A separation method includes a separation step of using a zeolite membrane composite to separate a branched diolefin from a branched hydrocarbon mixture containing the branched diolefin and at least one branched hydrocarbon in which the number of carbon-carbon double bonds is 1 or less and that is of an equivalent carbon number n to the branched diolefin. The zeolite membrane composite used in this step is a zeolite membrane composite that includes a porous support and a FAU-type zeolite membrane formed on at least one surface of the porous support, and in which the FAU-type zeolite membrane is a silylated FAU-type zeolite membrane including a silyl group at the surface thereof.

The present application relates to a method for synthesizing nanozeolite Y crystals, nanozeolite Y crystals obtainable by said method, and the use of the synthesized nanozeolite Y crystals in cracking hydrocarbons, as molecular sieves or as ion-exchangers.

Improved alkylation catalysts, alkylation methods, and methods of making alkylation catalysts are described. The alkylation method comprises reaction over a solid acid, zeolite-based catalyst and can be conducted for relatively long periods at steady state conditions. The alkylation catalyst comprises a crystalline zeolite structure, a Si/Al molar ratio of 20 or less, less than 0.5 weight percent alkali metals, and further having a characteristic catalyst life property. Some catalysts may contain rare earth elements in the range of 10 to 35 wt %. One method of making a catalyst includes a calcination step following exchange of the rare earth element(s) conducted at a temperature of at least 575° C. to stabilize the resulting structure followed by an deammoniation treatment. An improved method of deammoniation uses low temperature oxidation.

Improved alkylation catalysts, alkylation methods, and methods of making alkylation catalysts are described. The alkylation method comprises reaction over a solid acid, zeolite-based catalyst and can be conducted for relatively long periods at steady state conditions. The alkylation catalyst comprises a crystalline zeolite structure, a Si/Al molar ratio of 20 or less, less than 0.5 weight percent alkali metals, and further having a characteristic catalyst life property. Some catalysts may contain rare earth elements in the range of 10 to 35 wt %. One method of making a catalyst includes a calcination step following exchange of the rare earth element(s) conducted at a temperature of at least 575° C. to stabilize the resulting structure followed by an deammoniation treatment. An improved method of deammoniation uses low temperature oxidation.

A method for synthesizing a supported molecular sieve membrane by microwaves includes the steps of aging, heating and synthesizing. The aging step is to make a support in contact with a synthetic liquid at 25° C. to 70° C. for 10 hours to 24 hours; the heating step is to raise a temperature of an aged system from an aging temperature to a synthesis temperature within 1 minute to 10 minutes; and the synthesizing step is to synthesize at 80° C. to 120° C. for 2 minutes to 15 minutes. The steps of heating and synthesizing are powered by microwaves.

A method for synthesizing a supported molecular sieve membrane by microwaves includes the steps of aging, heating and synthesizing. The aging step is to make a support in contact with a synthetic liquid at 25° C. to 70° C. for 10 hours to 24 hours; the heating step is to raise a temperature of an aged system from an aging temperature to a synthesis temperature within 1 minute to 10 minutes; and the synthesizing step is to synthesize at 80° C. to 120° C. for 2 minutes to 15 minutes. The steps of heating and synthesizing are powered by microwaves.

The present application relates to a method for synthesizing nanozeolite Y crystals, nanozeolite Y crystals obtainable by said method, and the use of the synthesized nanozeolite Y crystals in cracking hydrocarbons, as molecular sieves or as ion-exchangers.

A small crystal size, high surface area aluminogermanosilicate molecular sieve material, designated SSZ-120, is provided. SSZ-120 can be synthesized using 3,3′-[2,6-naphthalenebis(methylene)]bis[1,2-dimethyl-1H-imidazolium] dications as a structure directing agent. SSZ-120 may be used in organic compound conversion reactions and/or sorptive processes.

A small crystal size, high surface area aluminogermanosilicate molecular sieve material, designated SSZ-120, is provided. SSZ-120 can be synthesized using 3,3′-[2,6-naphthalenebis(methylene)]bis[1,2-dimethyl-1H-imidazolium] dications as a structure directing agent. SSZ-120 may be used in organic compound conversion reactions and/or sorptive processes.

A separation method includes a separation step of using a zeolite membrane composite to separate a branched diolefin from a branched hydrocarbon mixture containing the branched diolefin and at least one branched hydrocarbon in which the number of carbon-carbon double bonds is 1 or less and that is of an equivalent carbon number n to the branched diolefin. The zeolite membrane composite used in this step is a zeolite membrane composite that includes a porous support and a FAU-type zeolite membrane formed on at least one surface of the porous support, and in which the FAU-type zeolite membrane is a silylated FAU-type zeolite membrane including a silyl group at the surface thereof.