In a processing method for a ceramic-based composite material in which the ceramic-based composite material is molded by layering sheets obtained by impregnating reinforced fibers with a slurry containing ceramic powder and calcining the sheets after curing, the processing method includes a step of layering the sheets in a layering direction to form a laminate, and a step of covering the laminate with a vacuum bag and evacuating the inside of the vacuum bag to mold a cured laminate. In the step of molding the cured laminate, a slurry-removing material configured to absorb excess slurry is disposed with respect to the laminate, and a degassing circuit member provided on at least one side of the laminate and configured to discharge air bubbles generated inside the laminate is disposed with respect to the laminate.

A dielectric body includes a plurality of crystal grains of which a main component is barium titanate, and an additive including Zr, Eu and Mn. At least one of the plurality of crystal grains has a core-shell structure having a core and a shell. A Zr/Ti atomic concentration ratio is 0.02 or more and 0.10 or less. An Eu/Ti atomic concentration ratio is 0.001 or more and 0.03 or less. A Mn/Ti atomic concentration ratio is 0.005 or more and 0.05 or less. A total atomic concentration of the one or more rare elements is smaller than an atomic concentration of Eu when the dielectric body has the one or more rare earth elements. A median diameter of the plurality of crystal grains is 200 nm or more and 400 nm or less.

A dielectric body includes a plurality of crystal grains of which a main component is barium titanate, and an additive including Zr, Eu and Mn. At least one of the plurality of crystal grains has a core-shell structure having a core and a shell. A Zr/Ti atomic concentration ratio is 0.02 or more and 0.10 or less. An Eu/Ti atomic concentration ratio is 0.001 or more and 0.03 or less. A Mn/Ti atomic concentration ratio is 0.005 or more and 0.05 or less. A total atomic concentration of the one or more rare elements is smaller than an atomic concentration of Eu when the dielectric body has the one or more rare earth elements. A median diameter of the plurality of crystal grains is 200 nm or more and 400 nm or less.

The present invention discloses a polyimide-based composite carbon film with high thermal conductivity and a preparation method therefor. The preparation method includes: uniformly coating the surface of a polyimide-based carbon film with an aqueous graphene oxide solution, and then covering the same with another polyimide-based carbon film uniformly coated with an aqueous graphene oxide solution; repeating such operation; after the polyimide-based carbon films are dried, bonding the polyimide-based carbon films by means of graphene oxide so as to form a thick film; bonding the polyimide-based carbon films more tightly by means of further low-temperature hot pressing; and finally, obtaining a thick polyimide-based carbon film with high thermal conductivity by repairing defects by means of low-temperature heating pre-reduction and high-temperature and high-pressure thermal treatment. The thick polyimide-based carbon film with high thermal conductivity has a thickness greater than 100 μm and an in-plane thermal conductivity of even reaching 1700 W/mK or above.

A method of producing a core-shell particle includes introducing a barium titanate-based base powder and an additive to a reactor, and exposing the barium titanate-based base powder and the additive to a thermal plasma torch to obtain core-shell particles including a core portion having barium titanate (BaTiO.sub.3) and a shell portion including the additive and formed on a surface of the core portion.

A grain-grade zirconia toughened alumina ceramic substrate and a method for preparing the same. The ceramic substrate is prepared from alumina power (main phase) and zirconia powder (secondary phase) in a binary azeotrope of anhydrous ethanol and butanone in the presence of magnesia-alumina spinel powder (as sintering aid), phosphate ester (as dispersant), polyvinyl butyral (as binder) and dibutyl phthalate (as plasticizer). In a mixture of the alumina power and the zirconia powder, a volume percentage of the alumina power is 82.44-96.7%, and a volume percentage of the zirconia powder is 3.30-17.56%. The magnesia-alumina spinel powder is 0.1-4.0% by weight of the mixture of the alumina power and the zirconia powder. A particle size ratio of the alumina powder to the zirconia powder is 2.415-4.444.

A paste for ceramic 3D shaping according to the present invention is a paste for ceramic 3D shaping containing a curable resin and inorganic particles, in which the inorganic particles contain ceramic particles and glass particles.

The present invention provides a method of preparing bulk BSCCO-based material, the method comprising: mixing a first solution with a second solution at a pre-determined temperature to form a gel, wherein the first solution comprises salts of at least bismuth, strontium, calcium and copper and the second solution comprises a precipitating agent; drying the gel to form a xerogel; grinding the xerogel to form a homogeneous metalorganic precursor; and calcining the homogeneous metalorganic precursor to form bulk BSCCO-based materials. Further steps may enable preparation of 2D BSCCO flakes.

In a manufacturing method for manufacturing a dispersion body, a plurality of types of solid particles, water, and a liquid other than water are mixed. The solid particles and the liquid are selected such that Hansen spheres of at least two types of the solid particles and a Hansen sphere of at least one type of the liquid mutually overlap, and a Hansen solubility parameter distance to water of at least one type of the solid particles of which the Hansen spheres overlap that of the liquid is greatest among all solid particles used in manufacturing of the dispersion body, and used to manufacture the dispersion body.

A method of making abrasive particles includes: providing a slurry comprising non-colloidal solid particles and a liquid vehicle; forming at least a portion of the slurry into shaped bodies contacting a substrate; at least partially drying the shaped bodies to provide shaped abrasive precursor particles; separating at least a portion of the shaped abrasive precursor particles from the substrate; and converting at least a portion of the shaped abrasive precursor particles into shaped abrasive particles. The shaped abrasive particles comprise alpha alumina having an average crystal grain size of 0.8 to 8 microns and an apparent density that is at least 92 percent of the true density. Each shaped abrasive particle has a respective surface comprising a plurality of smooth sides that form at least four vertexes. Shaped abrasive particles, abrasive articles including them, and methods of using are also disclosed.