The use of calcium aluminate cement in autoclaved cement products, cementitious compositions suitable for forming the autoclaved cement products, and methods for making the cementitious compositions and autoclaved cement products.

Method of making foamed gypsum slurry having 15 to 90 volume percent gas bubbles including: passing first slurry including water and on dry basis 50 to 98 wt. % calcium sulfate hemihydrate, 1 to 50 wt. % calcium carbonate, and 0.1 to 10 wt. % cellulose thickener via a first hose to a Wye connector conduit first inlet opening at Rate C and passing alum solution via a second hose to a second inlet opening of the conduit at Rate D to create combined mixed stream passing from the conduit to a static mixer for mixing for Time 3 to activate at least a portion of the calcium carbonate and alum to generate CO.sub.2 and create the foamed gypsum slurry; transferring the slurry from the mixer to a cavity between two wall boards via a third hose. Allowing the slurry in the cavity to expand, harden and dry.

Method of making foamed gypsum slurry having 15 to 90 volume percent gas bubbles including: passing first slurry including water and on dry basis 50 to 98 wt. % calcium sulfate hemihydrate, 1 to 50 wt. % calcium carbonate, and 0.1 to 10 wt. % cellulose thickener via a first hose to a Wye connector conduit first inlet opening at Rate C and passing alum solution via a second hose to a second inlet opening of the conduit at Rate D to create combined mixed stream passing from the conduit to a static mixer for mixing for Time 3 to activate at least a portion of the calcium carbonate and alum to generate CO.sub.2 and create the foamed gypsum slurry; transferring the slurry from the mixer to a cavity between two wall boards via a third hose. Allowing the slurry in the cavity to expand, harden and dry.

[Object]

To provide the friction material for the disc brake such as an automobile, which is manufactured by forming the NAO friction material composition, enabling to restrain the brake vibration during braking in a high temperature.

[Means to Resolve]

In the friction material for the disc brake pad, which is manufactured by forming the NAO friction material composition that does not contain the copper component but contains the binder, the fiber base, the organic friction modifier, the inorganic friction modifier, and the lubricant, the friction material composition contains 1-4 weight % of the cashew dust as the organic friction modifier relative to the entire amount of the friction material composition, 7-12 weight % of the muscovite as the inorganic friction modifier relative to the entire friction material composition, and 0.5-5 weight % of the aluminum particle as the inorganic friction modifier relative to the entire amount of the friction material composition.

[Object]

To provide the friction material for the disc brake such as an automobile, which is manufactured by forming the NAO friction material composition, enabling to restrain the brake vibration during braking in a high temperature.

[Means to Resolve]

In the friction material for the disc brake pad, which is manufactured by forming the NAO friction material composition that does not contain the copper component but contains the binder, the fiber base, the organic friction modifier, the inorganic friction modifier, and the lubricant, the friction material composition contains 1-4 weight % of the cashew dust as the organic friction modifier relative to the entire amount of the friction material composition, 7-12 weight % of the muscovite as the inorganic friction modifier relative to the entire friction material composition, and 0.5-5 weight % of the aluminum particle as the inorganic friction modifier relative to the entire amount of the friction material composition.

The present invention relates to an improved drywall finish and joint compound comprised of a mixture of fractured aluminum oxide, glass bead, calcium sulfate, calcium carbonate, magnesium aluminum phyllosilicate, aluminum silicate hydroxide, polyvinyl acetate, polyvinyl alcohol, metamorphic mineral, sodium bicarbonate, silicon and aluminides, talc, kaolin, and metal oxide. The improved drywall finish and joint compound is capable of adhering to drywall, wood, concrete, brick, stone, steel and other surfaces, and can be applied using a conventional trowel or similar device, cures quickly, and eliminates the need for taping and bedding. The compound saves extensive time and labor when installing, repairing or working with drywall.

The present invention relates to an improved drywall finish and joint compound comprised of a mixture of fractured aluminum oxide, glass bead, calcium sulfate, calcium carbonate, magnesium aluminum phyllosilicate, aluminum silicate hydroxide, polyvinyl acetate, polyvinyl alcohol, metamorphic mineral, sodium bicarbonate, silicon and aluminides, talc, kaolin, and metal oxide. The improved drywall finish and joint compound is capable of adhering to drywall, wood, concrete, brick, stone, steel and other surfaces, and can be applied using a conventional trowel or similar device, cures quickly, and eliminates the need for taping and bedding. The compound saves extensive time and labor when installing, repairing or working with drywall.

In order to specify a catalytic converter, especially SCR catalytic converter, with maximum catalytic activity, this catalytic converter has at least one catalytically active component and additionally at least one porous inorganic filler component having meso- or macroporosity. The organic porous filler component has a proportion of about 5 to 50% by weight. More particularly, a diatomaceous earth or a pillared clay material is used as the porous inorganic filler component.

In order to specify a catalytic converter, especially SCR catalytic converter, with maximum catalytic activity, this catalytic converter has at least one catalytically active component and additionally at least one porous inorganic filler component having meso- or macroporosity. The organic porous filler component has a proportion of about 5 to 50% by weight. More particularly, a diatomaceous earth or a pillared clay material is used as the porous inorganic filler component.

The composition for preparation of a fire resistant interlayer includes an aqueous alkali silicate solution and a silicon dioxide compound. The composition has a molar ratio of silicon dioxide (SiO2) to alkali metal oxide (M2O) of larger than 2. The composition further includes a stabilisation agent and the stabilisation agent includes zinc (Zn).