Embodiments of the invention are amendments to hot-mix asphalt (“HMA”) which open new price/performance areas to asphalt cement concrete (“ACC”) pavement. Equivalent-performing pavement may be made at lower cost, or higher-performing pavement may be made at equivalent-to-prior-art cost. The amendments, recycled asphalt pavement (“RAP”, and including recycled asphalt shingles [“RAS”]), and reinforcing fiber (aramid fiber) may be adjusted as described herein to achieve a desired price/performance target.

The invention relates to processes for making improved ultra-high performance concrete with plasma-treated inclusions and articles made from the same. The invention includes a process for producing silicon carbide and multiwalled carbon nanotubes by heating agricultural waste husks in an inert atmosphere to a temperature higher than 1300 degrees C. to obtain a mixture containing silicon carbide and MWCNTs, and treating the mixture to extract the silicon carbide and MWCNTs for use as microinclusions in ultra high performance concrete.

An anti-blast concrete and a method of fabricating an anti-blast structure member using such anti-blast concrete are disclosed. The composition of the anti-blast concrete according to the invention includes, in parts by weight, 1.0 part by weight of cement, 1.0 to 2.5 parts by weight of fine aggregates, 1.0 to 2.5 parts by weight of coarse aggregates, and a plurality of reinforcing fibers. The weight ratio of the reinforcing fibers to the cement ranges from 0.5% to 3%. The plurality of reinforcing fibers are a plurality of carbon fibers or a plurality of aramid fibers. A test body, made of the anti-blast concrete of the invention, has an average number of times of repeated impacts at an impact energy of 49.0 Joules equal to or larger than 41 times at 28 days of age.

A precast concrete beam A beam for use in construction of a long span bridge structure comprising: a reinforcing member having a geometric configuration selected from a group consisting of: a “U” tub beam with composite deck system; a decked I-beam; and an adjacent box beam; said geometric configuration formed of a UHPC mix having: an initial compressive strength, f′.sub.ci=10.0 ksi; a compressive strength at service, f′.sub.c=17.4 ksi; a modulus of elasticity of concrete, E.sub.c=6500 ksi; a residual rupture stress, f.sub.rr=0.75 ksi; and a concrete unit weight, w.sub.c=0.155 kcf; and
said UHPC mix further comprises a plurality of discontinuous fibers distributed randomly throughout a concrete matrix, said plurality of discontinuous fibers formed of a material selected from the group consisting of: steel; polypropylene; nylon; polyvinyl alcohol; polyolefin; polyethylene; polyester; acrylic; aramid; carbon; silica glass; basalt glass; glass fiber-reinforced polymer; and basalt fiber-reinforced polymer.

A precast concrete beam A beam for use in construction of a long span bridge structure comprising: a reinforcing member having a geometric configuration selected from a group consisting of: a “U” tub beam with composite deck system; a decked I-beam; and an adjacent box beam; said geometric configuration formed of a UHPC mix having: an initial compressive strength, f′.sub.ci=10.0 ksi; a compressive strength at service, f′.sub.c=17.4 ksi; a modulus of elasticity of concrete, E.sub.c=6500 ksi; a residual rupture stress, f.sub.rr=0.75 ksi; and a concrete unit weight, w.sub.c=0.155 kcf; and
said UHPC mix further comprises a plurality of discontinuous fibers distributed randomly throughout a concrete matrix, said plurality of discontinuous fibers formed of a material selected from the group consisting of: steel; polypropylene; nylon; polyvinyl alcohol; polyolefin; polyethylene; polyester; acrylic; aramid; carbon; silica glass; basalt glass; glass fiber-reinforced polymer; and basalt fiber-reinforced polymer.

Reinforcing filaments or fibers, such as aromatic polyamide (aramid) fibers, can be reliably measured and consistently mixed into asphalt cement concrete by soaking the fibers in a wetting agent, then severing them to a desired length, and mixing the segments with other ACC ingredients. The wetting agent holds the fibers together loosely, so they can be distributed more uniformly throughout the ACC without clumping. The wetting agent soaks into the ACC mixture and/or evaporates, leaving the reinforcing fibers behind.

A structure for protecting a substrate. The structure comprises an inner tie coat layer which can bond to the substrate, a geopolymer foam layer, and an outer protective layer. The geopolymer foam layer is the reaction product of a mixture comprising an aluminosilicate source, an alkali activator, reinforcing fibres, and a plurality of microparticles.

A structure for protecting a substrate. The structure comprises an inner tie coat layer which can bond to the substrate, a geopolymer foam layer, and an outer protective layer. The geopolymer foam layer is the reaction product of a mixture comprising an aluminosilicate source, an alkali activator, reinforcing fibres, and a plurality of microparticles.

A composite blast furnace mineral powder and a synthetic material made from same. The composite blast furnace mineral powder consists of the following materials in percentage by mass: 40-98.4% of blast furnace mineral powder, 7-20% of acrylic polymer emulsion or 1.5-3% of redispersible latex powder, 0.1-2% of fiber, 0-3% of pigment and the balance of filler. The composite blast furnace mineral powder can be pressed into a profile or a brick blank.

Provided herein is an asphalt binder composition, and more particularly, an amine-containing asphalt binder composition capable of improving mixability between an asphalt binder and an aggregate, and compactibility and water resistance of an asphalt paving mixture. More particularly, the present invention relates to an asphalt binder composition capable of being used in hot mix asphalt for improving workability and/or stripping-resistance, warm-mix asphalt, recycling of reclaimed asphalt pavement, or the like.