The present invention can provide light-colored magnetic particles having a zirconium oxide coating layer formed on a magnetic core, and having a silver coating layer formed on the zirconium oxide coating layer, and a part of the surface of the zirconium oxide coating layer is exposed to the outside, but chemical resistance is excellent, and thus the magnetic particles hardly cause a change of magnetic characteristics so as to be suitable for security elements.

Disclosed is a duplex stainless clad steel plate in which a duplex stainless steel plate as a cladding metal is bonded or joined to one or both surfaces of a base steel plate, in which the base steel plate comprises a predetermined chemical composition such that Nb/N is 3.0 or more and Ceq is 0.35 to 0.45, and the duplex stainless steel plate comprises: a predetermined chemical composition such that PI is 33.0 to 38.0; and a microstructure containing a ferrite phase in an area fraction of 35% to 65%, and in the microstructure, an amount of precipitated Cr is 1.00% or less and an amount of precipitated Mo is 0.50% or less.

Flaky magnetic metal particles of embodiments each have a flat surface and a magnetic metal phase containing iron (Fe), cobalt (Co), and silicon (Si). An amount of Co is from 0.001 at % to 80 at % with respect to the total amount of Fe and Co. An amount of Si is from 0.001 at % to 30 at % with respect to the total amount of the magnetic metal phase. The flaky magnetic metal particles have an average thickness of from 10 nm to 100 μm. An average value of the ratio of the average length in the flat surface with respect to a thickness in each of the flaky magnetic metal particles is from 5 to 10,000. The flaky magnetic metal particles have the difference in coercivity on the basis of direction within the flat surface.

A soft magnetic powder of the invention has a composition represented by Fe.sub.100-a-b-c-d-e-fCu.sub.aSi.sub.bB.sub.cM.sub.dM′.sub.eX.sub.f (at %) [wherein M is Nb, W, Ta, Zr, Hf, Ti, or Mo, M′ is V, Cr, Mn, Al, a platinum group element, Sc, Y, Au, Zn, Sn, or Re, X is C, P, Ge, Ga, Sb, In, Be, or As, and a, b, c, d, e, and f are numbers that satisfy the following formulae: 0.1≤a≤3, 0<b≤30, 0<c≤25, 5≤b+c≤30, 0.1≤d≤30, 0≤e≤10, and 0≤f≤10], wherein a crystalline structure having a particle diameter of 1 nm or more and 30 nm or less is contained in an amount of 40 vol % or more, and the difference in the coercive force of the powder after classification satisfies predetermined conditions.

A soft magnetic powder of the invention has a composition represented by Fe.sub.100-a-b-c-d-e-fCu.sub.aSi.sub.bB.sub.cM.sub.dM′.sub.eX.sub.f (at %) [wherein M is Nb, W, Ta, Zr, Hf, Ti, or Mo, M′ is V, Cr, Mn, Al, a platinum group element, Sc, Y, Au, Zn, Sn, or Re, X is C, P, Ge, Ga, Sb, In, Be, or As, and a, b, c, d, e, and f are numbers that satisfy the following formulae: 0.1≤a≤3, 0<b≤30, 0<c≤25, 5≤b+c≤30, 0.1≤d≤30, 0≤e≤10, and 0≤f≤10], wherein a crystalline structure having a particle diameter of 1 nm or more and 30 nm or less is contained in an amount of 40 vol % or more, and the difference in the coercive force of the powder after classification satisfies predetermined conditions.

Described herein are thin metal strips having hot rolled exterior side surfaces characterized as being primarily or substantially free of all prior austenite grain boundaries, or at least primarily or substantially free of all prior austenite grain boundaries, and including elongated surface structure. As a result, because the prior austenite grain boundaries are not primarily or substantially present, all such prior austenite grain boundaries are not susceptible to grain boundary etching due to acid etching or pickling. In particular examples, the thin metal strips undergo hot rolling performed with a coefficient of friction equal to or greater than 0.20 with or without use of lubrication.

The present disclosure relates to an iron-based prealloy powder having excellent strength and processability, and an iron-based alloy powder for powder metallurgy and a sinter-forged member using the same. The iron-based prealloy powder for powder metallurgy according to an embodiment of the present disclosure includes 0.5 to 5.0 wt % of Cu, 0.1 to 0.5 wt % of Mo, and a balance of Fe and other inevitable impurities. A Cu content (Cu %) and a Mo content (Mo %) satisfy the following Relational Equation (1):
0.3×Cu %+3×Mo %≤2.7  (1).

The present disclosure relates to an iron-based prealloy powder having excellent strength and processability, and an iron-based alloy powder for powder metallurgy and a sinter-forged member using the same. The iron-based prealloy powder for powder metallurgy according to an embodiment of the present disclosure includes 0.5 to 5.0 wt % of Cu, 0.1 to 0.5 wt % of Mo, and a balance of Fe and other inevitable impurities. A Cu content (Cu %) and a Mo content (Mo %) satisfy the following Relational Equation (1):
0.3×Cu %+3×Mo %≤2.7  (1).

Disclosed is a multi-layer rolled composite board, comprising a transition layer provided between two adjacent composite layers, wherein the transition layer is an anisotropic steel sheet. Also disclosed is a manufacturing method for the multi-layer rolled composite board, the method comprising the following steps: (1) providing a transition layer between adjacent composite layers to assemble a blank, and creating a vacuum between the layers; and (2) performing composite rolling, comprising: heating the blank to 1100-1260° C. and maintaining the temperature for 0.6 h or above, then performing hot rolling at a temperature of Ar3 or above, with the final rolling temperature being controlled to be higher than 820° C., cooling at a speed of 30-100° C./s after rolling, and then coiling, with the coiling temperature being controlled to be 20-750° C. The multi-layer rolled composite board of the present invention can be greatly transformed according to different compositions and processes so as to achieve different strength grades ranging from 150 MPa to 1700 MPa, thereby providing the basis for different specific mechanical properties for the whole steel sheet.

An iron-based rare earth boron-based isotropic magnet alloy, which has an alloy composition represented by T.sub.100-x-y-z(B.sub.1-nC.sub.n).sub.xRE.sub.yM.sub.z (where T is a transition metal element containing at least Fe, RE contains at least Nd, and M is one or more metal elements selected from the group consisting of Al, Si, V, Cr, Ti, Mn, Cu, Zn, Ga, Zr, Nb, Mo, Ag, Hf, Ta, W, Pt, Au, and Pb), 4.2 atom %≤x≤5.6 atom %, 11.5 atom %≤y≤13.0 atom %, 0.0 atom %≤z≤5.0 atom %, and 0.0≤n≤0.5, and the iron-based rare earth boron-based isotropic magnet alloy has an average crystal grain size of 10 nm to less than 70 nm as a main phase.