Provided are a hot-dip zinc plated steel material and a method for preparing same, the hot-dip zinc plated steel material comprising: base iron comprising 0.01-1.6 wt % of Si and 1.2-3.1 wt % of Mn; a Zn—Al—Mg alloy plating layer; and an Al-rich layer formed on the interface of the base iron and Zn—Al—Mg alloy plating layer, wherein the rate of occupied surface area of the Al-rich layer is 70% or higher (including 100%).

Provided are a hot-dip zinc plated steel material and a method for preparing same, the hot-dip zinc plated steel material comprising: base iron comprising 0.01-1.6 wt % of Si and 1.2-3.1 wt % of Mn; a Zn—Al—Mg alloy plating layer; and an Al-rich layer formed on the interface of the base iron and Zn—Al—Mg alloy plating layer, wherein the rate of occupied surface area of the Al-rich layer is 70% or higher (including 100%).

Provided is a plated steel sheet applicable for various purposes as in construction materials, household electric appliances, automobiles, etc. and, more particularly, to a hot dip plated steel sheet having excellent corrosion resistance and workability and a manufacturing method therefor.

Provided is a plated steel sheet applicable for various purposes as in construction materials, household electric appliances, automobiles, etc. and, more particularly, to a hot dip plated steel sheet having excellent corrosion resistance and workability and a manufacturing method therefor.

An aluminum-based plated steel sheet according to an aspect of the present invention includes: a base material; an aluminum-based plating layer located above the base material; and an intermetallic compound layer that is located between the base material and the aluminum-based plating layer and contains an intermetallic compound of Al and Fe, in which the base material has a chemical component within a predetermined range, the aluminum-based plating layer contains, on average, 80 mass % or more and 97 mass % or less of Al, 3 mass % or more and 15 mass % or less of Si, 0 mass % or more and 5 mass % or less of Zn, 0 mass % or more and 5 mass % or less of Fe, 0 mass % or more and 3 mass % or less in total of one or more selected from the group consisting of Mg and Ca, and impurities so that a total amount thereof is 100 mass %, an average value of a thickness of the intermetallic compound layer is 2 μm or more and 10 μm or less, a maximum value of the thickness of the intermetallic compound layer is 10 μm or more and 25 μm or less, and a standard deviation of the thickness of the intermetallic compound layer is 2 μm or more and 10 μm or less.

To solve a problem about warpage of a steel sheet due to a difference in temperature raising rate between an overlapped part and a one-sheet part. This manufacturing method includes: a step of heating an overlapped blank; a step of transferring the heated overlapped blank; and a step of performing presswork on the heated overlapped blank by using a die, in which in the heating step, when sheet thicknesses of the first and second steel sheets are set to t1 and t2, respectively, and an average heating rate at a sheet temperature from 20 to 800° C. of a portion with a total sheet thickness (t1+t2) of an overlapped portion, and that of a non-overlapped portion are set to V and v1, respectively, the total sheet thickness (t1+t2) is 2.5 to 5.0 mm, a maximum length L of the overlapped portion is 100 to 1100 mm, an area S1 of the first steel sheet, an area S2 of a portion, of the second steel sheet, which is overlapped with the first steel sheet, and the average heating rates V and v1 satisfy Expressions (1) to (3), and the heating is performed at a heating temperature and for a heating time within a specific range on a plane of coordinates defined by the heating time and the heating temperature.

A cold-rolled and heat-treated steel sheet having a microstructure consisting of, in surface fraction: between 10% and 30% of retained austenite, the retained austenite being present as films having an aspect ratio of at least 3 and as Martensite Austenite islands, less than 8% of the Martensite Austenite islands having a size above 0.5 μm, at most 1% of fresh martensite, at most 50% of tempered martensite, and recovered martensite containing precipitates of at least one element chosen among niobium, titanium and vanadium. A method for manufacturing the cold-rolled and heat-treated steel sheet is also described.

A cold-rolled and heat-treated steel sheet having a microstructure consisting of, in surface fraction: between 10% and 30% of retained austenite, the retained austenite being present as films having an aspect ratio of at least 3 and as Martensite Austenite islands, less than 8% of the Martensite Austenite islands having a size above 0.5 μm, at most 1% of fresh martensite, at most 50% of tempered martensite, and recovered martensite containing precipitates of at least one element chosen among niobium, titanium and vanadium. A method for manufacturing the cold-rolled and heat-treated steel sheet is also described.

Fe-Al-based plated hot-stamped member exhibiting excellent formed part corrosion resistance and post-coating corrosion resistance and manufacturing method. The hot-stamping member includes Fe-Al-based plated layer on one or both surfaces of a base material, the base material has a predetermined steel component, Fe-Al-based plated layer has a thickness of 10 μm or more and 60 μm or less, formed by A, B, C and D layers sequentially from a surface toward the base material, and each of the four layers is a Fe-Al-based intermetallic compound containing Al, Fe, Si, Mn and Cr for predetermined contents with the balance made up of impurities, the D layer further contains Kirkendall voids each of which cross-sectional area is 3 μm.sup.2-30 μm.sup.2 for 10 pieces/6000 μm.sup.2 or more and 40 pieces/6000 μm.sup.2 or less.

Provided is a highly corrosion-resistant plated steel sheet having plating adhesion and resistance to liquid metal embrittlement. A highly corrosion-resistant plated steel sheet comprises a base steel sheet and a plated layer, which sequentially comprises an Fe—Al alloy layer and an MgZn.sub.2 layer from an interface with the base steel sheet.