A coated article is described herein that may comprise a substrate and an optical coating. The substrate may have a major surface comprising a first portion and a second portion. A first direction that is normal to the first portion of the major surface may not be equal to a second direction that is normal to the second portion of the major surface. The optical coating may be disposed on at least the first portion and the second portion of the major surface. The coated article may exhibit at the first portion of the substrate and at the second portion of the substrate hardness of about 8 GPa or greater at an indentation depth of about 50 nm or greater as measured on the anti-reflective surface by a Berkovich Indenter Hardness Test.

Strengthened glass substrates with glass fits and methods for forming the same are disclosed. According to one embodiment, the present invention provides a glass frit with a coefficient of thermal expansion less than or equal to the coefficient of thermal expansion of the glass substrate where it is going to be painted. The glass frit of the present invention has similar ion exchange properties to the glass substrate that is going to be used to paint with the glass frit allowing the glass substrate to be ion-exchanged. The glass frit of the present invention is mixed with an organic carrier.

A method of etching a substrate comprises: contacting a substrate having a thickness with an etchant disposed in a vessel for a period of time until the thickness has reduced by at least 2 μm and at an average rate of 1 μm per minute to 6.7 μm per minute, the etchant having a temperature of 170° C. to 300° C. and comprising a molten mixture of two or more alkali hydroxides; and ceasing contacting the substrate with the etchant. The etchant in some instances comprises a molten mixture of NaOH and KOH. For example, the etchant in some instances includes a molten mixture of 24 wt. % to 72 wt. % NaOH, and 76 wt. % to 28 wt. % KOH. In some instances, the method alters the weight percentage of Na.sup.+, K.sup.+ and Li.sup.+ in the composition of the surface of the substrate by less than 1%.

The purpose of the present invention is to provide a chemically-strengthened glass exhibiting both surface strength and abrasion-resistant anti-fingerprint (AFP) properties. The present invention relates to a plate-shaped chemically-strengthened glass which has a compressive stress layer provided to a glass surface layer, a glass surface hydrogen concentration profile in a specific range, and a surface strength and abrasion-resistant anti-fingerprint (AFP) properties which are in specific ranges.

To provide a crystallized glass substrate including a surface with a compressive stress layer, in which a stress depth DOL.sub.zero of the compressive stress layer, at which the compressive stress is 0 MPa, is 45 to 200 μm, a compressive stress CS on an outermost surface of the compressive stress layer is 400 to 1400 MPa, and CS×DOL.sub.zero, which is a product of the compressive stress CS on the outermost surface and the stress depth DOL.sub.zero (μm), is 4.8×10.sup.4 or more.

A display device includes a display module having a folding area and a non-folding area adjacent to the folding area. A glass substrate is disposed on the display module and comprises a first layer and a second layer disposed on the first layer. The second layer has a compressive strength that is higher than a compressive strength of the first layer. The first layer and the second layer of the glass substrate each include a folding portion overlapping the folding area and having a first thickness and a non-folding portion overlapping the non-folding area and having a second thickness greater than the first thickness. The second layer of the non-folding portion has a thickness that is greater than a thickness of the second layer of the folding portion.

The present invention relates to a chemically strengthened glass ceramic including a crystalline phase, having two main surfaces opposed to each other, and including an amorphized region in a surface layer of at least one of the main surfaces and a crystallized region inside the glass, in which the amorphized region has a crystallinity of 10 vol % or less at a depth of 100 nm from an outermost surface of the glass.

A colored glass article includes greater than or equal to 50 mol % and less than or equal to 80 mol % SiO.sub.2; greater than or equal to 7 mol % and less than or equal to 25 mol % Al.sub.2O.sub.3; greater than or equal to 1 mol % and less than or equal to 15 mol % B.sub.2O.sub.3; greater than or equal to 5 mol % and less than or equal to 20 mol % Li.sub.2O; greater than or equal to 0.5 mol % and less than or equal to 15 mol % Na.sub.2O; greater than 0 mol % and less than or equal to 1 mol % K.sub.2O; and greater than or equal to 1×10.sup.−6 mol % and less than or equal to 1 mol % Au. R.sub.2O—Al.sub.2O.sub.3 is greater than or equal to −5 mol % and less than or equal to 7 mol %, R.sub.2O being the sum of Li.sub.2O, Na.sub.2O, and K.sub.2O.

A chemically toughenable or toughened sheet-like glass article is provided. The article has a glass with a composition comprising Al.sub.2O.sub.3, SiO.sub.2, Li.sub.2O, and Na.sub.2O, wherein (Al.sub.2O.sub.3)−(Li.sub.2O+Na.sub.2O), in mol %, is less than 0; a thickness between 0.3 mm and 4 mm; a light transmittance of at least 0.001% to at most 60% at 450 nm, of at least 0.001% to at most 30% at 540 nm, and of at least 0.001% to at most 30% at 630 nm; and an IR transmittance of at least 10% to not more than 99% at any wavelength in a wavelength range from 900 nm to 1100 nm. The light and IR transmittances are determined for a thickness of the article of 1 mm.

A windshield according to the present invention includes an outer glass plate, an inner glass plate that faces the outer glass plate, and an intermediate film disposed between the outer glass plate and the inner glass plate, and in at least a partial region of the outer glass plate and the inner glass plate, compressive principal stress on a surface on a vehicle exterior side of the outer glass plate is larger than compressive principal stress on a surface on a vehicle interior side of the inner glass plate.