An elongate shaped abrasive particle comprises an elongate shaped ceramic body having opposed first and second ends joined to each other by at least two longitudinal sidewalls. At least one of the at least two longitudinal sidewalls is concave along its length. At least one of the first and second ends is a fractured surface. Methods of making elongate shaped abrasive particles and abrasive articles including them are also disclosed.

An elongate shaped abrasive particle comprises an elongate shaped ceramic body having opposed first and second ends joined to each other by at least two longitudinal sidewalls. At least one of the at least two longitudinal sidewalls is concave along its length. At least one of the first and second ends is a fractured surface. Methods of making elongate shaped abrasive particles and abrasive articles including them are also disclosed.

A composition for forming a PZT-based piezoelectric film formed of Mn-doped composite metal oxides is provided, the composition including: PZT-based precursors containing metal atoms configuring the composite metal oxides; a diol; and polyvinylpyrrolidone, in which when a metal atom ratio in the composition is shown as Pb:Mn:Zr:Ti, the PZT-based precursors are contained so that a metal atom ratio of Pb is satisfied to be from 1.00 to 1.20, a metal atom ratio of Mn is satisfied to be equal to or greater than 0.002 and less than 0.05, a metal atom ratio of Zr is satisfied to be from 0.40 to 0.55, a metal atom ratio of Ti is satisfied to be from 0.45 to 0.60, and the total of Zr and Ti in a metal atom ratio is 1.

A composition for forming a PZT-based piezoelectric film formed of Mn-doped composite metal oxides is provided, the composition including: PZT-based precursors containing metal atoms configuring the composite metal oxides; a diol; and polyvinylpyrrolidone, in which when a metal atom ratio in the composition is shown as Pb:Mn:Zr:Ti, the PZT-based precursors are contained so that a metal atom ratio of Pb is satisfied to be from 1.00 to 1.20, a metal atom ratio of Mn is satisfied to be equal to or greater than 0.002 and less than 0.05, a metal atom ratio of Zr is satisfied to be from 0.40 to 0.55, a metal atom ratio of Ti is satisfied to be from 0.45 to 0.60, and the total of Zr and Ti in a metal atom ratio is 1.

Disclosed are embodiments of synthetic garnet materials for use in radiofrequency applications. In some embodiments, increased amounts of bismuth can be added into specific sites in the crystal structure of the synthetic garnet in order to boost certain properties, such as the dielectric constant and magnetization. Accordingly, embodiments of the disclosed materials can be used in high frequency applications, such as in base station antennas.

Disclosed are embodiments of synthetic garnet materials for use in radiofrequency applications. In some embodiments, increased amounts of bismuth can be added into specific sites in the crystal structure of the synthetic garnet in order to boost certain properties, such as the dielectric constant and magnetization. Accordingly, embodiments of the disclosed materials can be used in high frequency applications, such as in base station antennas.

The present invention generally relates to the use of pre-formed bodies of Chemically Bonded Ceramics (CBCs) biomaterial for implantation purposes wherein the bodies are prepared ex vivo allowing process parameters to be optimized for desired long term properties of the resulting CBC biomaterial. More particularly, the pre-formed CBC material bodies of the present invention are sintered. The pre-formed body of CBC material is machined to the desired geometry and then implanted using a CBC cementation paste for fixation of the body to tissue. The invention also relates to a method of preparing pre-formed bodies of CBC biomaterial for implantation purposes, methods of preparing an implant thereof having desired geometry, and a method of implantation of the implant, as well as a kit for use in the method of implantation.

A method of treating a carbon structure is provided. The method may include infiltrating the carbon structure with a silicon compound preparation, heat treating the carbon structure to form a plurality of silicon carbide whiskers in the carbon structure, and/or densifying the carbon structure.

A method of forming a porous sol gel, including a dried porous sol gel, is provided comprising forming a sol gel from a sol gel-forming composition comprising a silane solution and a catalyst solution; and non-supercritically drying the sol gel to provide a dried porous sol gel having no springback. The dried porous sol gel can include dried macroporous or mesoporous sol gels or dried hybrid aerogels. The materials may contain open or filled pores. Such materials are useful as thermal insulators.

A method of forming a porous sol gel, including a dried porous sol gel, is provided comprising forming a sol gel from a sol gel-forming composition comprising a silane solution and a catalyst solution; and non-supercritically drying the sol gel to provide a dried porous sol gel having no springback. The dried porous sol gel can include dried macroporous or mesoporous sol gels or dried hybrid aerogels. The materials may contain open or filled pores. Such materials are useful as thermal insulators.