A cement composition based on a sulfoaluminate clinker is described, together with its use for agglomerating and inerting sediment/dredging sludge, and the relative inerting method and apparatus.

The present invention belongs to the field of composite materials, particularly to an underwater non-dispersible quick-setting and rapid-hardening cement-based composite material and the preparation method and application thereof. The material consists of the following raw materials in percentage by weight: 32%-34% of silicate cement, 8.8%-9% of calcium aluminate, 5%-7% of magnesium oxide, 0.5%-2% of sulfur trioxide, 0.2%-0.3% of polycarboxylate high performance water-reducing agent, 0.3%-0.7% of flocculant, 0.05%-0.2% of setting accelerator, 0.05%-0.2% of air-entraining agent, 0.05%-0.3% of rust inhibitor, 26%-31% of fine aggregate, 13%-18% of coarse aggregate, and 8.4%-8.5% of water. The material can be used for rapid repair of cement buildings in water conservancy projects, the repair material can be quickly set and the initial strength can be guaranteed.

The present invention belongs to the field of composite materials, particularly to an underwater non-dispersible quick-setting and rapid-hardening cement-based composite material and the preparation method and application thereof. The material consists of the following raw materials in percentage by weight: 32%-34% of silicate cement, 8.8%-9% of calcium aluminate, 5%-7% of magnesium oxide, 0.5%-2% of sulfur trioxide, 0.2%-0.3% of polycarboxylate high performance water-reducing agent, 0.3%-0.7% of flocculant, 0.05%-0.2% of setting accelerator, 0.05%-0.2% of air-entraining agent, 0.05%-0.3% of rust inhibitor, 26%-31% of fine aggregate, 13%-18% of coarse aggregate, and 8.4%-8.5% of water. The material can be used for rapid repair of cement buildings in water conservancy projects, the repair material can be quickly set and the initial strength can be guaranteed.

A method cementing a well is provided. The method includes the use of hydraulic cement composition that includes a set time control additive. The set time control additive includes a water soluble calcium salt such as calcium nitrate, a water soluble chloride salt such as sodium chloride, and a hydroxy carboxylic acid.

A method cementing a well is provided. The method includes the use of hydraulic cement composition that includes a set time control additive. The set time control additive includes a water soluble calcium salt such as calcium nitrate, a water soluble chloride salt such as sodium chloride, and a hydroxy carboxylic acid.

A method of producing a carbonated composite material is described that includes: providing a carbonatable cementitious material in particulate form; mixing the carbonatable cementitious material with water to produce a mix; forming a predetermined shape with the mix, wherein the predetermined shape has an initial pore structure containing an initial pore solution having a first pH; pre-conditioning the predetermined shape to remove a predetermined amount of the water from the predetermined shape to produce a pre-conditioned shape; carbonating the pre-conditioned shape in an environment comprising carbon dioxide to produce a modified pore structure containing a modified pore solution having and a second pH, wherein the difference between the first pH and the second pH is represented by a ΔpH, and the ΔpH is 1.0 or less, 0.75 or less, 0.5 or less, 0.25 or less, or about 0.0. A calcium silicate composition including solid components and liquid components having improved pore solution pH stability is also disclosed.

A method of producing a carbonated composite material is described that includes: providing a carbonatable cementitious material in particulate form; mixing the carbonatable cementitious material with water to produce a mix; forming a predetermined shape with the mix, wherein the predetermined shape has an initial pore structure containing an initial pore solution having a first pH; pre-conditioning the predetermined shape to remove a predetermined amount of the water from the predetermined shape to produce a pre-conditioned shape; carbonating the pre-conditioned shape in an environment comprising carbon dioxide to produce a modified pore structure containing a modified pore solution having and a second pH, wherein the difference between the first pH and the second pH is represented by a ΔpH, and the ΔpH is 1.0 or less, 0.75 or less, 0.5 or less, 0.25 or less, or about 0.0. A calcium silicate composition including solid components and liquid components having improved pore solution pH stability is also disclosed.

According to some embodiments, a curable mixture configured to set in the presence of water, wherein the mixture comprises magnesium oxide, a primary cementitious component and at least one accelerant. A proportion by weight of the primary cementitious component is 80% to 120% of a proportion of magnesium oxide by weight.

According to some embodiments, a curable mixture configured to set in the presence of water, wherein the mixture comprises magnesium oxide, a primary cementitious component and at least one accelerant. A proportion by weight of the primary cementitious component is 80% to 120% of a proportion of magnesium oxide by weight.

An aqueous suspension including 5 to 65 wt. % of calcium hydroxide, wherein at least 50 wt. % of the calcium hydroxide is present in the form of nanoparticles, and at least one compound for stabilizing the suspension. The aqueous suspension accelerates the setting of mineral binder compositions without adversely affecting the processing properties of the composition.