A plated steel includes: a steel; and a plating layer that is provided on a surface of the steel, in which the plating layer includes, by mass %, Al: 5.00% to 35.00%, Mg: 2.50% to 13.00%, Fe: 5.00% to 40.00%, Si: 0% to 2.00%, Ca: 0% to 2.00%, and a remainder of Zn and impurities, and in a cross section of the plating layer, the area fraction of a Zn solid-solution Fe.sub.2Al.sub.5 phase in which 5% or more of Zn is solid-soluted is 10% to 60% and the area fraction of a MgZn.sub.2 phase is 10% to 90%.

A plated steel includes: a steel; and a plating layer that is provided on a surface of the steel, in which the plating layer includes, by mass %, Al: 5.00% to 35.00%, Mg: 2.50% to 13.00%, Fe: 5.00% to 40.00%, Si: 0% to 2.00%, Ca: 0% to 2.00%, and a remainder of Zn and impurities, and in a cross section of the plating layer, the area fraction of a Zn solid-solution Fe.sub.2Al.sub.5 phase in which 5% or more of Zn is solid-soluted is 10% to 60% and the area fraction of a MgZn.sub.2 phase is 10% to 90%.

A method of pretinning a guidewire core made of shape memory alloy and having an elongate axis, comprising: placing a ball of solder in a pocket in a soldering block; melting the ball of solder; holding a guidewire core over the ball of solder; lowering the guidewire core into the ball of solder; removing the guidewire from the ball of solder.

A method of pretinning a guidewire core made of shape memory alloy and having an elongate axis, comprising: placing a ball of solder in a pocket in a soldering block; melting the ball of solder; holding a guidewire core over the ball of solder; lowering the guidewire core into the ball of solder; removing the guidewire from the ball of solder.

A flat steel product for hot forming may be produced from a steel substrate that includes a steel comprising 0.1-3% by weight Mn and up to 0.01% by weight B, along with a protective coating that is applied to the steel substrate. The protective coating may be based on Al and may contain up to 20% by weight of other alloy elements. Also disclosed are methods for producing such flat steel products, steel components, and methods for producing steel components. Absorption of hydrogen is minimized during heating necessary for hot forming. This is achieved at least in part through an alloy constituent of 0.1-0.5% by weight of at least one alkaline earth or transition metal in the protective coating, wherein an oxide of the alkaline earth or transition metal is formed on an outer surface of the protective coating during hot forming of the flat steel product.

A flat steel product for hot forming may be produced from a steel substrate that includes a steel comprising 0.1-3% by weight Mn and up to 0.01% by weight B, along with a protective coating that is applied to the steel substrate. The protective coating may be based on Al and may contain up to 20% by weight of other alloy elements. Also disclosed are methods for producing such flat steel products, steel components, and methods for producing steel components. Absorption of hydrogen is minimized during heating necessary for hot forming. This is achieved at least in part through an alloy constituent of 0.1-0.5% by weight of at least one alkaline earth or transition metal in the protective coating, wherein an oxide of the alkaline earth or transition metal is formed on an outer surface of the protective coating during hot forming of the flat steel product.

Provided is a method for preparing a metal oxide or a metal hydroxide nano thin-film material by a molten salt method, which mainly comprises the following steps: heating a low-melting-point salt to a molten state, adding a substrate into the molten salt before or after melting for reaction; adding a metal source and continuing the reaction for a period of time; removing the substrate, cooling the substrate to a room temperature, cleaning and drying the substrate to obtain the metal oxide or metal hydroxide nano thin-film material; wherein, the mass ratio of the low-melting-point salt to the metal source is 100-1.5:1. The metal oxide and metal hydroxide nano-film materials with various nano-morphologies prepared by the method of the present application have morphologies that can be regulated and controlled by the types and proportions of the low-melting-point salts and metal sources.

Provided is a method for preparing a metal oxide or a metal hydroxide nano thin-film material by a molten salt method, which mainly comprises the following steps: heating a low-melting-point salt to a molten state, adding a substrate into the molten salt before or after melting for reaction; adding a metal source and continuing the reaction for a period of time; removing the substrate, cooling the substrate to a room temperature, cleaning and drying the substrate to obtain the metal oxide or metal hydroxide nano thin-film material; wherein, the mass ratio of the low-melting-point salt to the metal source is 100-1.5:1. The metal oxide and metal hydroxide nano-film materials with various nano-morphologies prepared by the method of the present application have morphologies that can be regulated and controlled by the types and proportions of the low-melting-point salts and metal sources.

A coated stainless-steel substrate including a coating including nanographites and a binder being sodium silicate, wherein the stainless-steel substrate has the following composition in weight percent: C≤1.2%, Cr≥11.0%, Ni≥8.0% and on a purely optional basis, one or more elements such as Nb≤6.0%, B≤1.0%, Ti≤3.0%, Cu≤5.0%, Co≤3.0%, N≤1.0%, V≤3.0%, Si≤4.0%, Mn≤5.0%, P≤0.5%, S≤0.5%, Mo≤6.0%, Ce≤1.0%, the remainder of the composition being made of iron and inevitable impurities resulting from the elaboration. A method for the manufacture of this coated stainless-steel substrate is also provided.

A coated stainless-steel substrate including a coating including nanographites and a binder being sodium silicate, wherein the stainless-steel substrate has the following composition in weight percent: C≤1.2%, Cr≥11.0%, Ni≥8.0% and on a purely optional basis, one or more elements such as Nb≤6.0%, B≤1.0%, Ti≤3.0%, Cu≤5.0%, Co≤3.0%, N≤1.0%, V≤3.0%, Si≤4.0%, Mn≤5.0%, P≤0.5%, S≤0.5%, Mo≤6.0%, Ce≤1.0%, the remainder of the composition being made of iron and inevitable impurities resulting from the elaboration. A method for the manufacture of this coated stainless-steel substrate is also provided.