A method of making sintered components made from an iron-based powder composition and the sintered component per se. The method is especially suited for producing components which will be subjected to wear at elevated temperatures, consequently the components consists of a heat resistant stainless steel with hard phases including chromium carbo-nitrides. Examples of such components are parts in turbochargers for internal combustion engines.

A method of making sintered components made from an iron-based powder composition and the sintered component per se. The method is especially suited for producing components which will be subjected to wear at elevated temperatures, consequently the components consists of a heat resistant stainless steel with hard phases including chromium carbo-nitrides. Examples of such components are parts in turbochargers for internal combustion engines.

A high-strength cold-rolled steel sheet and a hot-dipped galvanized steel sheet with low deviation of material properties and excellent formability, and a method for manufacturing same are provided. The present invention relates to a low-yield-ratio high-strength cold-rolled steel sheet with low deviation of directional material and excellent formability, comprising 0.05-0.15 wt % of C, 0.2-1.5 wt % of Si, 2.2-3.0 wt % of Mn, 0.001-0.10 wt % of P, 0.010 wt % or less of S, 0.01-0.10 wt % of sol.Al, 0.010 wt % or less of N, and the balance of Fe and impurities, satisfying Si/(Mn+Si)≦0.5, wherein the microstructure of the steel sheet includes 40% or more of ferrite, 10% or less of bainite, 3% or less of residual austenite, and a balance of martensite, and the area fraction of a Mn band present in the martensite phase is 5% or less.

A grain-oriented electrical steel sheet that includes a base coating with a high TiN ratio advantageous for the application of tension to the steel sheet and has excellent magnetic property is provided. The grain-oriented electrical steel sheet includes: a base coating having a peak value PTiN of TiN in the form of osbornite, observed in a range of 42°<2θ<43° and a peak value PMg.sub.2SiO.sub.4 of Mg.sub.2SiO.sub.4 in the form of forsterite, observed in a range of 35°<2θ<36° of both more than 0 and satisfying a relationship PTiN≧PMg.sub.2SiO.sub.4, in thin-film X-ray diffraction analysis; and an iron loss W.sub.17/50 of 1.0 W/kg or less.

A grain-oriented electrical steel sheet that includes a base coating with a high TiN ratio advantageous for the application of tension to the steel sheet and has excellent magnetic property is provided. The grain-oriented electrical steel sheet includes: a base coating having a peak value PTiN of TiN in the form of osbornite, observed in a range of 42°<2θ<43° and a peak value PMg.sub.2SiO.sub.4 of Mg.sub.2SiO.sub.4 in the form of forsterite, observed in a range of 35°<2θ<36° of both more than 0 and satisfying a relationship PTiN≧PMg.sub.2SiO.sub.4, in thin-film X-ray diffraction analysis; and an iron loss W.sub.17/50 of 1.0 W/kg or less.

A high strength galvanized steel sheet having excellent surface qualities, plating adhesion, and formability is provided, wherein a galvanized layer is formed on a cold-rolled steel sheet comprising 0.1-0.3 wt % of C, 1-2.5 wt % of Si, 2.5-8 wt % of Mn, 0.001-0.5 wt % of sol. Al, at most 0.04 wt % of P, at most 0.015 wt % of S, at most 0.02 wt % of N (excluding 0 wt %), 0.1-0.7 wt % of Cr, at most 0.1 wt % of Mo, (48/14)*[N] to 0.1 wt % of Ti, 0.005-0.5 wt % of Ni, 0.01-0.07 wt % of Sb, at most 0.1 wt % of Nb, and at most 0.005 wt % of B, with the remainder being Fe and other inevitable impurities.

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 30% or more of a ferrite phase, 40% to 65% of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 40% to 55% and the total area ratio of a bainite phase having a grain diameter of more than 5 μm and/or a martensite phase having a grain diameter of more than 5 μm is 20% or less, and a tensile strength is 980 MPa or more.

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 30% or more of a ferrite phase, 40% to 65% of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 40% to 55% and the total area ratio of a bainite phase having a grain diameter of more than 5 μm and/or a martensite phase having a grain diameter of more than 5 μm is 20% or less, and a tensile strength is 980 MPa or more.

Provided are a high-strength steel sheet and a method for manufacturing the steel sheet. The high-strength steel sheet has a specified chemical composition with the balance being Fe and inevitable impurities, a microstructure including, in terms of area ratio, 25% or less of a ferrite phase, 75% or more of a bainite phase and/or a martensite phase, and 5% or less of cementite, in which, in a surface layer that is a region within 50 μm from the surface in the thickness direction, the area ratio of a ferrite phase is 5% to 20%, and a tensile strength is 1180 MPa or more.

A punching method includes: punching out a plurality of electrical steel sheets in a stacked state by a mold, wherein sheet thicknesses of the electrical steel sheets are set to be 0.35 mm or less, a Vickers hardness (test force 1 kg) of the sheets is set to be 150 to 400, and an average crystal grain size of the sheets is set to be 50 to 250 μm, a clearance of the mold is set to be 7% or more of a minimum sheet thickness of the sheet thicknesses of the electrical steel sheets and equal to or lower than 7% of a total sheet thickness of the electrical steel sheets, and a pressure that a sheet presser of the mold applies to the electrical steel sheets is set to be 0.10 MPa or more.