Coated glass panes having a glass pane and a coating in at least one region of at least one side of the glass pane. The glass pane is composed of glass with SiO.sub.2 and B.sub.2O.sub.3. The coating includes first coating applied in at least one region of the at least one side. The first coating has a binder with SiO.sub.2 and a pigment. The glass pane, in the at least one region, has a flexural strength between at least 5 and at most 170 MPa.

A process for obtaining a material including a textured glass substrate coated, on at least one of its textured faces, with an antireflective coating of sol-gel type based on porous silica, includes a stage of application, to the at least one textured face of the substrate, of a solution containing at least one silica precursor and at least one pore-forming agent, then a heat treatment stage targeted at consolidating the antireflective coating. Before the application stage, the glass substrate is subjected to a preheating stage, so that the at least one textured face intended to be coated with the antireflective coating has a temperature within a range extending from 30° C. to 100° C. immediately before the application stage.

The invention provides a method of processing glass that involves forming a flexible gel layer on a flexible glass sheet to create a glass-gel sheet; rolling-up the glass-gel sheet into the form of a roll; placing the roll in a dryer; and drying the flexible gel layer so as to form a flexible aerogel layer. Some embodiments provide a glazing unit that includes a glass-aerogel sheet located between first and second panes of the glazing unit, where the glass-aerogel sheet includes a flexible glass sheet and a flexible aerogel layer on the flexible glass sheet. In such embodiments, the first and second panes each have thicknesses that are greater than a thickness of the flexible glass sheet. Other embodiments provide a glass assembly having a flexible aerogel layer on a flexible glass sheet, with the flexible glass sheet being laminated to a glass pane.

A system and method of production of matt effect or matt glass that eliminates the double-sided printing process in the production process of glasses used in products such as ovens, refrigerators, bottle cabinets, combi boilers, built-in appliances, fume hoods, stove glass, etc., prevents fingerprints on glass and increases the scratch resistance.

The vehicle rear information acquisition system of the disclosure includes: a back window at a rear of a vehicle; and an information acquisition device disposed inside the vehicle, opposing the back window, and configured to apply and/or receive light to acquire information from outside the vehicle, the back window including a glass plate and a coating film on at least a part of a surface of the glass plate, and having a privacy region for protecting privacy inside the vehicle and an information acquisition region opposing the information acquisition device and transmitting the light, the privacy region having the coating film on the surface of the glass plate, the privacy region having a visible light transmittance of 10% or less, the information acquisition region having a visible light transmittance of 25% or more.

A greenhouse according to the present invention includes: a ceiling portion; and in at least a portion of the ceiling portion, a glass sheet with a coating film. The glass sheet with a coating film has a total light transmittance of 90% to 98%, a haze ratio of 20% to 80%, and a hemispherical transmittance of 80% to 90%. When a test is performed according to JIS R 1703-1: 2007 by applying oleic acid to a surface of a coating film and subsequently irradiating the surface with ultraviolet light at an intensity of 1.0 mW/cm.sup.2, a time period from start of irradiation with the ultraviolet light to a point at which a water contact angle on the surface reaches 5° is 24 hours or less.

A glass substrate with a silica film according to the present invention includes a glass substrate and a silica film formed using a silica film-forming composition, in which the composition includes at least one kind selected from the group consisting of a hydrolyzable compound, a hydrolyzate thereof, and a hydrolysis condensation compound thereof, and at least one kind selected from the group consisting of a silica particle and a zirconia particle, the hydrolyzable compound consisting of a tetraalkoxysilane, a compound (compound I) represented by formula I: (R.sub.3-p(L).sub.pSi-Q-Si(L).sub.pR.sub.3-p), optionally a fluoroalkylsilane having a hydrolysable group, and optionally a zirconium compound having a hydrolyzable group, and the contents of the tetraalkoxysilane, the compound I, and the at least one kind selected from the group consisting of a silica particle and a zirconia particle in terms of SiO.sub.2/ZrO.sub.2 fall within specified ranges, respectively.

A surface finishing method, an anti-glare coating, and a display device having same are provided. The surface finishing method includes adding diffusion particles which have a density less than that of a resin material, and controlling the thickness of the resin material in an anti-glare material coated on a surface of a substrate to be greater than the particle size of the diffusion particles, so that the diffusion particles are evenly dispersed in the resin layer, and a part of the volume of the diffusion particles are exposed on a surface of the resin layer. Thus, the uniformity of the surface haze of the anti-glare coating can be enhanced, and flashing points of the display device can be avoided.

A process for forming a fingerprint-resistant coating on a substrate comprising activating the substrate by exposure to a plasma, and then depositing on the activated substrate at least one alkyl backbone monolayer, and hydroxyl-polyhedral oligomeric silsesquioxane (OH-POSS) nanoparticles.

Provided are methods of forming stacks comprising a substrate and one or more sol-gel layers disposed on the substrate. Also provided are stacks formed by these methods. The sol-gel layers in these stacks, especially outer layers, may have a porosity of less than 1% or even less than 0.5%. In some embodiments, these layers may have a surface roughness (R.sub.a) of less than 1 nanometers. The sol-gel layers may be formed using radiative curing and/or thermal curing at temperatures of between 400° C. and 700° C. or higher. These temperatures allow application of sol-gel layers on new types of substrates. A sol-gel solution, used to form these layers, may have colloidal nanoparticles with a size of less than 20 Angstroms on average. This small size and narrow size distribution is believed to control the porosity of the resulting sol-gel layers.