The present disclosure relates to the manufacture of ceramic products by aqueous gelcasting. Exemplary ceramic products include sanitary ware, such as toilets and sinks. The process includes a slurrying step, a mixing step, a molding step involving aqueous gelcasting, a drying step, a glazing step, and a firing step.

A method to solidify cremation remains includes milling the cremation remains to a reduced particle size, adding water to the cremation remains to produce a mixture; shaping the mixture into wet ware having a desired shape, drying the wet ware to greenware that is sufficiently dry for firing, and firing the greenware in a kiln until solidified to one or more cremains solids consisting of the cremation remains. A product formed of solidified cremation remains is also disclosed.

In order to specify a catalytic converter, especially SCR catalytic converter, with maximum catalytic activity, this catalytic converter has at least one catalytically active component and additionally at least one porous inorganic filler component having meso- or macroporosity. The organic porous filler component has a proportion of about 5 to 50% by weight. More particularly, a diatomaceous earth or a pillared clay material is used as the porous inorganic filler component.

In order to specify a catalytic converter, especially SCR catalytic converter, with maximum catalytic activity, this catalytic converter has at least one catalytically active component and additionally at least one porous inorganic filler component having meso- or macroporosity. The organic porous filler component has a proportion of about 5 to 50% by weight. More particularly, a diatomaceous earth or a pillared clay material is used as the porous inorganic filler component.

The present disclosure relates to the manufacture of ceramic products by aqueous gelcasting. Exemplary ceramic products include sanitary ware, such as toilets and sinks. The process includes a slurrying step, a mixing step, a molding step involving aqueous gelcasting, a drying step, a glazing step, and a firing step.

What are described are a process for producing an insulating product for the refractory industry or an insulating material as intermediate for production of such a product, and a corresponding insulating material/insulating product. Likewise described are the use of a matrix encapsulation process in the production of an insulating product for the refractory industry and a corresponding insulating product and/or an insulating material as intermediate for production of such a product.

What are described are a process for producing an insulating product for the refractory industry or an insulating material as intermediate for production of such a product, and a corresponding insulating material/insulating product. Likewise described are the use of a matrix encapsulation process in the production of an insulating product for the refractory industry and a corresponding insulating product and/or an insulating material as intermediate for production of such a product.

Disclosed are a low-shrinkage, high-strength, and large ceramic plate and a manufacturing method thereof. The method comprises the following steps: (1) preparing a ceramic raw material powder; (2) subjecting an acicular wollastonite to surface coating with a silane coupling agent and to pre-dispersion with a fumed silica to obtain a pre-treated acicular wollastonite; and (3) thoroughly mixing the ceramic raw material powder and the pre-treated acicular wollastonite and granulating the resulting mixture, the amount of the pre-treated acicular wollastonite added being 10 wt % to 30 wt % of the ceramic raw material powder, and subjecting the resulting granules to dry pressing and sintering to obtain the large ceramic plate. The acicular wollastonite is incorporated into the manufacturing of the large ceramic plate to take full advantage of the reinforcing effect and low sintering shrinkage characteristics of the acicular wollastonite. The invention reduces sintering shrinkage and increases product strength.

A composition comprises at least one form of attapulgite present in a solid weight fraction amount ranging from 0.25% to 5%; kaolin present in a solid weight fraction amount ranging from 17% to 50%; and optionally Ball Clay in a solid weight fraction amount ranging from 0% to 25%. Although makeable by other processes, in some embodiments, the composition is makeable by mixing component ingredients. Although usable for other purposes, in some embodiments, the composition is used to make ceramic pieces, e.g., via casting, pressing, jiggering or jollying, especially when the slip has solids, chemistry and viscosity suitable for shaping before drying, sintering, and optionally finishing.

A composition comprises at least one form of attapulgite present in a solid weight fraction amount ranging from 0.25% to 5%; kaolin present in a solid weight fraction amount ranging from 17% to 50%; and optionally Ball Clay in a solid weight fraction amount ranging from 0% to 25%. Although makeable by other processes, in some embodiments, the composition is makeable by mixing component ingredients. Although usable for other purposes, in some embodiments, the composition is used to make ceramic pieces, e.g., via casting, pressing, jiggering or jollying, especially when the slip has solids, chemistry and viscosity suitable for shaping before drying, sintering, and optionally finishing.