Described are cementitious reagent materials produced from globally abundant inorganic feedstocks. Also described are methods for the manufacture of such cementitious reagent materials and forming the reagent materials as microspheroidal glassy particles. Also described are apparatuses, systems and methods for the thermochemical production of glassy cementitious reagents with spheroidal morphology. The apparatuses, systems and methods makes use of an in-flight melting/quenching technology such that solid particles are flown in suspension, melted in suspension, and then quenched in suspension. The cementitious reagents can be used in concrete to substantially reduce the CO.sub.2 emission associated with cement production.

Described are cementitious reagent materials produced from globally abundant inorganic feedstocks. Also described are methods for the manufacture of such cementitious reagent materials and forming the reagent materials as microspheroidal glassy particles. Also described are apparatuses, systems and methods for the thermochemical production of glassy cementitious reagents with spheroidal morphology. The apparatuses, systems and methods makes use of an in-flight melting/quenching technology such that solid particles are flown in suspension, melted in suspension, and then quenched in suspension. The cementitious reagents can be used in concrete to substantially reduce the CO.sub.2 emission associated with cement production.

Described are cementitious reagent materials produced from globally abundant inorganic feedstocks. Also described are methods for the manufacture of such cementitious reagent materials and forming the reagent materials as microspheroidal glassy particles. Also described are apparatuses, systems and methods for the thermochemical production of glassy cementitious reagents with spheroidal morphology. The apparatuses, systems and methods makes use of an in-flight melting/quenching technology such that solid particles are flown in suspension, melted in suspension, and then quenched in suspension. The cementitious reagents can be used in concrete to substantially reduce the CO.sub.2 emission associated with cement production.

Provided are a textile reinforced cement composite for suppressing occurrence of slipping and a crack and a manufacturing method thereof. The textile reinforced cement composite for suppressing occurrence of slipping and a crack can suppress slipping between a textile grid reinforcement and a cement composite by using an angulated filling material mixed therewith when a textile reinforced cement composite having a textile grid reinforcement embedded in a cement composite is manufactured, suppress occurrence of a crack of the cement composite, suppress occurrence of a crack of the cement composite due to a fiber bridging reaction by using organic fiber mixed therewith, induce distribution of fine cracks, suppress degradation of fluidity of the cement composite caused by mixing of the angulated filling material by using a spherical binder and a chemical admixture added thereto, and suppress slipping between the textile grid reinforcement and the cement composite by using a fine powder binder having a predetermined particle size and mixed therewith.

Provided are a textile reinforced cement composite for suppressing occurrence of slipping and a crack and a manufacturing method thereof. The textile reinforced cement composite for suppressing occurrence of slipping and a crack can suppress slipping between a textile grid reinforcement and a cement composite by using an angulated filling material mixed therewith when a textile reinforced cement composite having a textile grid reinforcement embedded in a cement composite is manufactured, suppress occurrence of a crack of the cement composite, suppress occurrence of a crack of the cement composite due to a fiber bridging reaction by using organic fiber mixed therewith, induce distribution of fine cracks, suppress degradation of fluidity of the cement composite caused by mixing of the angulated filling material by using a spherical binder and a chemical admixture added thereto, and suppress slipping between the textile grid reinforcement and the cement composite by using a fine powder binder having a predetermined particle size and mixed therewith.

Described are cementitious reagent materials produced from globally abundant inorganic feedstocks. Also described are methods for the manufacture of such cementitious reagent materials and forming the reagent materials as microspheroidal glassy particles. Also described are apparatuses, systems and methods for the thermochemical production of glassy cementitious reagents with spheroidal morphology. The apparatuses, systems and methods makes use of an in-flight melting/quenching technology such that solid particles are flown in suspension, melted in suspension, and then quenched in suspension. The cementitious reagents can be used in concrete to substantially reduce the CO.sub.2 emission associated with cement production.

Described are cementitious reagent materials produced from globally abundant inorganic feedstocks. Also described are methods for the manufacture of such cementitious reagent materials and forming the reagent materials as microspheroidal glassy particles. Also described are apparatuses, systems and methods for the thermochemical production of glassy cementitious reagents with spheroidal morphology. The apparatuses, systems and methods makes use of an in-flight melting/quenching technology such that solid particles are flown in suspension, melted in suspension, and then quenched in suspension. The cementitious reagents can be used in concrete to substantially reduce the CO.sub.2 emission associated with cement production.

A magnetizable concrete wireless power transfer pad can include a base, an inductive coil and a pillar. The base can comprise a magnetizable base concrete including concrete and first magnetizable particles, the first magnetizable particles having a magnetic permeability and a magnetic saturation. The inductive coil can be positioned directly adjacent and centered over the base, the inductive coil forming an inductive coil gap at its center inner perimeter between a conductive wire that form the inductive coil, the inductive coil having an outer perimeter, a lateral width, and a longitudinal length. The pillar can extend up from the base through the inductive coil gap, the pillar comprising a magnetizable pillar concrete including concrete and second magnetizable particles, the second magnetizable particles having a magnetic permeability and a magnetic saturation such that the base and the pillar collectively shape an external magnetic field produced by the inductive coil to increase the mutual coupling with a receiver pad, that way increasing the power transfer capabilities of the system.

A magnetizable concrete wireless power transfer pad can include a base, an inductive coil and a pillar. The base can comprise a magnetizable base concrete including concrete and first magnetizable particles, the first magnetizable particles having a magnetic permeability and a magnetic saturation. The inductive coil can be positioned directly adjacent and centered over the base, the inductive coil forming an inductive coil gap at its center inner perimeter between a conductive wire that form the inductive coil, the inductive coil having an outer perimeter, a lateral width, and a longitudinal length. The pillar can extend up from the base through the inductive coil gap, the pillar comprising a magnetizable pillar concrete including concrete and second magnetizable particles, the second magnetizable particles having a magnetic permeability and a magnetic saturation such that the base and the pillar collectively shape an external magnetic field produced by the inductive coil to increase the mutual coupling with a receiver pad, that way increasing the power transfer capabilities of the system.

Described are cementitious reagent materials produced from globally abundant inorganic feedstocks. Also described are methods for the manufacture of such cementitious reagent materials and forming the reagent materials as microspheroidal glassy particles. Also described are apparatuses, systems and methods for the thermochemical production of glassy cementitious reagents with spheroidal morphology. The apparatuses, systems and methods makes use of an in-flight melting/quenching technology such that solid particles are flown in suspension, melted in suspension, and then quenched in suspension. The cementitious reagents can be used in concrete to substantially reduce the CO.sub.2 emission associated with cement production.