A wallboard product and a method of making a wallboard product are provided. The method may include providing a wallboard core. And exterior surface may be provided to the wallboard core. The exterior surface may include a magnesium compound.

Environmental barrier coatings including a bondcoat layer including silicon and a rare earth silicate-based hermetic layer and rare earth silicate-based non-hermetic layer are provided. The rare earth silicate-based hermetic layer is deposited on the bondcoat via a thermal spray process and has an elastic modulus ranging from 100 GPa to 180 GPa. The at least one rare earth silicate-based non-hermetic layer is deposited on the rare earth silicate-based hermetic layer and has an elastic modulus ranging from 50 GPa to 100 GPa. Coated gas turbine engine components and methods for coating gas turbine engine components are also provided.

Disclosed is a coated composite comprising a seal coat disposed on a composite material wherein the seal coat comprises protective particles and a matrix.

Disclosed is a coated composite comprising a seal coat disposed on a composite material wherein the seal coat comprises protective particles and a matrix.

In one aspect, an article comprises a substrate that comprises a ceramic matrix composite; and a metal oxide layer disposed on the substrate; where the metal oxide layer has a marking etched into the metal oxide via laser ablation. The markings include alphabets, numbers, symbols, bar codes, matrix bar codes, quick response codes, or a combination thereof. Disclosed herein too is a method comprising disposing upon a ceramic matrix composite a metal oxide layer; and laser ablating the metal oxide layer to etch the metal oxide layer. The etchings produce markings that comprise alphabets, numbers, symbols, bar codes, matrix bar codes, quick response codes, or a combination thereof.

In one aspect, an article comprises a substrate that comprises a ceramic matrix composite; and a metal oxide layer disposed on the substrate; where the metal oxide layer has a marking etched into the metal oxide via laser ablation. The markings include alphabets, numbers, symbols, bar codes, matrix bar codes, quick response codes, or a combination thereof. Disclosed herein too is a method comprising disposing upon a ceramic matrix composite a metal oxide layer; and laser ablating the metal oxide layer to etch the metal oxide layer. The etchings produce markings that comprise alphabets, numbers, symbols, bar codes, matrix bar codes, quick response codes, or a combination thereof.

A preparation method includes the following steps: Step (1): pressing and then drying body powder to form a green brick; Step (2): applying a ground coat on the surface of the green brick; Step (3): inkjet-printing a pattern on the surface of the green brick having the ground coat, and applying an isolation glaze; Step (4): applying a fully polished glaze on the surface of the green brick having the isolation glaze; and Step (5): drying, firing, and polishing the green brick having the fully polished glaze to obtain a hard wear-resistant polished glazed ceramic tile. The phase composition of the fired fully polished glaze is as follows: 10 to 20 percent by weight of corundum, 20 to 30 percent by weight of hyalophane, 0.5 to 1.0 percent by weight of hematite, and 50 to 68 percent by weight of amorphous phase.

A preparation method includes the following steps: Step (1): pressing and then drying body powder to form a green brick; Step (2): applying a ground coat on the surface of the green brick; Step (3): inkjet-printing a pattern on the surface of the green brick having the ground coat, and applying an isolation glaze; Step (4): applying a fully polished glaze on the surface of the green brick having the isolation glaze; and Step (5): drying, firing, and polishing the green brick having the fully polished glaze to obtain a hard wear-resistant polished glazed ceramic tile. The phase composition of the fired fully polished glaze is as follows: 10 to 20 percent by weight of corundum, 20 to 30 percent by weight of hyalophane, 0.5 to 1.0 percent by weight of hematite, and 50 to 68 percent by weight of amorphous phase.

A preparation method includes the following steps: Step (1): pressing and then drying body powder to form a green brick; Step (2): applying a ground coat on the surface of the green brick; Step (3): inkjet-printing a pattern on the surface of the green brick having the ground coat, and applying an isolation glaze; Step (4): applying a fully polished glaze on the surface of the green brick having the isolation glaze; and Step (5): drying, firing, and polishing the green brick having the fully polished glaze to obtain a hard wear-resistant polished glazed ceramic tile. The phase composition of the fired fully polished glaze is as follows: 10 to 20 percent by weight of corundum, 20 to 30 percent by weight of hyalophane, 0.5 to 1.0 percent by weight of hematite, and 50 to 68 percent by weight of amorphous phase.

The present invention relates to a method for the manufacturing of a coated panel, in particular a wall, ceiling or flooring panel for applications in outdoor areas, as well as such a panel. The method comprises the following steps: providing a carrier plate of mineral wool and/or glass wool, comprising a front side and a rear side, applying a primer onto the front side of the carrier plate, thereafter applying a liquid first oligomer in an amount of 30 to 150 g/m.sup.2 onto the front side of the carrier plate; thereafter applying a liquid second oligomer, which differs from the first oligomer, in an amount of 30 to 180 g/m.sup.2 onto the wet surface of the before applied layer of the first oligomer.