A grain-oriented electrical steel sheet according to the present invention has a steel sheet surface provided with grooves. An average protrusion height of the surface protrusion extending along a longitudinal direction of the groove is more than 5 μm and not more than 10 μm. When the surface protrusion is viewed in a cross section including the longitudinal direction of the groove and a normal direction of the steel sheet surface, the surface protrusion includes specific portions each having a height of 50% or more with respect to a height of each peak point appearing on a profile line of the surface protrusion. In the longitudinal direction of the groove, the total length of the specific portions is a length of 30% or more with respect to an overall length of the surface protrusion.

A high permeability grain oriented electrical steel having a chemistry comprising, all in weight percent, 2.5% to 4.5% silicon, 0.02% to 0.08% carbon, 0.01 to 0.05% aluminum, 0.005% to 0.050% sulfur or selenium, 0.02 to 0.20% manganese, 0.05 to 0.20% tin, 0.05 to 1% copper, 0.5% to 2.0% chromium, up to 0.10% phosphorus and up to 0.20% antimony with the balance being essentially iron and residual elements. The steel contains chromium and phosphorus in such amounts that a Cr:(P+0.25Sb) ratio is below 80:1 or, below 50:1, or below 30:1 which provides highly stable magnetic properties in the finished steel sheet. A hot processed band comprised of such steel is annealed and rapidly cooled after such annealing at a rate of at least 50° C. per second from 875-950° C. to a temperature below 400° C. prior to cold rolling to final thickness. Such steel forming a hot processed band having a thickness of from 1.5 to 4.0 mm and having a volume resistivity of at least 50 μΩ-cm, an austenite volume fraction (γ1150° C.) of at least 20%, and an isomorphic layer thickness of at least 2% of the total thickness on at least one surface of the hot processed band.

A motor comprising a steel sheet used as a core material of the motor, wherein the steel sheet includes a composition including: by mass %, 0.010% or less of C; 2.0% to 7.0% of Si; 2.0% or less of Al; 0.05% to 1.0% of Mn; 0.005% or less of S; 0.005% or less of N; and balance Fe and inevitable impurities; the steel sheet includes a magnetic flux density changing area where a change ΔB in magnetic flux density to a change ΔH=50 A/m in a magnetic field, is equal to or higher than 0.50 T; a thickness of the steel sheet is 0.05 mm to 0.20 mm; and an eddy-current loss of the steel sheet, at 1000 Hz−1.0 T, is equal to or less than 0.55 of a total iron loss.

A hot stamped body comprising a steel base material and an Al—Zn—Mg-based plating layer formed on a surface of the steel base material, wherein the plating layer has a predetermined chemical composition, the plating layer comprises an interfacial layer positioned at an interface with the steel base material and containing Fe and Al and a main layer positioned on the interfacial layer, the main layer comprises, by area ratio, 10.0 to 85.0% of an Mg—Zn containing phase and 15.0 to 90.0% of an Fe—Al containing phase, the Mg—Zn containing phase comprises at least one selected from the group consisting of an MgZn phase, Mg.sub.2 Zn.sub.3 phase, and MgZn.sub.2 phase, and the Fe—Al containing phase comprises at least one of an FeAl phase and Fe—Al—Zn phase and an area ratio of the Fe—Al—Zn phase in the main layer is 10.0% or less.

Grain-oriented electrical steel sheet excellent in magnetic properties and adhesion of a primary coating to a base steel sheet and with few defects where the base metal is exposed in point defects and a method for manufacturing grain-oriented electrical steel sheet are provided. This is characterized by being provided with a base steel sheet and a primary coating. The primary coating satisfies (1) Number density D3 of Al concentrated regions: 0.015 to 0.150/μm.sup.2 (2) (Area S5 of regions comprised of anchoring oxide layer regions and Al concentrated regions)/(area S3 of Al concentrated regions)≥0.30, (3) Distance H5 of mean value of heights in thickness direction of regions of comprised of anchoring oxide layer regions and Al concentrated regions minus HO: 0.4 to 4.0 μm, (4) (Perimeter L5 of regions comprised of anchoring oxide layer regions and Al concentrated regions)/(observed area S0): 0.020 to 0.500 μm/μ.sup.2, and (5) (Area S1 of anchoring oxide layer regions)/(observed area S0)≥0.15.

