Provided is a method for preparing a metal oxide or a metal hydroxide nano thin-film material by a molten salt method, which mainly comprises the following steps: heating a low-melting-point salt to a molten state, adding a substrate into the molten salt before or after melting for reaction; adding a metal source and continuing the reaction for a period of time; removing the substrate, cooling the substrate to a room temperature, cleaning and drying the substrate to obtain the metal oxide or metal hydroxide nano thin-film material; wherein, the mass ratio of the low-melting-point salt to the metal source is 100-1.5:1. The metal oxide and metal hydroxide nano-film materials with various nano-morphologies prepared by the method of the present application have morphologies that can be regulated and controlled by the types and proportions of the low-melting-point salts and metal sources.

The present invention relates to a method for producing a substrate (2) which is coated with an alkali metal (1), in which method a promoter layer (3) which is composed of a material which reacts with the alkali metal (1) by at least partial chemical reduction of the promoter layer (3) is applied to a surface of the substrate (2) and a surface of the promoter layer (3) is acted on by an alkali metal (1) and then the alkali metal (1) is converted into the solid phase and a coating containing the alkali metal is formed.

Disclosed is a method for surface-modifying titanium alloy, comprising the following steps: carburizing titanium alloy in solid carburizing agent A and solid carburizing agent B, and then performing gas co-infiltration to realize surface modification treatment of titanium alloy; the solid carburizing agent A includes raw materials of charcoal powder a, barium carbonate, calcium carbonate, barium acetate, urea and cerium carbonate, and the solid carburizing agent B includes raw materials of charcoal powder b, barium carbonate, calcium carbonate and cerium carbonate; and the gases used in the gas co-infiltration are ammonia, air and acetylene.

The present disclosure appropriately shortens a processing step for processing a substrate in which a silicon layer and a silicon germanium layer are alternatively laminated. The present disclosure provides a substrate processing method of processing the substrate in which the silicon layer and the silicon germanium layer are alternatively laminated, which includes forming an oxide film by selectively modifying a surface layer of an exposed surface of the silicon germanium layer by using a processing gas including fluorine and oxygen and converted into plasma.

Provided is a sliding component having a low coefficient of friction and capable of exerting stable sliding characteristics from the initial stage of sliding, and a manufacturing method capable of easily manufacturing the sliding component. A sliding component (1) includes an iron substrate (10), in which graphite particles (13) are dispersed in an iron base (11), and a tin coating (20) formed on the iron substrate (10), the tin coating (20) including tin as a main material. The graphite particles (13) of the sliding component (1) are exposed through the tin coating (20). The manufacturing method includes: a preparation step of preparing an iron substrate (10) including graphite particles (13) dispersed in an iron base (11); and a film forming step of forming a tin coating (20) on the surface of the iron substrate (10), the tin coating (20) including tin as a main material. The film forming step forms the tin coating (20) so that the graphite particles (13) are exposed through the tin coating (20).

press hardening method includes the following steps: A. the provision of a steel sheet for heat-treatment, precoated with a zinc- or aluminum-based pre-coating, B. the deposition of a hydrogen barrier pre-coating over a thickness from 10 to 550 nm, and comprising at least one element chosen from among: nickel, chromium, magnesium, aluminum and yttrium, C. batch annealing of the precoated steel sheet to obtain a pre-alloyed steel sheet, the cooling after the batch annealing being performed at a speed of 29.0° C.h.sup.−1 or less, D. the cutting of the pre-alloyed steel sheet to obtain blank, E. thermal treatment of the blank to obtain a fully austenitic microstructure in the steel, F. the transfer of the blank into a press tool, G. the hot-forming of the blank to obtain a part, H. the cooling of the part obtained at step G).

A ferritic stainless steel sheet includes a base metal and a nitrided layer that is formed on a surface of the base metal, a chemical composition of the base metal contains, in mass %, C: 0.001 to 0.020%, Si: 0.01 to 1.50%, Mn: 0.01 to 1.50%, P: 0.010 to 0.050%, S: 0.0001 to 0.010%, Cr: 16.0 to 25.0%, N: 0.001 to 0.030%, Ti: 0.01 to 0.30%, and optional elements, with the balance: Fe and unavoidable impurities, a steel microstructure of the base metal includes, in volume ratio, 95% or more of a ferritic phase, the nitrided layer is a layer that is present in a region from a surface of a rolled surface to a 0.05 μm depth position in a sheet thickness direction, and an average nitrogen concentration in the nitrided layer is, in mass %, 0.80% or more.

The present invention provides a method of heat treating a steel component including the sequential steps of: (a) carbonitriding the steel component; (b) quenching the steel component; (c) optionally tempering the steel component; and (d) ferritically nitrocarburizing the steel component.

The present invention provides a method of heat treating a steel component including the sequential steps of: (a) carbonitriding the steel component; (b) quenching the steel component; (c) optionally tempering the steel component; and (d) ferritically nitrocarburizing the steel component.

Methods of fabricating objects using additive manufacturing are provided. The methods create in situ dispersoids within the object. The methods are used with refractory alloy powders which are pretreated to increase the oxygen content to between 500 ppm and 3000 ppm or to increase the nitrogen content to between 250 ppm and 1500 ppm. The pretreated powders are then formed into layers in an environmentally controlled chamber of an additive manufacturing machine. The environmentally controlled chamber is adjusted to have between 500 ppm and 200 ppm oxygen. The layer of pretreated powder is then exposed to a transient moving energy source for melting and solidifying the layer; and creating in situ dispersoids in the layer.