A process includes converting hydrocarbons to at least one molecular energy carrier and carbon dioxide, reacting said carbon dioxide with a divalent metal-containing silicate to form solid divalent metal carbonate and silicate and utilizing at least one of said carbonate and silicate in the production of construction and/or chemical material.

A process includes converting hydrocarbons to at least one molecular energy carrier and carbon dioxide, reacting said carbon dioxide with a divalent metal-containing silicate to form solid divalent metal carbonate and silicate and utilizing at least one of said carbonate and silicate in the production of construction and/or chemical material.

Garnet silicate is garnet silicate containing, as a main component, silicate represented by a general formula: Lu.sub.2CaMg.sub.2(SiO.sub.4).sub.3. The garnet silicate includes primary particles having a particle shape derived from a crystal structure of garnet. Moreover, the garnet silicate further contains alkaline metal including at least lithium, in which a content of the alkaline metal is less than 2000 ppm. The garnet silicate phosphor includes garnet silicate and ions which are included in the garnet silicate and function as a light emission center. The wavelength converter includes the garnet silicate phosphor. A light emitting device includes the garnet silicate phosphor or the wavelength converter.

Garnet silicate is garnet silicate containing, as a main component, silicate represented by a general formula: Lu.sub.2CaMg.sub.2(SiO.sub.4).sub.3. The garnet silicate includes primary particles having a particle shape derived from a crystal structure of garnet. Moreover, the garnet silicate further contains alkaline metal including at least lithium, in which a content of the alkaline metal is less than 2000 ppm. The garnet silicate phosphor includes garnet silicate and ions which are included in the garnet silicate and function as a light emission center. The wavelength converter includes the garnet silicate phosphor. A light emitting device includes the garnet silicate phosphor or the wavelength converter.

A method for producing forsterite microparticles having a primary particle size of 1, to 50 nm, as determined through electron microscopy. The method includes spray-drying, in an atmosphere of 50° C. or higher and lower than 300° C., a solution containing a water-soluble magnesium salt and colloidal silica at a mole ratio of magnesium atoms to silicon atoms (Mg/Si) of 2; and subsequently, firing the spray-dried product in air at 800 to 1,000° C.

Calcium silicate powders are provided. The calcium silicate powders comprise porous calcium silicate particles and an additive, the additive being at least partially penetrated into the pores of the particles. The additive is present in an amount of between 1.5 and 50%w, wherein %w is the weight ratio, expressed as percentage, of the dry weight of the additive over the dry weight of the combination of the calcium silicate particles and additive.

Provided is a method of preparing a metal oxide-silica composite aerogel and a metal oxide-silica composite aerogel having an excellent weight reduction property prepared by the method. The method comprises adding an acid catalyst to a first water glass solution to prepare an acidic water glass solution (step 1); adding a metal ion solution to the acidic water glass solution to prepare a precursor solution (step 2); and adding a second water glass solution to the precursor solution and performing a gelation reaction (step 3).

Provided is a method of preparing a metal oxide-silica composite aerogel and a metal oxide-silica composite aerogel having an excellent weight reduction property prepared by the method. The method comprises adding an acid catalyst to a first water glass solution to prepare an acidic water glass solution (step 1); adding a metal ion solution to the acidic water glass solution to prepare a precursor solution (step 2); and adding a second water glass solution to the precursor solution and performing a gelation reaction (step 3).

The present invention relates to inorganic fibres having a composition comprising: 61.0 to 70.8 wt% SiO.sub.2; 28.0 to 39.0 wt% CaO; 0.10 to 0.85 wt% MgO other components, if any, providing the balance up to 100 wt %,

The sum of SiO.sub.2 and CaO is greater than or equal to 98.8 wt % and the other components comprise less than 0.70 wt % Al.sub.2O.sub.3, if any.

The present invention relates to inorganic fibres having a composition comprising: 61.0 to 70.8 wt% SiO.sub.2; 28.0 to 39.0 wt% CaO; 0.10 to 0.85 wt% MgO other components, if any, providing the balance up to 100 wt %,

The sum of SiO.sub.2 and CaO is greater than or equal to 98.8 wt % and the other components comprise less than 0.70 wt % Al.sub.2O.sub.3, if any.