤0.3  Equation (1)

(wherein Ti, Al, C, N, and Mn denote amounts (wt %) of the respective elements).

A non-oriented electrical steel sheet with an average magnetostriction λ.sub.p-p at 400 Hz and 1.0 T of not more than 4.5×10.sup.−6, and area ratio of recrystallized grains at a section in rolling direction of steel sheet of 40 to 95% and an average grain size of 10 to 40 μm is obtained by subjecting a steel slab containing, in mass %, C: not more than 0.005%, Si: 2.8 to 6.5%, Mn: 0.05 to 2.0%, Al: not more than 3.0%, P: not more than 0.20%, S: not more than 0.005%, N: not more than 0.005%, Ti: not more than 0.003%, V: not more than 0.005% and Nb: not more than 0.005% and satisfying Si—2Al—Mn≥0 to hot rolling, hot-band annealing, cold rolling and finish annealing under adequate cold rolling and finish annealing conditions, and a motor core is manufactured by such a steel sheet.

Disclosed is a method for manufacturing a stainless steel for a polymer electrolyte membrane fuel cell separator, and more particularly, a method for manufacturing a stainless steel for a polymer electrolyte membrane fuel cell separator capable of obtaining low contact resistance and high corrosion resistance by effectively removing a non-conductive coating and forming a new coating. According to an embodiment, the disclosed method for manufacturing a stainless steel for a polymer electrolyte membrane fuel cell separator includes performing alternating current electrolysis by immersing, in a sulfuric acid solution, a stainless steel having a passivation coating formed on a surface thereof by cold rolling and bright annealing, wherein the alternating current electrolysis is performed by applying a current density of 10 to 30 A/dm.sup.2.

A ferritic stainless steel sheet includes a base metal and a nitrided layer that is formed on a surface of the base metal, a chemical composition of the base metal contains, in mass %, C: 0.001 to 0.020%, Si: 0.01 to 1.50%, Mn: 0.01 to 1.50%, P: 0.010 to 0.050%, S: 0.0001 to 0.010%, Cr: 16.0 to 25.0%, N: 0.001 to 0.030%, Ti: 0.01 to 0.30%, and optional elements, with the balance: Fe and unavoidable impurities, a steel microstructure of the base metal includes, in volume ratio, 95% or more of a ferritic phase, the nitrided layer is a layer that is present in a region from a surface of a rolled surface to a 0.05 μm depth position in a sheet thickness direction, and an average nitrogen concentration in the nitrided layer is, in mass %, 0.80% or more.

According to an exemplary embodiment of the present invention, a method for manufacturing a grain-oriented electrical steel sheet includes: a step of hot-rolling a slab to manufacture a hot-rolled steel sheet; a step of performing hot-rolled sheet annealing on the hot-rolled steel sheet; a step of performing primary cold-rolling on the hot-rolled sheet annealed hot-rolled steel sheet; a step of performing primary decarburization annealing on the primarily cold-rolled steel sheet; a step of performing secondary cold-rolling on the decarburization-annealed steel sheet; a step of performing secondary decarburization annealing on the secondarily cold-rolled steel sheet; and a step of performing continuous annealing on the secondarily decarburization-annealed steel sheet.

Provided are a motor core having excellent fatigue resistance and a method of manufacturing the motor core at a low cost. The motor core that is an electrical-steel-sheet-stacked body has an outer peripheral surface in which an appearance ratio of recrystallized grains with a grain size of 15 μm or less is 70% or more of a sheet thickness of the motor core.

A laminated core (100) has a plurality of legs having an extension direction in a direction perpendicular to a lamination direction of electrical steel sheets and a plurality of yokes having an extension direction in a direction orthogonal to the lamination direction of the electrical steel sheets and the extension direction of the legs, and, in the same position of the electrical steel sheet in the lamination direction, at least a partial region of the legs and at least a partial region of the yokes are configured by the same electrical steel sheet. The electrical steel sheet is disposed such that a first direction of directions of easy magnetization of the electrical steel sheet is along the extension direction of the legs and a second direction of the directions of easy magnetization of the electrical steel sheet is along the extension direction of the yokes.