A seamless steel pipe of the present invention is a seamless steel pipe having a composition that includes, in mass %, C: 0.02 to 0.12%, Si: 0.010 to 1.00%, Mn: 0.10 to 2.00%, P: 0.050% or less, S: 0.004% or less, Al: 0.010 to 0.100%, Cu: 0.03 to 0.80%, Ni: 0.02 to 0.50%, Cr: 0.55 to 1.00%, Sb: 0.005 to 0.20%, and the balance Fe and incidental impurities, and satisfying the following formula (1),

1.7×Cu*+11×Cr*+3.8×Sb*≥13.5   (1), where Cu*, Cr*, and Sb* represent average concentrations of Cu, Cr, and Sb, respectively, in mass %, as measured in a region 0.5 to 2.0 mm away from an outer surface of the steel pipe, the seamless steel pipe having a yield strength of 230 MPa or more, and a tensile strength of 380 MPa or more.

An austenitic stainless steel material is provided that has high creep strength even when used at an average operation temperature of more than 600 to 750° C. after welding with higher heat input, and furthermore, has excellent stress relaxation cracking resistance even after use for a long time period at the average operation temperature after welding with higher heat input. The steel material has a chemical composition which consists of, in mass %, C: 0.030% or less, Si: 1.50% or less, Mn: 2.00% or less, P: 0.045% or less, S: 0.0300% or less, Cr: 15.00 to 25.00%, Ni: 8.00 to 20.00%, N: 0.050 to 0.250%, Nb: 0.10 to 1.00%, Mo: 0.05 to 5.00%, and B: 0.0005 to 0.0100%, with the balance being Fe and impurities, and a ratio of the dissolved N amount (mass %) with respect to the content of N (mass %) in the steel material is 0.40 to 0.90.

Provided is a method for manufacturing a high-strength galvanized steel sheet. Heating in a first half of oxidizing treatment is performed at a temperature of 400° C. to 750° C. in an atmosphere having a particular O.sub.2 concentration and a particular H.sub.2O concentration, and heating in a second half of the oxidizing treatment is performed at a temperature of 600° C. to 850° C. in an atmosphere having a particular O.sub.2 concentration and a particular H.sub.2O concentration. Subsequently, heating in a heating zone for reduction annealing is performed to a temperature of 650° C. to 900° C. at a particular heating rate in an atmosphere having a particular H.sub.2 concentration and a particular H.sub.2O concentration with the balance being N.sub.2 and inevitable impurities, and soaking in a soaking zone for the reduction annealing is performed in an atmosphere having a particular H.sub.2 concentration and a particular H.sub.2O concentration with the balance being N.sub.2 and inevitable impurities.

A stainless steel material including a base material made of ferritic stainless steel, a Cr oxide layer formed on a surface of the base material, and a spinel oxide layer formed on a surface of the Cr oxide layer, wherein a chemical composition of the base material satisfies [16.0≤Cr+3×Mo−2.5×B−17×C−3−Si≤35.0], a thickness of the Cr oxide layer (T.sub.Cr) and a thickness of the spinel oxide layer (T.sub.S) satisfy [0.55≤T.sub.Cr/T.sub.S≤6.7], the base material contains precipitate including one or more kinds selected from a M.sub.23C.sub.6, a M.sub.2B, a complex precipitate in which M.sub.2B acts as a precipitation nucleus, and M.sub.23C.sub.6 precipitates on a surface of the M.sub.2B, and a complex precipitate in which NbC acts as a precipitation nucleus, and M.sub.23C.sub.6 precipitates on a surface of the NbC, and a part of the precipitate protrude from the surface of the Cr oxide layer.

A steel for forging mechanical parts including the following elements, expressed in percentage by weight 0.2%≤C≤0.5%; 0.8%≤Mn≤1.5% ; 0.4%≤Si≤1%; 0.15%≤V≤0.6%; 0.01%≤Nb≤0.15%; 0.01%≤Cr≤0.5%; 0.01%≤P≤0.05%; 0.04%≤S≤0.09%; 0.01%≤N≤0.025%; and can contain one or more of the following optional elements 0%≤Al≤0.05%; 0%≤Mo≤0.5%; 0.01%≤Ni≤0.5%; 0%≤Ti≤0.2%; 0%≤B≤0.008%; 0%≤Cu≤0.5%; the remainder composition being composed of iron and unavoidable impurities caused by processing, the microstructure of said steel comprising 50% to 90% of Pearlite, 10% to 40% of Ferrite, with an optional presence of acicular ferrite between 0% and 2%, a niobium equivalent of 80% or more.