A ferrite sintered magnet contains a main phase formed of ferrite having a hexagonal magnetoplumbite type crystalline structure; a first subphase containing La, Ca, and Fe, in which an atomic ratio of La is higher than that of the main phase, and the atomic ratio of La is higher than an atomic ratio of Ca; and a second subphase containing La, Ca, Si, B, and Fe, in which an atomic ratio of Ca is higher than an atomic ratio of La, an atomic ratio of B is higher than an atomic ratio of Fe, and the atomic ratio of Fe is lower than that of the main phase. An area ratio of the second subphase on a cross-sectional surface of the ferrite sintered magnet is greater than or equal to 1%.

A multiphase ferrite composition includes a primary phase consisting of a MnZn ferrite matrix; and 0.01 to 10 weight percent microscaled inclusion particles comprising an orthoferrite RFeO3 wherein R is a rare earth ion, yttrium iron garnet (YIG), or a combination thereof, wherein the microscaled inclusion particles have an average particle size (D50) of 0.1 micron to 5 microns, and wherein the D50 of the microscaled inclusion particles is smaller than the average particle size (D50) of the MnZn ferrite particles; and optionally 0.01 to 5 weight percent additive; wherein weight percent is based on the total weight of the multiphase ferrite composition. A method of manufacturing the multiphase ferrite composition is also disclosed.

A ferrite sintered body of the invention includes; a main component including 48.65 to 49.45 mol % of iron oxide in terms of Fe.sub.2O.sub.3, 2 to 16 mol % of copper oxide in terms of CuO, 28.00 to 33.00 mol % of zinc oxide in terms of ZnO, and a balance including nickel oxide, and a subcomponent including boron oxide in an amount of 5 to 100 ppm in terms of B.sub.2O.sub.3 with respect to 100 parts by weight of the main component, in which the ferrite sintered body includes crystal grains having an average crystal grain size of 2 to 30 μm.

Disclosed herein are embodiments of an enhanced resonant frequency hexagonal ferrite material, such as Y-phase hexagonal ferrite material, and methods of manufacturing. In some embodiments, sodium or potassium can be added into the crystal structure of the hexagonal ferrite material in order to achieve improved resonant frequencies in the range of 500 MHz to 1 GHz useful for radiofrequency applications.

Disclosed herein are embodiments of an enhanced resonant frequency hexagonal ferrite material, such as Y-phase hexagonal ferrite material, and methods of manufacturing. In some embodiments, sodium or potassium can be added into the crystal structure of the hexagonal ferrite material in order to achieve improved resonant frequencies in the range of 500 MHz to 1 GHz useful for radiofrequency applications.

The present invention relates to a ferrite particle, containing a crystal phase component containing a perovskite crystal represented by the compositional formula:

RZrO.sub.3 (provided that R represents an alkaline earth metal element), and having an apparent density in a range represented by the following formula:

1.90≤Y≤2.45

provided that Y in the formula is the apparent density (g/cm.sup.3) of the ferrite particle.

The present invention relates to a ferrite particle, containing a crystal phase component containing a perovskite crystal represented by the compositional formula:

RZrO.sub.3 (provided that R represents an alkaline earth metal element), and having an apparent density in a range represented by the following formula:

1.90≤Y≤2.45

provided that Y in the formula is the apparent density (g/cm.sup.3) of the ferrite particle.

A ferrite sintered magnet has a ferrite phase having a magnetoplumbite-type crystal structure, and contains at least a metal element A, a metal element R, Fe, Co, Zn, and B. The element A is at least one kind of element selected from the group consisting of Sr, Ba, Ca, and Pb, and essentially includes Ca. The element R is at least one kind of element selected from the group consisting of Bi and rare-earth elements including Y, and essentially includes La. Atomic ratios of the metal elements satisfy the following expressions.

A.sub.1-rR.sub.rFe.sub.xCo.sub.yZn.sub.z  (1)

0.40≤r≤0.70  (2)

8.20≤x≤9.34  (3)

0.05<y≤0.50  (4)

0<z≤0.20  (5)

The content of Si is 0 to 0.60% by mass in terms of SiO.sub.2, and the content of B is 0.01 to 0.70% by mass in terms of B.sub.2O.sub.3.

The invention relates to an electrode material, preferably an inert anode material comprising at least a metal core and a cermet material, characterized in that: said metal core contains at least one nickel (Ni) and iron (Fe) alloy, said cermet material comprises at least as percentages by weight: 45 to 80% of a nickel ferrite oxide phase (2) of composition Ni.sub.xFe.sub.yM.sub.zO.sub.4 with 0.60 ≤x≤0.90; 1.90≤y≤2.40; 0.00≤z≤0.20 and M being a metal selected from aluminum (Al), cobalt (Co), chromium (Cr), manganese (Mn), titanium (Ti), zirconium (Zr), tin (Sn), vanadium (V), niobium (Nb), tantalum (Ta) and hafnium (Hf) or being a combination of these metals, 15 to 45% of a metallic phase (1) comprising at least one alloy of nickel and copper.

A dielectric ceramic composition and a multilayer ceramic electronic component are provided, the dielectric ceramic composition includes a barium titanate base material main component and a subcomponent, a microstructure after sintering includes a first crystal grain including 3 or less domain boundaries and a second crystal grain including 4 or more domain boundaries, and an area ratio of the second crystal grain to the total crystal grains is 20% or less.