A neodymium-iron-boron permanent magnet, a preparation method and use thereof are disclosed. The neodymium-iron-boron permanent magnet has a composition represented by formula I: [mHR(1-m) (Pr.sub.25Nd.sub.75)].sub.x(Fe.sub.100-a-b-c-dM.sub.aGa.sub.bIn.sub.cSn.sub.d).sub.100-x-yB.sub.y formula I; where a is 0.995-3.493, b is 0.114-0.375, c is 0.028-0.125, d is 0.022-0.100; x is 29.05-30.94, y is 0.866-1.000; m is 0.02-0.05; HR is Dy and/or Tb; M is at least one selected from the group consisting of Co, Cu, Ti, Al, Nb, Zr, Ni, W and Mo.

A soft magnetic alloy and the like which simultaneously satisfy a high saturation magnetic flux density Bs and a high corrosion resistance. A soft magnetic alloy includes Mn and a component expressed by a compositional formula of ((Fe.sub.(1−(α+β))Co.sub.αNi.sub.β).sub.1−γX1.sub.γ).sub.(1−(a+b+c+d+e))B.sub.aP.sub.bSi.sub.cC.sub.dCr.sub.e (atomic ratio). X1 is one or more selected from Ti, Zr, Hf, Nb, Ta, Mo, W, Al, Ga, Ag, Zn, S, Ca, Mg, V, Sn, As, Sb, Bi, N, O, Au, Cu, rare earth elements, and platinum group elements. Further, a to e and α to γ are within predetermined ranges. Mn amount f (at %) is within a range of 0.002≤f<3.0. The soft magnetic alloy satisfies a corrosion potential of −630 mV or more and −50 mV or less and a corrosion current density of 0.3 μA/cm.sup.2 or more and 45 μA/cm.sup.2 or less.

A grain-oriented electrical steel sheet having a metallographic structure after secondary-recrystallized annealing including matrix grains of Goss-oriented secondary recrystallized grains, wherein an existence frequency of Goss-oriented crystal grains having a major diameter of 5 mm or less in the matrix grains is 1.5 grains/cm.sup.2 or more and 8 grains/cm.sup.2 or less, and the magnetic flux density B8 is 1.88 T or more, and wherein deviation angles from a rolling direction of [001] direction of the Goss-oriented crystal grains having the major diameter of 5 mm or less are 7″ or less and 5° or less, in terms of a simple or arithmetic average of α angle and β angle, respectively, wherein the α angle represents an angle formed by a longitudinal direction and a projection of the [001] on a specimen surface, and the β angle represents a tilt of the [001] out of the specimen surface.

A magnetic particle-containing composition contains magnetic particles having a plurality of peak tops in a particle size distribution curve showing a volume-based frequency distribution, a resin, and a solvent.

A magnetic particle-containing composition contains magnetic particles having a plurality of peak tops in a particle size distribution curve showing a volume-based frequency distribution, a resin, and a solvent.

An insulating material-coated soft magnetic powder includes: a core particle that includes a base portion containing a soft magnetic material containing Fe as a main component and at least one of Si, Cr, and Al, and that includes an oxide film provided on a surface of the base portion and containing an oxide of at least one of Si, Cr, and Al; and an insulating film that is provided on a surface of the core particle and that contains a ceramic, in which a thickness of the insulating film is 5 nm or more and 300 nm or less, and the oxide contained in the oxide film and the ceramic contained in the insulating film are mutually diffused at an interface between the oxide film and the insulating film.

The present invention relates to a soft high-silicon steel sheet, and more particularly, to a soft high-silicon steel sheet which has ductility even if the silicon content thereof is greater than 4%, and can thus be manufactured into a steel sheet having a high silicon content only by means of rolling without an additional siliconizing process. The soft high-silicon steel sheet may include a silicon content greater than 4 wt % and less than or equal to 7 wt % and 1 to 20% of chromium, or may include 5 to 7 wt % of Si+Al and 1 to 20 wt % of chromium.

The invention provides a method for manufacturing a powder magnetic core through simple compression molding and capable of manufacturing a complicatedly shaped powder magnetic core with reliable high strength and insulating properties. The invention is directed to a method for manufacturing a powder magnetic core with a metallic soft magnetic material powder, the method including: a first step including mixing a soft magnetic material powder and a binder; a second step including compression molding the mixture obtained after the first step; a third step including performing at least one of grinding and cutting on the compact obtained after the second step; and a fourth step including heat-treating the compact after the third step, wherein in the fourth step, the compact is heat-treated so that an oxide layer containing an element constituting the soft magnetic material powder is formed on the surface of the soft magnetic material powder.

Provided is an oriented electrical steel sheet including: a forsterite film formed on one side or both sides of an oriented electrical steel sheet substrate; and a ceramic layer formed on an entire or partial region of the forsterite film. Provided is a manufacturing method for an oriented electrical steel sheet including: preparing an oriented electrical steel sheet having a forsterite film formed on one surface or both surfaces thereof; and forming a ceramic layer by spraying ceramic powder on the forsterite film.

A sintered magnet contains Sm—Fe—N-based crystal grains and has high coercivity; and a magnetic powder is capable of forming a sintered magnet without lowering the coercivity even if heat is generated in association with the sintering. A sintered magnet comprises a crystal phase composed of a plurality of Sm—Fe—N-based crystal grains and a nonmagnetic metal phase present between the Sm—Fe—N crystal grains adjacent to each other, wherein a ratio of Fe peak intensity I.sub.Fe to SmFeN peak intensity I.sub.SmFeN measured by an X-ray diffraction method is 0.2 or less. A magnetic powder comprises Sm—Fe—N-based crystal particles and a nonmagnetic metal layer covering surfaces of the Sm—Fe—N crystal particles.